| Type: | Titanium Sheets |
|---|---|
| Application: | Industrial |
| Technique: | Hot Rolled |
| Grade: | GR1 |
| Shape: | Square |
| Thickness: | 0.3mm-120mm |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier
| CP Grade 1 Titanium Plate and sheet Type | Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate |
| Grade | ASME SB265,AMS 4911,AMS 4919,AMS 4914,ASTM F67,ASTM F136, MSRR, AMS, BS |
| Titanium Alloy Gr 1 Plate Length | 1000mm-13000mm or as required |
| Gr 1 Titanium Plate Width | 1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required |
| UNS R50400 Plate Thickness | 0.3 to 120mm or as required |
| ASTM B265 Titanium Alloy Gr 1 Plate Process | Hot/ Cold Rolled/forging |
| UNS R50400 Plate surface | No.1, No. 2D, No. 2B, BA, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled ASTM B265 Titanium Alloy Gr 1 Plate, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc. |
| ASTM B265 Titanium Alloy Gr 1 Plate, Sheet and Strip | JIS: N0, N2, N1, NW2200, NW2201, NW4400, NW5500, NW6002, etc |
| Titanium Grade 1 Sheet ASTM | ASTM B265 |
| Titanium Grade 1 Sheet AMS | AMS 4902 |
| Tolerances of width and thickness | EN 10258 (formerly DIN 59381),EN 10151 ASTM B265 Titanium Alloy Gr 1 strip for springs,EN 10088 ASTM B265 Titanium Alloy Gr 1 strip (general) |
| Ti 6Al 4v Grade 1 Titanium Plate standards and approvals | EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID |
| Standard Grade 1 ALLOY Plate & Sheet Sizes | 1000 x 2000 mm, 1220 x 2440 mm, 1500 x 3000 mm, 2000 x 2000 mm, 2000 x 4000 mm |
| Cold rolled Gr 1 Titanium Plate 0.5-6.4 mm | |
| Hot rolled Gr 1 Titanium Plate 3.0-60.0 mm | |
| UNS R50400 Plate Hardness | Soft, Hard, Half Hard, Quarter Hard, Spring Hard ASTM B265 Titanium Alloy Gr 1 Sheet suppliers |
| Availability of Titanium Alloy Gr 1 Foil sizes | Thickness : 8-100 microns (0.00031-0.004 in) |
| Width: Up to 500 mm (19.5 in) | |
| Weight (in rolls) : Up to 50 kg (110 lb); e.g. approxi- mately 1400 m at 8 microns and ap- proximately 112 m at 100 microns. | |
| Cutting | To provide a comprehensive service, we use a variety of cutting methods, including: |
| Laser Plate Cutting,Plasma Plate Cutting,Oxy-propane Flame Cutting | |
| Plasma profiles | As per customer's drawings |
| Value added services for Cp Grade 1 Titanium Plate | Laser cutting, Waterjet cutting, Plasma cutting, Bending and mechanical processing, edge preparation, welding, sawing and shearing. |
| China Grade 1 Titanium Plate Manufacturer | ASTM B265 Titanium Alloy Gr 1 Plate: material 3/16″ [5.00 mm] and over in thickness and over 10″ [250 mm] in width;Gr 1 Titanium Sheet: material under 3/16″ [5.00 mm] in thickness and 24″ [600 mm] and over in width;Alloy Titanium Grade 1 Clad plate: Alloy Titanium Grade 1 Clad plate is a composite steel plate made by bonding UNS R50400 Titanium Grade 1 Plate, etc.ASTM B265 Titanium Alloy Gr 1 Strip: cold-rolled material under 3/16″ [5.00 mm] in thickness and under 24″ [600 mm] in width. |
| UNS R50400 Plate Origin | CHINA |
| Packing of Grade 1 plate | Bundles with waterproof cloth outside or plywood box |
| Test | UT, SGS testing, TUV etc |
| Why buy UNS R50400 Sheet from DAXUN? | Free quote,Free sample,EN 10204 3.1,Mill Test Certificate is supplied with shipment.,NABL Approved Lab Reports,Any third party inspection is accepted.,Tested to ASTM A923 Method "C" or ASTM G48 Method "A".Minimum Nitrogen content and Ferrite Count Test |
Today, DAXUN Alloys stands as a premier global producer and supplier of exceptionally high-quality Grade 1 titanium plates.
Pure Grade 1 titanium plate, renowned for its excellent ductility and cold formability, is perfect for deep drawing applications. Grade 1 titanium offers outstanding general and seawater corrosion resistance, as well as resilience against oxidizing, neutral, and mildly reducing media, including chlorides. With about half the density of nickel-based alloys, titanium's high strength-to-weight ratio and superior corrosion resistance make it an optimal choice for various harsh chemical environments. Commercially pure Grade 1 titanium is the softest and most ductile, boasting excellent cold formability, superb corrosion resistance, exceptional weldability, and good impact hardness.
ASTM B265 Titanium Gr 1 Plate Producers, Titanium Gr 1 Sheets, Titanium Gr 1 Finished Plates, ASTM B265 Titanium Grade 1 Coil Suppliers, Pure Titanium Gr 1 Hot Rolled Plates, Titanium Gr 1 Cold Rolled Plates, Titanium ASTM B265 Gr 1 Sheets, Gr 1 Titanium Patterned Plates Dealers, Titanium Gr 1 Perforated Plates, Titanium Grade 1 Sheets and Plates Manufacturers in China.
We ensure timely and rapid delivery of Grade 1 titanium plate products. This efficiency is supported by a seamless system encompassing production capacity, information flow, logistics, and capital flow. For instance, Daxun's order data is instantly pushed to the logistics system, ensuring real-time data synchronization. Strategically located close to highways, rivers, and seas, our logistics center guarantees reasonable scheduling, swift responses, and efficient loading, ensuring tasks are completed punctually.
Grade 1 titanium plate, characterized by lower density and high ductility, is ideal for industries prioritizing weight reduction and deep drawing processes. Key applications include medical, chemical equipment, and aerospace sectors. Its strength and corrosion resistance also make it perfect for marine, chemical processing, and desalination industries. Typical uses of Grade 1 titanium alloys encompass oil and gas components, reaction and pressure vessels, piping systems, power, heat exchangers, linings, flue gas desulfurization systems, and various industrial components. Common standards: ASTM B265, ASTM F67, AMS4911, AMS4928, AMS4943, AMS4944, AMS4945, AMS4967, AMS4972.
The cold-rolled thickness range for Grade 1 Titanium Plates spans from 0.3 mm to 6.0 mm, while the hot-rolled range extends from 4.76 mm to 155 mm. Plates are produced by longitudinal and transverse rolling, available in hot-rolled or heat-treated conditions. For specialized requirements, creep flattening can be employed as a heat treatment to relieve internal stresses and meet specific flatness standards. Plates can also be provided as cut blanks-parts with intricate shapes cut from a parent plate. Further processing, mechanical or chemical, is tailored to customer specifications.
About the Chemical Composition of (Ti 6AL-4V) Grade 5 Titanium Sheet
| Chemical Composition: | |||
| Symbol | Element | Min % | Max % |
| Al | Aluminum | 5.50% | 6.75% |
| V | Vanadium | 3.50% | 4.50% |
| Fe | Iron | 0.30% | |
| O | Oxygen | 0.20% | |
| C | Carbon | 0.08% | |
| N | Nitrogen | 0.05% | |
| H | Hydrogen | 0.01% | |
| Y | Yttrium | 0.01% | |
| Other, each | 0.10% | ||
| Other, total | 0.40% | ||
| Ti | Titanium | Remainder | |
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
About the Chemical Composition of Grade 2 Titanium Sheet
| Element | Weight % |
| C | ≤0.08 |
| O | ≤0.25 |
| N | ≤0.03 |
| H | ≤0.015 |
| Fe | ≤0.30 |
| *OEE | ≤0.10 |
| *OET | ≤0.40 |
| Ti | Remaining |
About the Mechanical Properties of Grade 2 Titanium Sheet
| Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
| psi | MPa | ksi | psi | MPa | ksi | % | |||||||
| Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
| 50,000 | |||||||||||||
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
| Fe | 0.2 | ||
| O | 0.18 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
| Density | |
| lb/in3 | g/cm3 |
| 0.163 | 4.51 |
| Tensile Strength | |
| ksi | MPa |
| 35 min | 240 min |
| Yield Strength | |
| ksi | MPa |
| 20 min | 138 min |
| Hardness | |
| 70 HRC max | |
| Elongation | |
| 24% min |
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
|---|---|---|---|
| Al | 2.5 | 3.5 | |
| V | 2.0 | 3.0 | |
| Fe | 0.25 | ||
| O | 0.15 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
DAXUN, a titan in metal expertise, is dedicated to both small and large titanium plate projects. As your cornerstone and enduring partner, DAXUN is poised to supply you with premium titanium plates and provide comprehensive technical assistance. More than just a supplier of industrial pure titanium and titanium alloy plates, DAXUN is your strategic ally, ready to help you overcome any challenges and fulfill all your needs, ensuring you achieve every project goal.
At DAXUN's service center in China, we stock a wide range of titanium plate products for rapid order processing. By offering essential processing, precise water jet cutting, and efficient plate nesting, we deliver significant value to our customers, helping them save both time and costs.
With continuous investment in our state-of-the-art production facilities and strategic capacity agreements with our partners, DAXUN ensures that we remain at the pinnacle of titanium plate quality, both now and in the future.
Reach out to DAXUN today to receive the latest updates on titanium plate prices and technical specifications.
| CP GR1 Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium plate PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
DAXUN is a prominent manufacturer and supplier of Ti-6AL-4V Grade 5 TC4 UNS R56400 Alloy Titanium Plates from China. Our mission is to create the world's most advanced titanium alloy plates, ensuring quick worldwide delivery. We produce and stock high-performance alloy titanium plates Grade 5 (UNS R56400) with thicknesses from 0.5mm to 300mm (0.5mm-6.0mm is cold rolled, 6.0-50mm is hot rolled, and 50mm and above are forged). Grade 5 titanium plate (Ti-6Al-4V) is celebrated for its exceptional strength, ductility, excellent corrosion resistance, and high-temperature tolerance, making it indispensable for both general and military industries. Compliant with ASTE, ASME, AMS, GB, GJB, MIL, JIS, EN, and many other standards.
Ti-6Al-4V Grade 5 titanium plates are primarily utilized in aerospace, military, power industry, vehicle armor, rocket precision guidance parts, and marine industry.
Grade 1
Today, DAXUN Alloys stands as a leading global producer and supplier of premium Grade 1 titanium plates.
Pure Grade 1 titanium plate boasts excellent ductility and cold formability, making it perfect for deep drawing applications. Known for its superior general and seawater corrosion resistance as well as resistance to oxidizing, neutral, and mildly reducing media, including chlorides, Grade 1 titanium is ideal for harsh chemical conditions. With a low density (about half that of nickel-based alloys), a high strength-to-weight ratio, and outstanding corrosion resistance, Grade 1 titanium is the softest and most ductile grade. It offers excellent cold formability, weldability, and good impact hardness.
ASTM B265 Titanium Grade 1 Plate Producers, Titanium Grade 1 Sheets, Titanium Grade 1 Finished Plates, ASTM B265 Titanium Grade 1 Coil Suppliers, Pure Titanium Grade 1 Hot Rolled Plates, Titanium Grade 1 Cold Rolled Plates, Titanium ASTM B265 Grade 1 Sheets, Grade 1 Titanium Patterned Plates Dealers, Titanium Grade 1 Perforated Plates, Titanium Grade 1 Sheets and Plates Manufacturers in China.
Grade 2
DAXUN specializes in producing and stocking commercially pure titanium plates Grade 2 (UNS R50400) with thicknesses from 0.5mm to 120mm. Grade 2 Titanium Plate (UNS R50400) is the 'workhorse' of the commercially pure titanium family, offering a superb mix of strength, ductility, and excellent corrosion resistance for various industrial applications.
Grade 2 Titanium Plate is a commercially pure titanium plate that provides an excellent balance of strength and ductility. It features good impact strength and weldability, along with robust corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, weakly reducing environments, and wet ***. It also stands out for its excellent resistance to seawater and salt solutions.
Titanium's low density, high strength-to-weight ratio, and corrosion resistance make it ideal for a vast array of applications. It effectively resists stress corrosion cracking, pitting, and crevice corrosion in chloride solutions below 70°C. With a melting point of 1660°C, Grade 2 Titanium Plate is the preferred alloy for most industrial applications requiring good ductility and corrosion resistance.
DAXUN is your go-to expert for both small and large titanium plate projects. As your dependable partner, we are ready to supply you with premium titanium plates and any technical assistance you need. Consider DAXUN not just as a supplier of industrial pure titanium plates and titanium alloy plates, but as a strategic ally to help you overcome any challenges and meet your project objectives.
Welcome to DAXUN's premier service center in China, where our extensive inventory of titanium plate products ensures rapid order processing. With our advanced basic processing techniques, precision water jet cutting, and efficient plate nesting solutions, we deliver unparalleled value. By choosing DAXUN, you not only save valuable time but also reduce costs, making us your perfect partner in success.
DAXUN's unwavering commitment to continuous investment in state-of-the-art production facilities and strategic capacity agreements with our trusted partners solidifies our position as an industry leader in titanium plate quality. Our dedication ensures that we remain at the pinnacle of excellence both now and in the future.
Reach out to DAXUN today for the most competitive prices and comprehensive technical information on our titanium plates. Our expert team is ready to assist you with all your requirements, ensuring you receive the best in quality and service.
Q1: What products can you offer?
A: We offer a diverse range of high-quality steel types, including 310S, 316L, 304, 304L, 201, 904L, 316H, and 316. Additionally, we provide 300 and 400 series steels.
We also specialize in duplex stainless steels like 2205, 2304, 2101, and 2507, as well as high-nickel alloys such as 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
Yes, we tailor our production to your specific drawings to ensure utmost satisfaction.
Q3. How does your factory do regarding quality control?
Quality is our utmost priority. We emphasize stringent quality control from start to finish.
Q4. Can I request to change the form of packaging and transportation?
Yes, we can modify the packaging and transportation form to suit your requirements.
However, please note that you will be responsible for any additional costs incurred during this process.
Q5. How does your factory do regarding quality control?
Quality is paramount for us. We maintain rigorous quality control throughout the entire production process.
Q6. How long is the delivery time?
A: Delivery typically takes 7-20 working days after payment confirmation.
If your order is urgent, we can expedite the process to meet your needs.
Q7. What is your Payment?
A: For small orders, we accept 100% T/T advance or Western Union payments.
B: For larger orders, 30% T/T in advance with the remaining 70% before shipment.
C: We also accept 100% Irrevocable LC at sight for substantial orders.
Q8: Can you make DDQ (Deep Drawing Quality)?
A: Yes, we can. Our materials are perfect for stainless steel pots, sinks, bowls, etc. Just let us know your specific needs, and we will adjust the mechanical properties accordingly.
Q9: How to get a sample?
A: FREE samples are available for your evaluation and testing. For small pieces, we may cover courier costs, depending on the situation.
Q10: Which countries have you exported to?
A: We have proudly exported stainless steel materials to Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many other countries.
Q11: How can I visit your company?
A: Fly to Guangzhou Baiyun International Airport, where we will be pleased to pick you up and bring you to our facilities.
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}