| Product Parameters: Stainless Steel rod | |
| Material | 304 304L |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
For more information on our high-quality stainless steel rods, please contact us at Daxun Alloys.
304 Stainless Steel Rod Chemical Composition
Chemical Composition (wt%) limits as specified in ASTM A240 and ASME SA240*
| Element | 304 | 304L |
| Carbon | 0.07 | 0.03 max |
| Chromium | 18.0-19.5 | 18.0-19.5 |
| Nickel | 8.0-10.5 | 8.0-12.0 |
| Manganese | 2.00 | 2.00 |
| Silicon | 0.75 | 0.75 |
| Nitrogen | 0.10 | 0.10 |
| Phosphorus | 0.045 | 0.045 |
| Sulfur | 0.030 | 0.030 |
304 Stainless Steel Rod Mechanical Properties
Mechanical property requirements for annealed products as specified in ASTM A240 and ASME SA240.
| Property | 304 | 304L |
| Yield Strength, min. (ksi) | 30 | 25 |
| Tensile Strength, min. (ksi) | 75 | 70 |
| Elongation, min. (%) | 40 | 40 |
| Hardness, max. (Rb) | 92 | 92 |
304 Stainless Steel Rod Physical Properties
Physical properties for Type 304/304L stainless steel.
| Property | 304/304LData |
| Density, lb/in3 | 0.285 |
| Modulus of Elasticity, psi | 28 x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 9.2 x 10-6 |
| Thermal Conductivity, Btu/ft hr ˚F | 9.4 |
| Specific Heat, Btu/lb ˚F | 0.12 |
| Electrical Resistivity, Microohm-in | 28.3 |
Our advanced forming capabilities include state-of-the-art radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills. Additionally, we employ a unique hydroforming process for manufacturing high-quality parts.
Our stainless steel rod heat treatments utilize cutting-edge furnace equipment to ensure material stability and optimal performance.
Daxun Stainless Steel boasts unparalleled smelting capabilities, utilizing the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace. These cutting-edge technologies minimize impurities during the smelting process, significantly enhancing the performance and quality of our premium stainless steel rods.
Our stainless steel products, including the Stainless Steel Round Rod 304L and 304 Cold Drawn variations, are fully certified and traceable. We are committed to delivering the highest quality stainless steel to leading industries such as aerospace, industrial, medical, marine, and military, ensuring unmatched reliability and performance.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
DAUXN 304/304L Stainless Steel Rods find extensive usage in numerous home and industrial settings, offering unparalleled versatility and reliability.
Can you do SS grinding bar & rod?
Yes, we specialize in manufacturing SS grinding bars & rods that boast precise dimensions, excellent roundness, and impeccable straightness, surpassing the quality of standard polished stainless steel bars. However, please note that the processing costs are higher.
Q1: What products can you offer?
A: We offer a diverse range of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, and 316L 300 series.
Additionally, we provide 400 series and duplex stainless steel such as 2205, 2304, 2101, 2507, as well as high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
Yes, we can manufacture products precisely according to your drawings, ensuring they meet your highest satisfaction.
Q3. How does your factory do regarding quality control?
Quality is our top priority. We implement stringent quality control measures from the initial stages to the final product.
Q4. Can I request to change the form of packaging and transportation?
Yes, we can modify the packaging and transportation methods to suit your requirements.
However, you will need to cover any additional costs incurred during this period, including any price differences.
Q5. How does your factory do regarding quality control?
Quality is our top priority. We implement stringent quality control measures from the initial stages to the final product.
Q6. How long is the delivery time?
A: Our standard delivery time is 7 to 20 working days after payment confirmation.
For urgent orders, we can expedite processing to meet your deadlines.
Q7. What is your Payment?
A: For full payment in advance, we accept 100% T/T or Western Union for small orders.
B: For larger orders, a 30% T/T deposit with the remaining 70% balance due before shipment.
C: For significant orders, we accept a 100% Irrevocable LC at sight.
Q8: Can you make DDQ (Deep Drawing Quality)?
A: Yes, we can. Our materials are ideal for applications like stainless steel pots, sinks, and bowls. Simply tell us your needs, and we'll adjust the mechanical properties accordingly.
Q9: How to get a sample?
A: We provide FREE samples for your evaluation. For small pieces, we may also cover the courier costs, subject to conditions.
Q10: Which countries have you exported to?
A: To date, we have exported our stainless steel materials to countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many more.
){kind=link}