| Product Parameters: Stainless Steel rod | |
| Material | 304 304L |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
For more information on stainless steel rods, please contact Daxun.
304 Stainless Steel Rod Chemical Composition
Chemical Composition (wt%) limits are as specified in ASTM A240 and ASME SA240*
| Element | 304 | 304L |
| Carbon | 0.07 | 0.03 max |
| Chromium | 18.0-19.5 | 18.0-19.5 |
| Nickel | 8.0-10.5 | 8.0-12.0 |
| Manganese | 2.00 | 2.00 |
| Silicon | 0.75 | 0.75 |
| Nitrogen | 0.10 | 0.10 |
| Phosphorus | 0.045 | 0.045 |
| Sulfur | 0.030 | 0.030 |
304 Stainless Steel Rod Mechanical Properties
Mechanical property requirements for annealed products are as specified in ASTM A240 and ASME SA240
| Property | 304 | 304L |
| Yield Strength, min. (ksi) | 30 | 25 |
| Tensile Strength, min. (ksi) | 75 | 70 |
| Elongation, min. (%) | 40 | 40 |
| Hardness, max. (Rb) | 92 | 92 |
304 Stainless Steel Rod Physical Properties
Physical properties for Type 304/304L stainless steel
| Property | 304/304LData |
| Density, lb/in3 | 0.285 |
| Modulus of Elasticity, psi | 28 x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 9.2 x 10-6 |
| Thermal Conductivity, Btu/ft hr ˚F | 9.4 |
| Specific Heat, Btu/lb ˚F | 0.12 |
| Electrical Resistivity, Microohm-in | 28.3 |
Our forming capabilities feature state-of-the-art radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills. These facilities enable the production of titanium rods and utilize a unique hydroforming process for manufacturing high-precision parts.
Our advanced heat treatment furnace equipment ensures the stability and exceptional performance of the stainless steel rod material, guaranteeing superior quality.
Daxun Stainless Steel is crafted using the world's most advanced technologies: vacuum induction furnace, vacuum consumable furnace, and electroslag furnace. These state-of-the-art methods significantly reduce impurities during the smelting process, thereby enhancing the overall performance and durability of our stainless steel rods.
Our stainless steel products are not only fully certified and traceable but also crafted to the highest standards. We proudly supply premium stainless steel to elite industries such as aerospace, industrial, medical, marine, and military, ensuring unmatched quality and reliability.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
The DAUXN 304/304L Stainless Steel RODS are employed in a diverse array of both residential and commercial applications, such as:
Can you produce stainless steel grinding bars and rods?
Absolutely! We specialize in crafting precision stainless steel grinding bars and rods with unmatched dimensional accuracy, roundness, and straightness. While these superior qualities make our grinding bars stand out compared to polished bars, they do come with a higher processing cost.
Q1: What products can you offer?
A: We provide a wide range of general steel types such as 310S, 316L, 304, 304L, 201, 904L, 316H, and 316. Additionally, we offer an extensive selection of 300 series alloys.
400 series options are available, alongside duplex stainless steel like 2205, 2304, 2101, and 2507. Moreover, we specialize in high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce products according to my drawings?
Yes, we can meticulously craft products based on your specific drawings, ensuring the highest level of satisfaction.
Q3. How does your factory ensure quality control?
Quality is our top priority. We maintain rigorous quality control measures throughout the entire production process, from start to finish.
Q4. Can the packaging and transportation method be changed upon request?
Yes, we can modify the packaging and transportation methods to meet your preferences.
However, you will need to cover any additional costs and adjustments incurred during this period.
Q5. What measures does your factory take for quality control?
Quality is paramount. We have stringent quality control protocols from the very beginning to the final stages of production.
Q6. What is the delivery time?
A: Standard delivery time is between 7 to 20 working days after payment confirmation.
For urgent orders, we can expedite the process to ensure timely completion.
Q7. What are your payment terms?
A: 100% T/T in advance or Western Union for small orders.
B: 30% T/T upfront and the remaining 70% before shipment.
C: 100% Irrevocable LC at sight for large orders.
Q8: Can you produce Deep Drawing Quality (DDQ) materials?
A: Yes, we can. Our DDQ materials are ideal for stainless steel pots, sinks, bowls, and more. Simply inform us of your specific usage, and we will tailor the mechanical properties to meet your requirements.
Q9: How can I obtain a sample?
A: We offer FREE samples for your evaluation and testing. For small pieces, we may cover the courier cost, depending on the circumstances.
Q10: Which countries have you exported to?
A: To date, we have exported our stainless steel materials to numerous countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many others.
){kind=link}