| CP Grade 1 Titanium Plate and sheet Type | Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate |
| Grade | ASME SB265,AMS 4911,AMS 4919,AMS 4914,ASTM F67,ASTM F136, MSRR, AMS, BS |
| Titanium Alloy Gr 1 Plate Length | 1000mm-13000mm or as required |
| Gr 1 Titanium Plate Width | 1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required |
| UNS R50400 Plate Thickness | 0.3 to 120mm or as required |
| ASTM B265 Titanium Alloy Gr 1 Plate Process | Hot/ Cold Rolled/forging |
| UNS R50400 Plate surface | No.1, No. 2D, No. 2B, BA, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled ASTM B265 Titanium Alloy Gr 1 Plate, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc. |
| ASTM B265 Titanium Alloy Gr 1 Plate, Sheet and Strip | JIS: N0, N2, N1, NW2200, NW2201, NW4400, NW5500, NW6002, etc |
| Titanium Grade 1 Sheet ASTM | ASTM B265 |
| Titanium Grade 1 Sheet AMS | AMS 4902 |
| Tolerances of width and thickness | EN 10258 (formerly DIN 59381),EN 10151 ASTM B265 Titanium Alloy Gr 1 strip for springs,EN 10088 ASTM B265 Titanium Alloy Gr 1 strip (general) |
| Ti 6Al 4v Grade 1 Titanium Plate standards and approvals | EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID |
| Standard Grade 1 ALLOY Plate & Sheet Sizes | 1000 x 2000 mm, 1220 x 2440 mm, 1500 x 3000 mm, 2000 x 2000 mm, 2000 x 4000 mm |
| Cold rolled Gr 1 Titanium Plate 0.5-6.4 mm | |
| Hot rolled Gr 1 Titanium Plate 3.0-60.0 mm | |
| UNS R50400 Plate Hardness | Soft, Hard, Half Hard, Quarter Hard, Spring Hard ASTM B265 Titanium Alloy Gr 1 Sheet suppliers |
| Availability of Titanium Alloy Gr 1 Foil sizes | Thickness : 8-100 microns (0.00031-0.004 in) |
| Width: Up to 500 mm (19.5 in) | |
| Weight (in rolls) : Up to 50 kg (110 lb); e.g. approxi- mately 1400 m at 8 microns and ap- proximately 112 m at 100 microns. | |
| Cutting | To provide a comprehensive service, we use a variety of cutting methods, including: |
| Laser Plate Cutting,Plasma Plate Cutting,Oxy-propane Flame Cutting | |
| Plasma profiles | As per customer's drawings |
| Value added services for Cp Grade 1 Titanium Plate | Laser cutting, Waterjet cutting, Plasma cutting, Bending and mechanical processing, edge preparation, welding, sawing and shearing. |
| China Grade 1 Titanium Plate Manufacturer | ASTM B265 Titanium Alloy Gr 1 Plate: material 3/16″ [5.00 mm] and over in thickness and over 10″ [250 mm] in width;Gr 1 Titanium Sheet: material under 3/16″ [5.00 mm] in thickness and 24″ [600 mm] and over in width;Alloy Titanium Grade 1 Clad plate: Alloy Titanium Grade 1 Clad plate is a composite steel plate made by bonding UNS R50400 Titanium Grade 1 Plate, etc.ASTM B265 Titanium Alloy Gr 1 Strip: cold-rolled material under 3/16″ [5.00 mm] in thickness and under 24″ [600 mm] in width. |
| UNS R50400 Plate Origin | CHINA |
| Packing of Grade 1 plate | Bundles with waterproof cloth outside or plywood box |
| Test | UT, SGS testing, TUV etc |
| Why buy UNS R50400 Sheet from DAXUN? | Free quote,Free sample,EN 10204 3.1,Mill Test Certificate is supplied with shipment.,NABL Approved Lab Reports,Any third party inspection is accepted.,Tested to ASTM A923 Method "C" or ASTM G48 Method "A".Minimum Nitrogen content and Ferrite Count Test |
Today, DAXUN Alloys stands as a premier global producer and supplier of superior Grade 1 titanium plates.
Pure Grade 1 titanium plates exhibit outstanding ductility and cold formability, making them perfect for deep drawing applications. Known for superior corrosion resistance in general and seawater environments, as well as resistance to oxidizing, neutral, and mildly reducing media, including chlorides. Titanium's low density-approximately half that of nickel-based alloys-coupled with a high strength-to-weight ratio and exceptional corrosion resistance, makes it an ideal choice for numerous challenging chemical conditions. Commercially pure Grade 1 titanium is the softest and most ductile, offering great cold formability, excellent corrosion resistance, superb weldability, and impressive impact hardness.
Producers of ASTM B265 Titanium Gr 1 Plates, Titanium Gr 1 Sheets, Finished Plates, Coil Suppliers, Hot Rolled Plates, Cold Rolled Plates, Patterned Plates Dealers, Perforated Plates, and Sheets and Plates Manufacturers in China.
We ensure our customers receive prompt and efficient delivery of Grade 1 titanium plate products. Our delivery speed is backed by an integrated system from production capacity to information and logistics flows. For instance, Daxun's order data is instantly pushed to the logistics system, ensuring seamless connectivity. Strategically located near highways, rivers, and seas, our processing center facilitates optimal scheduling, quick response times, and effective storage and transportation linkage, ensuring timely task completion.
Grade 1 titanium plate, with its lower density and high ductility, is ideal for industries prioritizing weight considerations and deep drawing processes. Key sectors include medical, chemical equipment, and aerospace. Additionally, its strength and corrosion resistance make it suitable for marine, chemical processing, and desalination applications. Common applications include oil and gas components, reaction and pressure vessels, piping systems, power systems, heat exchangers, linings, and flue gas desulfurization systems. Relevant standards: ASTM B265, ASTM F67, AMS4911, AMS4928, AMS4943, AMS4944, AMS4945, AMS4967, AMS4972.
The cold-rolled thickness range for Grade 1 Titanium Plates is 0.3 mm to 6.0 mm, available in hot rolled or heat-treated conditions. Hot-rolled thickness ranges from 4.76 mm to 155 mm, produced through longitudinal and transverse rolling. Plates can undergo creep flattening as a heat treatment to relieve internal stresses and meet specific flatness requirements. Custom shape cut blanks are available, with further processing-mechanical or chemical-tailored to meet customer requirements.
Chemical Composition of (Ti 6AL-4V) Grade 5 Titanium Sheet
| Chemical Composition: | |||
| Symbol | Element | Min % | Max % |
| Al | Aluminum | 5.50% | 6.75% |
| V | Vanadium | 3.50% | 4.50% |
| Fe | Iron | 0.30% | |
| O | Oxygen | 0.20% | |
| C | Carbon | 0.08% | |
| N | Nitrogen | 0.05% | |
| H | Hydrogen | 0.01% | |
| Y | Yttrium | 0.01% | |
| Other, each | 0.10% | ||
| Other, total | 0.40% | ||
| Ti | Titanium | Remainder | |
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
Chemical Composition of Grade 2 TitaniumSheet
| Element | Weight % |
| C | ≤0.08 |
| O | ≤0.25 |
| N | ≤0.03 |
| H | ≤0.015 |
| Fe | ≤0.30 |
| *OEE | ≤0.10 |
| *OET | ≤0.40 |
| Ti | Remaining |
Mechanical Properties of Grade 2 Titanium Sheet
| Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
| psi | MPa | ksi | psi | MPa | ksi | % | |||||||
| Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
| 50,000 | |||||||||||||
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
| Fe | 0.2 | ||
| O | 0.18 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
| Density | |
| lb/in3 | g/cm3 |
| 0.163 | 4.51 |
| Tensile Strength | |
| ksi | MPa |
| 35 min | 240 min |
| Yield Strength | |
| ksi | MPa |
| 20 min | 138 min |
| Hardness | |
| 70 HRC max | |
| Elongation | |
| 24% min |
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
|---|---|---|---|
| Al | 2.5 | 3.5 | |
| V | 2.0 | 3.0 | |
| Fe | 0.25 | ||
| O | 0.15 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
DAXUN is your premier metal specialist for both small and large-scale titanium plate projects. As a dedicated reference point and long-term partner, DAXUN stands ready to supply your business with top-tier titanium plates and comprehensive technical assistance. Consider DAXUN not just a supplier of pure industrial titanium and titanium alloy plates, but as a strategic ally, helping you overcome any hurdles and fulfilling your unique needs. With DAXUN, achieving your project goals has never been more attainable.
At DAXUN's service center in China, we maintain a robust inventory of titanium plate products, ensuring swift order processing. We offer enhanced value through basic processing, water jet cutting, and plate nesting services, designed to save our clients both time and money.
Thanks to continuous investments in our production facilities and strategic capacity agreements with our partners, DAXUN remains at the cutting edge of titanium plate quality today and into the future.
Get in touch with DAXUN today to access the latest pricing and technical details on our titanium plates.
| CP GR1 Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium plate PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
DAXUN: Premier Ti 6AL 4V-Grade 5-TC4 UNS R56400 Alloy Titanium Plate Manufacturer and Supplier from China! We are committed to pioneering the world's finest high-performance titanium alloy plates. Our swift global delivery encompasses ASTM B265 Grade 2 and Grade 5 Titanium Plates. At DAXUN, we manufacture and stock Grade 5 alloy titanium plates (UNS R56400) in thicknesses from 0.5mm to 300mm, where 0.5mm-6.0mm is cold rolled, 6.0-50mm is hot rolled, and anything above 50mm is forged. Grade 5 titanium plate (Ti-6Al-4V) stands as the quintessential titanium alloy material, celebrated for its high strength, ductility, and exceptional resistance to corrosion and high temperatures. It is extensively preferred in both general and military sectors. Compliance standards: ASTM, ASME, AMS, GB, GJB, MIL, JIS, EN, and more.
Ti-6Al-4V Grade 5 titanium plate is predominantly utilized in aerospace, military, power industry, vehicle armor, rocket precision guidance components, and the marine industry.
Titanium Grade 1
Currently, DAXUN Alloys stands at the forefront as a premier global producer and supplier of top-tier Grade 1 titanium plates.
Commercially pure Grade 1 titanium plate boasts outstanding ductility and cold formability, ideal for deep drawing applications. Renowned for exceptional resistance to general and seawater corrosion, as well as resilience against oxidizing, neutral, and mild reducing media (solutions) including chlorides. Titanium's low density (approximately half that of nickel-based alloys), combined with its high strength-to-weight ratio and corrosion resistance, makes it a prime choice for a myriad of challenging chemical conditions. Grade 1 titanium is the most ductile and softest commercially pure titanium, featuring excellent cold formability, superior corrosion resistance, outstanding weldability, and commendable impact hardness.
Producers of ASTM B265 Titanium Grade 1 Plates, Titanium Grade 1 Sheets, and Finished Plates. Suppliers of ASTM B265 Titanium Grade 1 Coils, Pure Titanium Gr 1 Hot Rolled Plates, Titanium Gr 1 Cold Rolled Plates. Dealers of Titanium ASTM B265 Grade 1 Sheets, Patterned and Perforated Plates. Manufacturers of Titanium Grade 1 Sheets and Plates in China.
Titanium Grade 2
DAXUN manufactures and stocks commercially pure titanium plates, Grade 2 (UNS R50400), in thicknesses from 0.5mm to 120mm. Grade 2 Titanium Plate (UNS R50400) is the workhorse of the commercially pure titanium family, offering a perfect synergy of high strength, ductility, and superb corrosion resistance for a multitude of industrial applications.
Grade 2 Titanium Plate is known for its unparalleled balance of strength and ductility. It exhibits outstanding impact strength and is highly weldable. It offers excellent corrosion resistance in heavily oxidizing environments, alkaline media, brine solutions, weakly reducing environments, and wet ***. Additionally, it demonstrates superior resistance to seawater and salt solutions.
With its low density, high strength-to-weight ratio, and robust corrosion resistance, titanium is an optimal material across various applications. It effectively counters stress corrosion cracking, pitting, and crevice corrosion in chloride solutions below 70°C. Boasting a melting point of 1660°C, Grade 2 Titanium Plate is the alloy of choice for most industrial uses necessitating good ductility and corrosion resistance.
DAXUN is a titan in both small and large titanium plate projects. As your reference point and long-term partner, DAXUN is dedicated to supplying titanium plates and offering extensive technical support. More than just a supplier, consider DAXUN your strategic partner, ready to help you navigate any challenges and fulfill your project objectives with precision and efficiency.
At DAXUN, our state-of-the-art service center in China boasts an extensive inventory of titanium plate products, ensuring rapid order fulfillment. By leveraging advanced processing techniques, including precision water jet cutting and efficient plate nesting, we add significant value for our customers, streamlining their operations and reducing both time and costs.
DAXUN's unwavering commitment to excellence is reflected in our continuous investment in cutting-edge production facilities and strategic capacity partnerships. These efforts solidify our position as a leader in titanium plate quality, now and well into the future.
Reach out to DAXUN today to access the most competitive prices and up-to-date technical information on our premium titanium plates.
Q1: What products can you offer?
A: We can offer a variety of general steel types, including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, and 316L 300.
Additionally, we provide 400 series and duplex stainless steels such as 2205, 2304, 2101, 2507, and high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
A: Yes, we can manufacture products based on your drawings to ensure complete satisfaction.
Q3. How does your factory manage quality control?
A: Quality is our top priority. We rigorously control quality from the initial stages to the final product.
Q4. Can I request a change in packaging and transportation format?
A: Yes, we can alter the packaging and transportation format per your request,
but you will need to cover any additional costs and the price differences incurred.
Q5. How does your factory manage quality control?
A: Quality is our top priority. We rigorously control quality from the initial stages to the final product.
Q6. What is the expected delivery time?
A: Delivery typically takes 7-20 working days after payment confirmation.
For urgent orders, we expedite the process to meet your timeline.
Q7. What payment methods do you accept?
A: We accept 100% T/T in advance, Western Union for small orders,
B: 30% T/T upfront and 70% balance before shipment,
C: 100% Irrevocable LC at sight for large orders.
Q8: Can you produce DDQ (Deep Drawing Quality) materials?
A: Yes, we can. Our materials are suitable for stainless steel pots, sinks, bowls, etc. Specify your usage, and we'll adjust the mechanical properties accordingly.
Q9: How can I get a sample?
A: FREE samples are available for your inspection and testing. For small pieces, we might cover the courier cost, depending on the situation.
Q10: Which countries have you exported to?
A: We have exported stainless steel materials to Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
Q11: How can I visit your company?
A: You can fly to Guangzhou Baiyun International Airport, and we will arrange a pick-up service for you.
){kind=link}