| Ti-6Al-4V Grade 5 Titanium pipe & Tubes Specification | ASTM B338 / ASTM B861 / ASTM B862 / ASME SB338 / ASME SB861 / ASME SB862 |
| Grade 5 Titanium pipe & Tubes Grades | Commercially pure titanium Grade 5-Ti-6Al4V- TC4- USN 56400 |
| Grade 5 Titanium pipe & Tubes Type | ot Rolled / Cold Drawn / Welded / ERW |
| Grade 5 Titanium pipe & Tubes Outer Diameter Size | Titanium seamless pipe - φ1.0mm to φ508.3mm |
| Titanium welded pipe - φ6.0mm to φ1219mm | |
| Grade 5 Titanium pipe & Tubes Wall Thickness | 1.0mm-50mm (customizable wall thickness) |
| Grade 5 Titanium pipe & Tubes Length | 5 to 7 Meters, 09 to 13 Meters, Single Random Length, Double Random Length And Customize Size. |
| Titanium pipe Form Ti-6Al-4V | ' Hollow, U' bent, LSAW, Hydraulic, Straight Tube, Boiler, Round, Tube Coil, Square, Rectangular Etc |
| Marking TC4 1.37165 | All Titanium Tubes Tubing are marked as follows: Grade, Standard, Thickness, OD, Heat No., Length (Or according to the customer's request.) |
| Uses of Titanium Alloy Tubes | Gas pipes, oil pipes, heat exchanger tubes, boiler tubes, fluid pipes, titanium exhaust pipes. |
| Grade 5 Titanium pipe & Tubes Pipe Ends | Plain Ends / Beveled Ends |
| Grade 5 Titanium pipe & Tubes Delivery Conditions | As Rolled, Cold Drawn, Hot Finish, Stress Relieved, Annealed, Hardened, Tempered |
| Grade 5 Titanium pipe & Tubes Coating | Electropolish, Mechanical Polish, Satin Finish, Passivated |
| Grade 5 Titanium pipe & Tubes Other Testing | ardness Test, Hydrostatic Test, Eddy Current test, Eddy Current, Tensile Test, Flattening, Flare Test, Annealed, Hydrostatic Test, Tempered, Stress Relieved etc. |
| Grade 5 Titanium pipe & Tubes Dimension | All Pipes Is Manufactured and Inspected / Tested to the Relevant standards including ASTM And ASME |
| Grade 5 Titanium pipe & Tubes Value Added Services | Draw / Expansion / Machining / Sand Blasting / Shot Blasting / Heat Treatment |
| Grade 5 Titanium pipe & Tubes Packaging | Loose / Bundle / Wooden Pallet / Wooden box-a / Plastic Cloth Wraps / Plastic End Caps / Beveled Protector |
| Grade 5 Titanium pipe & Tubes Shipment & Transportation | By Road - Truck / Train, By Sea - Break-bulk Conventional Vessel / FCL (Full Container Load) / LCL (Less Container Load) / 20 Feet Container / 40 Feet Container / 45 Feet Container / High Cube Container / Open Top Container, By Air - Freighter Civil Passenger and Cargo Planes |
| Grade 5 Titanium pipe & Tubes Material Test Certificate | Manufacturer Test Certificate As Per EN10204 3.1, 3.2 / Laboratory Test Certificate From NABL Approved Lab. / Under Third Party Inspection Agency Like SGS, TUV, DNV, LLOYDS, ABS ETC |
Grade 5 titanium tubes are widely embraced across various industries, especially under extreme corrosive conditions:
Daxun ensures unparalleled quality through a series of rigorous tests, including flattening, flaring, ultrasonic flaw detection, pitting and resistance, mechanical properties, hardness, material identification, and expansion tests. These comprehensive evaluations guarantee that Grade 1 Titanium Welded Pipe and Seamless Pipe materials meet application requirements. During production, we meticulously measure the diameter, thickness, and surface quality. Our standard delivery window stands at 5-7 days, with special size products delivered within 15-20 days.
The Ti-6Al4V Grade 5 Titanium Alloy Tube represents the pinnacle of commercial titanium alloys. Noted for its high strength and toughness, Grade 5 boasts excellent welding and processing attributes:
Our inventory includes Grade 5 Titanium Alloy Seamless Tubes, Forged Seamless Tubes, Welded Tubes, and more.
As a premier titanium alloy tube manufacturer and supplier based in China, Daxun Alloy delivers top-tier Grade 5 titanium pipes globally, earning accolades across numerous projects.
Ti 6Al-4V (Grade 5 Titanium) dominates the titanium alloy tube market, comprising over 50% of total titanium usage. Typically utilized in an annealed state, it operates efficiently up to 400°C (750°F). It is commonly welded with matching or ELI filler wire. Ti 6Al/4V offers superior strength compared to commercially pure titanium tubes, enhanced stiffness, and improved thermal properties (excluding thermal conductivity). Its thermal conductivity is approximately 60% lower than that of CP titanium. Grade 5's heat treatability allows for optimal strength and performance, coupled with excellent formability, low density, and superior corrosion resistance.
This Grade 5 titanium alloy stands as the epitome of strength, corrosion resistance, weldability, and machinability. Widely adopted across industries, it plays a pivotal role in military aircraft, aviation, rocket components, precision-guided parts, armor, naval equipment, and military vacuum systems. The closely related 6-4 ELI variant is a staple in surgical implants. Ideal for use in temperatures up to 400°C, it enhances ductility and toughness, especially in cold working conditions. Praised for its remarkable specific strength, this alloy is typically supplied in an annealed state, but can be heat-treated to boost strength for diverse applications. As a versatile, all-purpose titanium alloy, the Ti 6Al-4V titanium seamless tube offers exceptional properties across a temperature range of -210°C to 400°C. Grade 5 titanium alloy tube stands as the most commercialized titanium product, celebrated for its high strength, toughness, and excellent welding and processing characteristics.
Titanium Alloy Grade 5 Seamless Pipe, Titanium Gr 5 High Pressure Pipe, ASTM B338 Titanium Alloy Gr 5 Seamless Pipe, Titanium Gr 5 Thick Wall Pipe. As a leading China Titanium Grade 5 ERW Pipe Supplier, we offer premium Titanium Alloy Gr 5 Pipe, Titanium Gr 5 Electropolished Pipe, and Anti-corrosion Titanium Pipe. Our product range includes ASTM B338 Titanium Grade 5 Welded Pipe and ASTM B861 / ASME SB861 Titanium Grade 5 Seamless Pipe. Trust in our expertise as a China Titanium Gr-5 Seamless Pipe Manufacturer. Discover the excellence of Ti-6al-4v Pipe, whether you're in the market for ASTM B338 Titanium Grade 5 Pipe, Titanium Gr 5 Bright Annealed Pipe, Ti-6al-4v Pipe, Gr 5 Pipe, Titanium Gr 5 Pipe, or Titanium WERKSTOFF NR 3.7165 Pipe.
Exquisite Titanium Seamless Tubes
Daxun proudly produces:
Superior Hot-finished Titanium Tubes
Our premium tubes are available in the form of hot-rolled or hot-extruded, meticulously straightened, with machined inside and outside diameters, and beautifully surface polished. These titanium tubes can be supplied in either heat-treated or non-heat-treated forms, catering to diverse industry needs. Additionally, our state-of-the-art ultrasonic flaw detection ensures the highest quality standards.
Comprehensive Titanium Tube Materials Available:
Hot-rolled Titanium Tubes: Offering an outer diameter range from 19mm to 325mm, wall thickness from 9mm to 30mm, and lengths up to 5000mm, subject to mutual agreement between the manufacturer and the customer. - Hot-extruded Titanium Tubes: Available with an outer diameter of 50mm to 160mm, wall thickness of 7mm to 35mm, and lengths up to 3000mm, also subject to mutual agreement.
Precision Cold-finished Titanium Tubes
Our precision cold-finished titanium tubes are available in heat-treated, surface-etched, hydrostatically tested, or ultrasonically tested forms, aligning with rigorous manufacturing specifications. Tubes Supplied: - Outer diameter ranges from 6mm to 89mm, wall thickness from 0.5mm to 11mm, and lengths up to 6000mm, all customized on a case-by-case basis between the manufacturer and the customer.
High-Quality Titanium Welded Pipes
At DaXun, we manufacture and supply top-tier titanium pipes with diameters ranging from 12.7mm to 38.1mm (0.47in to 1.5in), wall thickness from 0.4mm to 1.65mm (0.016in to 0.065in, depending on diameter), and lengths up to 25000mm. Our titanium alloy pipes, available in Gr1, Gr2, and Gr12, are ideal for engineering and chemical industries. These welded pipes are crafted from flat rolled raw material via automatic tungsten inert gas (argon) welding on electric pipe welders, followed by meticulous heat treatment. The finished pipes undergo extensive mechanical testing, precise geometrical measurements, 100% ultrasonic and eddy current testing, and thorough pneumatic or hydrostatic testing. Each pipe is packed per customer specifications, ensuring compliance with ASTM B 338 and ASME SB 338 standards.
| CP GR1 Titanium tube PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium tube PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium tube PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
• ASTE B338 - Tubes: Titanium tubes standard, heat treatable
• AMS 4928 - Forgings and forging stock (annealed)
• AMS 4965 - Forgings (solution treated and aged)
• AMS 4967 - Forgings (annealed, heat treatable)
Typical hardness ranges from Rockwell C 30-34 in the annealed condition to Rockwell C 35-39 in the solution and aged condition.
Q1: What products can you offer?
A: We offer a diverse range of steel types, including general steel like 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L, along with 300 and 400 series steels. Additionally, we provide duplex stainless steel such as 2205, 2304, 2101, 2507, and high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
A: Absolutely, we can manufacture products tailored to your drawings to ensure they meet your utmost satisfaction.
Q3. How does your factory manage quality control?
A: Quality is our top priority. We consistently place great emphasis on quality control from the start to the finish of the production process.
Q4. Can I request to change the form of packaging and transportation?
A: Yes, we can adapt the packaging and transportation methods to meet your requests. However, please note that any additional costs incurred during this period, including the price differences, will be your responsibility.
Q5. How does your factory manage quality control?
A: Quality is our top priority. We consistently place great emphasis on quality control from the start to the finish of the production process.
Q6. What is the delivery time?
A: The delivery time ranges from 7 to 20 working days after payment confirmation.
If the order is urgent, we will prioritize it in our workshop to expedite completion.
Q7. What are your payment terms?
A: We accept the following payment terms:
B: 30% T/T upfront and the remaining 70% before shipment.
C: 100% Irrevocable LC at sight for large orders.
Q8: Can you produce Deep Drawing Quality (DDQ) materials?
A: Yes, we can. Our materials are suitable for making stainless steel pots, sinks, bowls, and more. Just let us know your specific usage, and we will adjust the mechanical properties to meet your requirements.
Q9: How can I obtain a sample?
A: FREE samples are available for your evaluation and testing. If you need a small piece, we can cover the courier cost depending on the situation.
Q10: Which countries have you exported to?
A: So far, we have exported our stainless steel materials to countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many others.
Q11: How can I visit your company?
A: You can fly to Guangzhou Baiyun International Airport, and we will arrange to pick you up from there.
){kind=link}