| Type: | Titanium Sheets |
|---|---|
| Application: | Industrial |
| Technique: | Hot Rolled |
| Grade: | GR1 |
| Shape: | Square |
| Thickness: | 0.3mm-120mm |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier
| CP Grade 1 Titanium Plate and sheet Type | Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate |
| Grade | ASME SB265,AMS 4911,AMS 4919,AMS 4914,ASTM F67,ASTM F136, MSRR, AMS, BS |
| Titanium Alloy Gr 1 Plate Length | 1000mm-13000mm or as required |
| Gr 1 Titanium Plate Width | 1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required |
| UNS R50400 Plate Thickness | 0.3 to 120mm or as required |
| ASTM B265 Titanium Alloy Gr 1 Plate Process | Hot/ Cold Rolled/forging |
| UNS R50400 Plate surface | No.1, No. 2D, No. 2B, BA, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled ASTM B265 Titanium Alloy Gr 1 Plate, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc. |
| ASTM B265 Titanium Alloy Gr 1 Plate, Sheet and Strip | JIS: N0, N2, N1, NW2200, NW2201, NW4400, NW5500, NW6002, etc |
| Titanium Grade 1 Sheet ASTM | ASTM B265 |
| Titanium Grade 1 Sheet AMS | AMS 4902 |
| Tolerances of width and thickness | EN 10258 (formerly DIN 59381),EN 10151 ASTM B265 Titanium Alloy Gr 1 strip for springs,EN 10088 ASTM B265 Titanium Alloy Gr 1 strip (general) |
| Ti 6Al 4v Grade 1 Titanium Plate standards and approvals | EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID |
| Standard Grade 1 ALLOY Plate & Sheet Sizes | 1000 x 2000 mm, 1220 x 2440 mm, 1500 x 3000 mm, 2000 x 2000 mm, 2000 x 4000 mm |
| Cold rolled Gr 1 Titanium Plate 0.5-6.4 mm | |
| Hot rolled Gr 1 Titanium Plate 3.0-60.0 mm | |
| UNS R50400 Plate Hardness | Soft, Hard, Half Hard, Quarter Hard, Spring Hard ASTM B265 Titanium Alloy Gr 1 Sheet suppliers |
| Availability of Titanium Alloy Gr 1 Foil sizes | Thickness : 8-100 microns (0.00031-0.004 in) |
| Width: Up to 500 mm (19.5 in) | |
| Weight (in rolls) : Up to 50 kg (110 lb); e.g. approxi- mately 1400 m at 8 microns and ap- proximately 112 m at 100 microns. | |
| Cutting | To provide a comprehensive service, we use a variety of cutting methods, including: |
| Laser Plate Cutting,Plasma Plate Cutting,Oxy-propane Flame Cutting | |
| Plasma profiles | As per customer's drawings |
| Value added services for Cp Grade 1 Titanium Plate | Laser cutting, Waterjet cutting, Plasma cutting, Bending and mechanical processing, edge preparation, welding, sawing and shearing. |
| China Grade 1 Titanium Plate Manufacturer | ASTM B265 Titanium Alloy Gr 1 Plate: material 3/16″ [5.00 mm] and over in thickness and over 10″ [250 mm] in width;Gr 1 Titanium Sheet: material under 3/16″ [5.00 mm] in thickness and 24″ [600 mm] and over in width;Alloy Titanium Grade 1 Clad plate: Alloy Titanium Grade 1 Clad plate is a composite steel plate made by bonding UNS R50400 Titanium Grade 1 Plate, etc.ASTM B265 Titanium Alloy Gr 1 Strip: cold-rolled material under 3/16″ [5.00 mm] in thickness and under 24″ [600 mm] in width. |
| UNS R50400 Plate Origin | CHINA |
| Packing of Grade 1 plate | Bundles with waterproof cloth outside or plywood box |
| Test | UT, SGS testing, TUV etc |
| Why buy UNS R50400 Sheet from DAXUN? | Free quote,Free sample,EN 10204 3.1,Mill Test Certificate is supplied with shipment.,NABL Approved Lab Reports,Any third party inspection is accepted.,Tested to ASTM A923 Method "C" or ASTM G48 Method "A".Minimum Nitrogen content and Ferrite Count Test |
Today, DAXUN Alloys stands as a premier global producer and supplier of superior Grade 1 titanium plates, affirming our commitment to quality and precision.
Pure Grade 1 titanium plates from DAXUN Alloys boast impressive ductility and cold formability, making them perfect for deep drawing applications. Known for their outstanding general and seawater corrosion resistance, these plates also withstand oxidizing, neutral, and mildly reducing solutions, including chlorides. The low density, approximately half that of nickel-based alloys, combined with high strength-to-weight ratio and superior corrosion resistance, make Grade 1 titanium an exceptional choice for harsh chemical environments. As the softest and most ductile commercial titanium, it offers excellent cold formability, corrosion resistance, weldability, and impact hardness.
We are distinguished producers of ASTM B265 Titanium Gr 1 Plates, Sheets, and Coils. Our offerings include Hot Rolled and Cold Rolled Plates, Patterned and Perforated Plates, and various Titanium Grade 1 products tailored to meet diverse industrial needs. Proudly manufacturing in China, we deliver premium quality titanium solutions.
At DAXUN Alloys, we ensure swift and timely delivery of Grade 1 titanium plates, powered by our advanced systems spanning production capacity, information flow, logistics, and capital flow. Our real-time data integration with logistics systems, strategic location near highways and water routes, efficient scheduling, and seamless storage and transportation coordination ensure reliable and punctual deliveries.
Grade 1 titanium plates, with their lower density and high ductility, are perfect for weight-sensitive industries and deep drawing processes. Key applications span across medical devices, chemical equipment, and aerospace. The exceptional strength and corrosion resistance of Grade 1 titanium make it ideal for marine, chemical processing, and desalination industries. Typical applications include oil and gas components, reaction and pressure vessels, piping systems, power generation, heat exchangers, linings, flue gas desulfurization systems, and various industrial components. Compliance with standards such as ASTM B265, ASTM F67, AMS4911, AMS4928, AMS4943, AMS4944, AMS4945, AMS4967, and AMS4972 ensures top-notch quality and reliability.
Our cold rolled Grade 1 Titanium Plates range from 0.3 mm to 6.0 mm in thickness, supplied in hot rolled or heat treated conditions. The hot rolled thickness spans from 4.76 mm to 155 mm, produced through longitudinal and transverse rolling. We offer creep flattening as a heat treatment to relieve internal stresses and meet special flatness requirements. Plates can be customized into cut blanks with complex shapes, ready for further mechanical or chemical processing as per customer needs.
About the chemical composition of (Ti 6AL-4V) Grade 5 titanium sheet
| Chemical Composition: | |||
| Symbol | Element | Min % | Max % |
| Al | Aluminum | 5.50% | 6.75% |
| V | Vanadium | 3.50% | 4.50% |
| Fe | Iron | 0.30% | |
| O | Oxygen | 0.20% | |
| C | Carbon | 0.08% | |
| N | Nitrogen | 0.05% | |
| H | Hydrogen | 0.01% | |
| Y | Yttrium | 0.01% | |
| Other, each | 0.10% | ||
| Other, total | 0.40% | ||
| Ti | Titanium | Remainder | |
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
About the chemical composition of Grade 2 titaniumsheet
| Element | Weight % |
| C | ≤0.08 |
| O | ≤0.25 |
| N | ≤0.03 |
| H | ≤0.015 |
| Fe | ≤0.30 |
| *OEE | ≤0.10 |
| *OET | ≤0.40 |
| Ti | Remaining |
About the mechanical properties of Grade 2 titanium sheet
| Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
| psi | MPa | ksi | psi | MPa | ksi | % | |||||||
| Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
| 50,000 | |||||||||||||
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
| Fe | 0.2 | ||
| O | 0.18 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
| Density | |
| lb/in3 | g/cm3 |
| 0.163 | 4.51 |
| Tensile Strength | |
| ksi | MPa |
| 35 min | 240 min |
| Yield Strength | |
| ksi | MPa |
| 20 min | 138 min |
| Hardness | |
| 70 HRC max | |
| Elongation | |
| 24% min |
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
|---|---|---|---|
| Al | 2.5 | 3.5 | |
| V | 2.0 | 3.0 | |
| Fe | 0.25 | ||
| O | 0.15 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
DAXUN: Your Ultimate Titanium Solution Expert. Specializing in both small and large-scale titanium plate projects, DAXUN is not just a supplier but your trusted partner in the journey of achieving excellence. Offering an extensive range of industrial pure titanium plates and titanium alloy plates, DAXUN stands as your strategic ally, ready to overcome any challenges and meet all your business needs. With DAXUN by your side, realize your project goals and elevate your enterprise to new heights.
Experience Unmatched Efficiency with DAXUN's Service Center in China. Our expansive stock of titanium plate products ensures rapid order processing. Through advanced basic processing, precise water jet cutting, and efficient plate nesting services, DAXUN adds unparalleled value, saving you both time and costs. Partner with us and gain a competitive edge in your market.
Pioneering the Future of Titanium Plate Quality. DAXUN's relentless investment in cutting-edge production facilities, coupled with strategic capacity agreements with our partners, ensures that we remain at the pinnacle of titanium plate excellence, now and in the future. Trust in our commitment to quality and innovation.
Reach Out to DAXUN Today. Discover the latest in titanium plate pricing and access comprehensive technical information. Secure your path to success with DAXUN's expert guidance and premier products.
| CP GR1 Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium plate PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
DAXUN is a premier Ti 6AL 4V-Grade 5-TC4 UNS R56400 Alloy Titanium Plate Manufacturer and Supplier based in China! Our mission is to create the world's most high-performance titanium alloy plates. We ensure swift worldwide deliveries of ASTM B265 Grade 2 and Grade 5 Titanium Plates. DAXUN offers and maintains a large inventory of alloy titanium plates Grade 5 (UNS R56400) with thicknesses ranging between 0.5mm and 300mm (0.5mm-6.0mm is cold rolled; 6.0-50mm is hot rolled; and 50mm and above are forged). Grade 5 titanium plate (Ti-6Al-4V) is renowned as the 'workhorse' of titanium alloy materials. It marries high strength, ductility, and superior corrosion and high-temperature resistance, making it highly esteemed in both general and military industries. Our products comply with standards such as ASTE, ASME, AMS, GB, GJB, MIL, JIS, EN, etc.
The Ti-6Al-4V Grade 5 titanium plate is predominantly utilized in aerospace, military industry, power industry, vehicle armor, rocket precision guidance parts, and the marine industry.
Grade 1
Today, DAXUN Alloys proudly stands as a leading global producer and supplier of premium-quality Grade 1 titanium plates.
Pure Grade 1 titanium plate is distinguished by its remarkable ductility and cold formability, making it ideal for deep drawing. Grade 1 titanium is celebrated for its excellent overall and seawater corrosion resistance, as well as its resilience against oxidizing, neutral, and mildly reducing media (solutions), including chlorides. With a low density (nearly half that of nickel-based alloys), high strength-to-weight ratio, and exceptional corrosion resistance, it is an outstanding choice for various demanding chemical environments. Commercially pure Grade 1 titanium is the softest and most ductile variant, offering superb cold formability, outstanding corrosion resistance, and excellent weldability combined with good impact hardness.
Producers of ASTM B265 Titanium Gr 1 Plates, Titanium Gr 1 Sheets, Finished Titanium Gr 1 Plates, Suppliers of ASTM B265 Titanium Grade 1 Coils, Hot Rolled Pure Titanium Gr 1 Plates, Cold Rolled Titanium Gr 1 Plates, Comprehensive Range of Titanium ASTM B265 Gr 1 Sheets, Dealers of Gr 1 Titanium Patterned and Perforated Plates, and Leading Manufacturers of Titanium Grade 1 Sheets and Plates in China.
Grade 2
DAXUN manufactures and maintains a comprehensive stock of commercially pure titanium plates Grade 2 (UNS R50400) in thicknesses from 0.5mm to 120mm. Grade 2 Titanium Plate (UNS R50400) is the 'workhorse' of the commercially pure titanium family, renowned for its excellent balance of high strength, ductility, and superb corrosion resistance, making it suitable for numerous industrial applications.
Grade 2 Titanium Plate, a commercially pure titanium plate, offers a superior balance between strength and ductility. It boasts good impact strength and ease of welding, along with excellent corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, weakly reducing environments, and wet ***. Additionally, it provides excellent resistance to seawater and salt solutions.
Titanium's low density, high strength-to-weight ratio, and remarkable corrosion resistance render it ideal for a myriad of applications. It demonstrates effective resistance against stress corrosion cracking, pitting, and crevice corrosion in chloride solutions below 70°C. With a melting point of 1660°C, Grade 2 Titanium Plate is the preferred alloy for most industrial applications demanding good ductility and corrosion resistance.
DAXUN is a distinguished metal expert adept at handling both small and large titanium plate projects. DAXUN is your invaluable reference point and long-term partner, ready to supply you with titanium plates and any technical assistance you require. Consider DAXUN not just as your supplier of industrial pure titanium and titanium alloy plates, but as your strategic partner, dedicated to helping you navigate any challenges and achieve your project goals with precision and efficiency.
DAXUN's premier service center in China offers an extensive inventory of titanium plate products, ready for swift order fulfillment. Leveraging basic processing, state-of-the-art water jet cutting, and efficient plate nesting, we deliver exceptional value to our customers, significantly reducing both time and costs.
At DAXUN, our unwavering commitment to continuous investment in cutting-edge production facilities, coupled with strategic capacity agreements with our esteemed partners, ensures that we consistently lead the market in titanium plate quality, both now and in the future.
Reach out to DAXUN today for the most competitive titanium plate prices and comprehensive technical information tailored to your needs.
Q1: What products can you offer?
A: We offer a wide range of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, and 316L. Our product line also includes 400 series steels and high-nickel alloys such as 904L, 800H, and 600H.
Additionally, we specialize in duplex stainless steel, featuring grades such as 2205, 2304, 2101, and 2507.
Q2. Can you produce the products according to my own drawings?
Absolutely, we can manufacture products tailored to your specific drawings, ensuring they meet and exceed your expectations.
Q3. How does your factory do regarding quality control?
Quality is our top priority. We meticulously control quality from the initial stages to the final product, ensuring excellence throughout the entire production process.
Q4. Can I request to change the form of packaging and transportation?
Yes, we can customize the packaging and transportation methods as per your requirements,
but please note that any additional costs incurred during this process will be your responsibility.
Q5. How does your factory do regarding quality control?
Quality is our top priority. We meticulously control quality from the initial stages to the final product, ensuring excellence throughout the entire production process.
Q6. How long is the delivery time?
A: Standard delivery time is 7-20 working days post-payment confirmation.
For urgent orders, we expedite our workflow to meet your deadlines.
Q7. What is your Payment?
A: 100% T/T in advance, Western Union (for small orders).
B: 30% T/T upfront with the remaining 70% payable before shipment.
C: 100% Irrevocable LC at sight (for large orders).
Q8: Can you make DDQ (Deep Drawing Quality)?
A: Yes, we can. Our materials are suitable for stainless steel pots, sinks, and bowls. Share your specific application, and we will adjust the mechanical properties to meet your requirements.
Q9: How to get a sample?
A: FREE samples are available for your review and testing. For small pieces, we may cover the courier costs, depending on the circumstances.
Q10: Which countries have you exported to?
A: We have successfully exported stainless steel materials to Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many more.
Q11: How to visit your company?
A: Fly to Guangzhou Baiyun International Airport, and we will arrange to pick you up.
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}