| Product Parameters: Stainless Steel rod | |
| Material | 410 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
ASTM A479 AISI 410 Stainless Steel Round Bar, ASTM A479 SS 410 Square Bar, 410 Stainless Steel Flat Bar, Stainless Steel 410 Rod. Extensive range of Stainless Steel 410 Round Bar, SS 410 Round Bar, SS DIN 1.4006 Round Bar manufacturers. Buy Stainless Steel 410 Bright Bar, 410 SS Polished Bar, SS 410 Rod suppliers. China AISI SS 410 Round Bar producers.
For more information on stainless steel rods, please contact Daxun.
410 Stainless Steel Rod Chemical Composition
| UNS No | S41000 |
| EN | 1.4006 |
| AISI | 410 |
| Carbon (C) | 0.08/0.15 |
| Silicon (Si) | 1 |
| Manganese (Mn) | 1 |
| Phosphorus (P) | 0.04 |
| *** (S) | 0.03 |
| Chromium (Cr) | 11.5/13.5 |
| Molybdenum (Mo) | |
| Nickel (Ni) | 0.75 |
| Property | Value |
| Density | 7.8 g/cc |
| Yield Strength | 1,225 MPa at a strain of 0.2% |
| Ultimate Tensile Strength | 1,525 MPa |
| Hardness | 126-192 Brinell hardness (annealed condition) 201-255 Brinell hardness (when hardened and tempered) |
| Bulk Modulus | 200 GPa |
| Melting Point | 1,480-1,530 °C |
| Corrosion Resistance | Good corrosion resistance in mild atmospheric environments, water, and some mild chemical environments. It shows pitting corrosion and brown staining in salt water conditions and offers lower resistance to acidic environments than the austenitic stainless steel alternatives. |
| Magnetism | Permeability 700-1,000. Highly responsive to magnetic fields, act as a strong magnetic flux carrier due to its martensitic structure. |
| Density (lb./ in^2) @ RT | 0.28 | |
| Modulus of Elasticity in Tension (psi x 10^6) | 29 | |
| Specific Heat (BTU/o F/lb.) | 32 to 212 oF | 0.11 |
| Thermal Conductivity (BTU/hr/ft^2/ft) | 212oF | 14.4 |
| 932oF | 16.6 | |
| Mean Coefficient of Thermal Expansion (in. x 10^-6 per o F) | 32 to 212oF | 5.5 |
| 32 to 1,200oF | 6.5 | |
| Electrical Resistivity (micro ohms - cm) | at 70oF | 22.5 |
Our advanced forming capabilities include state-of-the-art radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills for manufacturing titanium rods. We also employ a unique hydroforming process for producing high-quality parts.
Our stainless steel rod heat treatments utilize advanced furnace equipment to ensure material stability and superior performance.
At Daxun Stainless Steel, we employ the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace. These technologies minimize impurities in the smelting process, significantly enhancing the performance of our finished stainless steel rods.
Our stainless steel products come with full certification and traceability, ensuring the highest level of quality. We proudly serve leading industries such as aerospace, industrial, medical, marine, and military sectors, providing them with top-tier stainless steel solutions.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
APPLICATIONS:
CORROSION RESISTANCE:
Features:
Available Stock Sizes:
For unique sizes, please check specific product pages or contact us for a quote on custom size orders.
410 Stainless steel round bars are immensely versatile, finding applications across numerous sectors from construction to automotive parts. Recognizing the broad spectrum of uses, Daxun Alloys offers these round bars in multiple grades and sizes. Our advanced cutting service ensures precise fulfillment of your specifications every time.
Can you manufacture SS grinding bars & rods?
Absolutely! We specialize in producing SS grinding bars & rods with exceptional precision in dimension, roundness, and straightness, surpassing the quality of standard stainless steel polished bars. Please note, the processing cost is slightly higher.
Q1: What products can you offer?
A: We offer a broad range of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, and 316L.
We also provide the 400 series and duplex stainless steel such as 2205, 2304, 2101, 2507, etc., as well as high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
Yes, we can manufacture products according to your drawings to ensure they meet your precise specifications and satisfaction.
Q3. How does your factory handle quality control?
Quality is our top priority. We meticulously control quality throughout the entire production process, from start to finish.
Q4. Can I request to change the form of packaging and transportation?
Yes, we can modify the packaging and transportation methods to suit your preferences.
However, you will be responsible for any additional costs incurred during this period and the price differences.
Q5. How does your factory handle quality control?
Quality is our top priority. We meticulously control quality throughout the entire production process, from start to finish.
Q6. What is the usual delivery time?
A: Typically, delivery takes 7~20 working days after payment confirmation.
For urgent orders, we will expedite the process to complete it as soon as possible.
Q7. What are your payment terms?
A: 100% T/T in advance, or Western Union for small orders.
B: 30% T/T upfront and the remaining 70% before shipment.
C: 100% Irrevocable LC at sight for large orders.
Q8: Can you produce DDQ (Deep Drawing Quality) materials?
A: Yes, we can. Our materials are suitable for stainless steel pots, sinks, bowls, and more. Let us know your specific use case, and we will tailor the mechanical properties to meet your requirements.
Q9: How can I obtain a sample?
A: FREE samples are available for evaluation. For small pieces, we may cover courier costs depending on the situation.
Q10: Which countries have you exported to?
A: We have exported our stainless steel materials to countries including Vietnam, Thailand, Turkey, Russia, Morocco, South Korea, India, Pakistan, UAE, Ukraine, and more.
){kind=link}