| Type: | Titanium Sheets |
|---|---|
| Application: | Industrial |
| Technique: | Hot Rolled |
| Grade: | Gr5 Ti-6al-4V Gr7 Gr9 Gr23 |
| Shape: | Square |
| Thickness: | 0.3mm-120mm |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier
| Titanium Plate and sheet Type | Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate |
| Grade | ASME SB265,AMS 4911,AMS 4919,AMS 4914,ASTM F67,ASTM F136, MSRR, AMS, BS |
| Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate Length | 1000mm-13000mm or as required |
| Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Titanium Plate Width | 1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required |
| UNS Plate Thickness | 0.3 to 120mm or as required |
| ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate Process | Hot/ Cold Rolled/forging |
| UNS Plate surface | No.1, No. 2D, No. 2B, BA, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc. |
| ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate, Sheet and Strip | JIS: N0, N2, N1, NW2200, NW2201, NW4400, NW5500, NW6002, etc |
| DIN:H-Ni99.96, H-Ni99.95, H-Ni99.92, H-Ni99.90, H-Ni99.5, H-Ni99, etc | |
| Titanium Gr1 Gr2 Gr3 Gr4 Gr5 Sheet ASTM | ASTM B265 |
| Titanium Gr1 Gr2 Gr3 Gr4 Gr5 Sheet AMS | AMS 4902 |
| Tolerances of width and thickness | EN 10258 (formerly DIN 59381),EN 10151 ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 strip for springs,EN 10088 ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 strip (general) |
| Cp Gr1 Gr2 Gr3 Gr4 Gr5 Titanium Plate standards and approvals | EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID |
DAXUN excels in producing and maintaining an extensive inventory of commercially pure titanium plates, available in Gr1, Gr2, Gr3, and Gr4 (UNS) grades, with thicknesses ranging from a delicate 0.5 mm to a robust 120 mm. This versatile titanium plate, often lauded as the 'workhorse,' is treasured for its superb blend of high strength, remarkable ductility, and outstanding corrosion resistance, making it a cornerstone in various industrial applications.
The Gr1, Gr2, Gr3, and Gr4 titanium plates stand as paragons of commercially pure titanium excellence, perfectly balancing strength and ductility. Not only do they boast impressive impact strength, but they are also remarkably easy to weld. Their superior corrosion resistance shines in harsh, oxidizing environments, alkaline media, brine solutions, and wet ***. Moreover, they exhibit impeccable resistance to seawater and salt solutions.
Introducing the Gr5 grade5 Ti6Al4V titanium plate, a superior titanium alloy plate comprising 90% titanium, 6% aluminum, and 4% vanadium. This α-β type titanium alloy is masterfully engineered, with aluminum stabilizing the α phase and vanadium stabilizing the β phase. Renowned for its outstanding comprehensive performance, the Gr5 Ti-6Al-4V titanium alloy plate excels in both room temperature and high-temperature strength, offers remarkable creep resistance and thermal stability, and demonstrates high fatigue performance and *** growth resistance in seawater. Its notable fracture toughness and resistance to hot salt stress corrosion, combined with excellent process plasticity and superplasticity, make it adaptable to diverse processing, welding, and machining methods.
About the chemical composition of (Ti 6AL-4V) grade 5 titanium sheet
| Chemical Composition: | |||
| Symbol | Element | Min % | Max % |
| Al | Aluminum | 5.50% | 6.75% |
| V | Vanadium | 3.50% | 4.50% |
| Fe | Iron | 0.30% | |
| O | Oxygen | 0.20% | |
| C | Carbon | 0.08% | |
| N | Nitrogen | 0.05% | |
| H | Hydrogen | 0.01% | |
| Y | Yttrium | 0.01% | |
| Other, each | 0.10% | ||
| Other, total | 0.40% | ||
| Ti | Titanium | Remainder | |
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
About the chemical composition of grade 2 titaniumsheet
| Element | Weight % |
| C | ≤0.08 |
| O | ≤0.25 |
| N | ≤0.03 |
| H | ≤0.015 |
| Fe | ≤0.30 |
| *OEE | ≤0.10 |
| *OET | ≤0.40 |
| Ti | Remaining |
About the mechanical properties of grade 2 titanium sheet
| Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
| psi | MPa | ksi | psi | MPa | ksi | % | |||||||
| Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
| 50,000 | |||||||||||||
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
| Fe | 0.2 | ||
| O | 0.18 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
| Density | |
| lb/in3 | g/cm3 |
| 0.163 | 4.51 |
| Tensile Strength | |
| ksi | MPa |
| 35 min | 240 min |
| Yield Strength | |
| ksi | MPa |
| 20 min | 138 min |
| Hardness | |
| 70 HRC max | |
| Elongation | |
| 24% min |
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
|---|---|---|---|
| Al | 2.5 | 3.5 | |
| V | 2.0 | 3.0 | |
| Fe | 0.25 | ||
| O | 0.15 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
1. Cold-Rolled Titanium Plates: These exceptional plates are crafted through plate rolling, with the final stage being meticulous cold rolling. Available in work-hardened or heat-treated conditions, our sheets cater to your precise needs. Choose from mechanical or chemical processing based on your specific requirements for unparalleled results. 2. Hot-Rolled Titanium Plates: Masterfully produced by both longitudinal and transverse rolling, these plates come in thicknesses ranging from 3.0mm to 155mm and are supplied in a heat-treated state. For special flatness requirements, creep flattening can be employed. Available as cut blanks, they can be shaped into complex parts from the parent metal, tailored precisely to your needs.3. Forged Titanium Plates: Expertly produced by forging steel ingots on a vertical hydraulic press followed by rolling, or through open die forging, the dimensions of these slabs reach up to 580 mm in thickness, 2000 mm in width, and 6000 mm in length. Custom measurements and weights are agreed upon between the manufacturer and you, ensuring a perfect fit for your requirements.
| CP GR1 Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium plate PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
DAXUN, a prestigious manufacturer and supplier from China, specializes in producing Ti 6AL 4V-Grade 5-TC4 UNS R56400 Alloy Titanium Plates. We are dedicated to crafting the world's premier high-performance titanium alloy plates and ensuring swift global delivery. Our offerings include ASTM B265 Grade 2 and Grade 5 Titanium Plates. We stock and produce Grade 5 titanium alloy plates (UNS R56400) in thicknesses from 0.5mm to 300mm. Plates from 0.5mm to 6.0mm are cold-rolled, from 6.0mm to 50mm are hot-rolled, and those above 50mm are forged. Recognized as the 'workhorse' of titanium materials, Grade 5 titanium plates (Ti-6Al-4V) combine superior strength, ductility, and outstanding resistance to corrosion and high temperatures, making them invaluable for general and military applications. Our products meet standards such as ASTM, ASME, AMS, GB, GJB, MIL, JIS, and EN.
The Ti-6Al-4V Grade 5 Titanium Plate finds extensive use in sectors like aerospace, military, power industry, vehicle armor, precision guidance parts for rockets, and marine industry, testament to its versatile and robust properties.
Grade 1
Today, DAXUN Alloys stands at the forefront as a leading global producer and supplier of top-tier Grade 1 titanium plates.
Pure Grade 1 titanium plates are distinguished by their exceptional ductility and cold formability, making them ideal for deep drawing applications. Renowned for their excellent resistance to general corrosion and seawater, they also withstand oxidizing, neutral, and mildly reducing media, including chlorides. Titanium's low density, approximately half that of nickel-based alloys, combined with a high strength-to-weight ratio and superior corrosion resistance, makes Grade 1 an optimal choice for harsh chemical environments. It is the softest and most ductile of commercially pure titanium grades, offering excellent cold formability, corrosion resistance, weldability, and impact hardness.
DAXUN excels as a producer of ASTM B265 Titanium Gr 1 Plates, offering a variety of products including Titanium Gr 1 Sheets, Finished Plates, Coils, Hot Rolled Plates, Cold Rolled Plates, Patterned Plates, and Perforated Plates. As a leading manufacturer in China, we pride ourselves on delivering high-quality Titanium Grade 1 Sheets and Plates.
Grade 2
DAXUN offers commercially pure titanium plates, Grade 2 (UNS R50400), with thicknesses ranging from 0.5mm to 120mm. Known as the 'workhorse' of pure titanium, Grade 2 plates combine high strength, ductility, and excellent corrosion resistance, catering to a multitude of industrial applications.
Grade 2 Titanium Plates, being commercially pure, provide an exceptional balance of strength and ductility. They exhibit excellent impact strength, weldability, and corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, weakly reducing environments, and wet ***. Furthermore, they offer superb resistance to seawater and salt solutions.
With its low density, high strength-to-weight ratio, and exceptional corrosion resistance, titanium is ideal for diverse applications. Grade 2 Titanium Plates effectively resist stress corrosion cracking, pitting, and crevice corrosion in chloride solutions below 70°C. With a high melting point of 1660°C, they are the preferred choice for industrial applications that demand excellent ductility and corrosion resistance.
At DAXUN, we pride ourselves on being experts in both small and large titanium plate projects. Our commitment extends beyond supply; we aim to be your reference point and long-term partner, providing comprehensive technical assistance. Consider DAXUN not only as your supplier of industrial pure titanium and alloy plates but also as your strategic partner, ready to help you overcome any challenges and achieve your project goals.
At DAXUN's premier service center in China, we maintain a robust inventory of high-quality titanium plate products, enabling swift order fulfillment. By offering fundamental processing, precision water jet cutting, and efficient plate nesting services, we deliver exceptional value to our clients, significantly reducing both their time and costs.
DAXUN's unwavering commitment to continuous investment in our state-of-the-art production facilities, coupled with strategic capacity agreements with our esteemed partners, ensures that we remain at the pinnacle of titanium plate excellence, both now and in the foreseeable future.
Reach out to DAXUN today to discover the most competitive titanium plate prices and acquire detailed technical specifications. Your satisfaction is our priority.
Q1: What products can you offer?
A: We proudly offer a diverse range of top-quality steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, and 316, as well as the entire 300 series.
Our selection also features the 400 series and an array of duplex stainless steels such as 2205, 2304, 2101, and 2507. Additionally, we provide 904L, 800H, 600H high-nickel alloys.
Q2. Can you produce the products according to my own drawings?
Absolutely, we can craft products tailored to your specific drawings to ensure they meet your utmost satisfaction.
Q3. How does your factory do regarding quality control?
Quality is our utmost priority. We consistently emphasize rigorous quality control from the initial stages to the final product.
Q4. Can I request to change the form of packaging and transportation?
Yes, we can modify packaging and transportation forms based on your preferences.
Please note that any additional costs incurred during this process will be your responsibility.
Q5. How does your factory do regarding quality control?
Quality is our utmost priority. We consistently emphasize rigorous quality control from the initial stages to the final product.
Q6. How long is the delivery time?
A: Delivery typically ranges from 7 to 20 working days after payment confirmation.
For urgent orders, we can expedite production to meet your timeline requirements.
Q7. What is your Payment?
A: 100% T/T in advance, Western Union for smaller orders.
B: 30% T/T upfront and the remaining 70% before shipment.
C: 100% Irrevocable LC at sight for large orders.
Q8: Can you make DDQ (Deep Drawing Quality)?
A: Yes, we specialize in DDQ materials suitable for stainless steel pots, sinks, bowls, etc. Share your specific use case, and we'll tailor the mechanical properties to meet your needs.
Q9: How to get a sample?
A: We offer FREE samples for your evaluation and testing. If you need a small piece, we can cover the courier cost depending on the situation.
Q10: Which countries have you exported to?
A: To date, we've proudly exported stainless steel materials to Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many more.
Q11: How can I visit your company?
A: You can fly to Guangzhou Baiyun International Airport, and we will arrange to pick you up from there.
Suppliers with verified business licenses