| Product Parameters: Stainless Steel rod | |
| Material | 304 304L |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
For in-depth details on stainless steel rods, connect with Daxun.
304 Stainless Steel Rod Chemical Composition
Chemical Composition (wt%) Limits as Specified in ASTM A240 and ASME SA240*.
| Element | 304 | 304L |
| Carbon | 0.07 | 0.03 max |
| Chromium | 18.0-19.5 | 18.0-19.5 |
| Nickel | 8.0-10.5 | 8.0-12.0 |
| Manganese | 2.00 | 2.00 |
| Silicon | 0.75 | 0.75 |
| Nitrogen | 0.10 | 0.10 |
| Phosphorus | 0.045 | 0.045 |
| Sulfur | 0.030 | 0.030 |
304 Stainless Steel Rod Mechanical Properties
Mechanical property requirements for annealed products as defined in ASTM A240 and ASME SA240.
| Property | 304 | 304L |
| Yield Strength, min. (ksi) | 30 | 25 |
| Tensile Strength, min. (ksi) | 75 | 70 |
| Elongation, min. (%) | 40 | 40 |
| Hardness, max. (Rb) | 92 | 92 |
304 Stainless Steel Rod Physical Properties
Physical properties for Type 304/304L stainless steel.
| Property | 304/304LData |
| Density, lb/in3 | 0.285 |
| Modulus of Elasticity, psi | 28 x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 9.2 x 10-6 |
| Thermal Conductivity, Btu/ft hr ˚F | 9.4 |
| Specific Heat, Btu/lb ˚F | 0.12 |
| Electrical Resistivity, Microohm-in | 28.3 |
Our forming capabilities include state-of-the-art radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills. We also employ a unique hydroforming process for manufacturing parts.
Our advanced heat treatment furnace guarantees the stability and high performance of our stainless steel rods through meticulous heat treatment processes.
At Jiangsu Daxun Alloy Co., Ltd., our stainless steel is crafted using the most sophisticated smelting technology available. Utilizing state-of-the-art equipment including a vacuum induction furnace, vacuum consumable furnace, and electroslag furnace, we meticulously reduce impurities during the smelting process. This advanced methodology ensures that our 304L and 304 stainless steel round rods boast superior performance, reliability, and quality, setting a new benchmark in the industry.
Our stainless steel products come with full certifications and traceability. We deliver the finest quality stainless steel to top-tier industries such as aerospace, industrial, medical, marine, and military sectors.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
The DAUXN 304/304L Stainless Steel RODS are versatile, finding use in a broad spectrum of domestic and industrial applications, such as:
Can you provide stainless steel grinding bars and rods?
Absolutely, we specialize in SS grinding bars and rods with precision in dimension, roundness, and straightness, surpassing stainless steel polished bars. Please note, the processing cost is higher for these specialized products.
Q1: What products can you offer?
A: We offer a broad range of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, and 316L.
Additionally, we provide the 400 series, duplex stainless steel such as 2205, 2304, 2101, 2507, and high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
Yes, we can manufacture products precisely according to your drawings, ensuring the utmost satisfaction.
Q3. How does your factory handle quality control?
Quality is our top priority. We emphasize stringent quality control from the start to the finish of the production process.
Q4. Can I request changes to the packaging and transportation methods?
Certainly, we can modify the packaging and transportation methods as per your request.
However, please note that any additional costs and differences incurred will be your responsibility.
Q5. How does your factory handle quality control?
Quality is our top priority. We emphasize stringent quality control from the start to the finish of the production process.
Q6. What is the typical delivery time?
A: Our usual delivery time is 7 to 20 working days after payment confirmation.
For urgent orders, we will expedite the production process to meet your deadlines.
Q7. What are your payment terms?
A: We accept 100% T/T in advance or Western Union for small orders.
B: We also accept 30% T/T in advance, with the remaining 70% before shipment.
C: For large orders, we accept 100% Irrevocable LC at sight.
Q8: Can you produce Deep Drawing Quality (DDQ) material?
A: Yes, we can. Our materials are suitable for stainless steel pots, sinks, bowls, etc. Let us know your specific usage, and we'll adjust the mechanical properties to meet your needs.
Q9: How can I obtain a sample?
A: We provide FREE samples for your evaluation. For small pieces, we may cover the courier cost depending on the situation.
Q10: Which countries have you exported to?
A: We have successfully exported our stainless steel materials to countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
){kind=link}