| Customization: | Available |
|---|---|
| Type: | Stainless Steel Bars |
| Standard: | ASTM, AISI, GB, JIS, DIN, EN |
|
Still deciding? Get samples of US$ 1/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Product Parameters: Stainless Steel rod | |
| Material | 2507 S32750 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
ASTM A276 Super Duplex Steel S32750 Round Bar, Super Duplex Steel Bar Supplier, Super Duplex Steel UNS S32760 Bright Bar, Super Duplex Steel 2507 Bar, Super Duplex Steel UNS S32950 Flat Bar, Austenitic Super Duplex Steel S32760 Round Bar, Hot Rolled Super Duplex Steel S32760 Round Bar, Super Duplex Steel S32760 Round Bar, Super Duplex Steel UNS S32750 Manufacturer from China.
For more information on stainless steel rods, please contact Daxun.
2507 Stainless Steel Rod Chemical Composition
| Grade | Super Duplex 2507 |
| UNS Designation | S32750 |
| Carbon (C) Max. | 0.03 |
| Manganese (Mn) Max. | 1.2 |
| Phosphorous (P) Max. | 0.035 |
| *** (S) Max. | 0.02 |
| Silicon (Si) Max. | 0.8 |
| Chromium (Cr) | 24.0-26.0 |
| Nickel (Ni) | 6.0-8.0 |
| Molybdenum (Mo) | 3.0-5.0 |
| Nitrogen (N) | 0.24-0.32 |
| Iron (Fe) | Bal. |
| Copper (Cu) | 0.5 |
| Other Elements | - |
| Physical Properties of Super Duplex 2507 Alloys in the Annealed Condition at -20°F to +100°F | ||||||||||||||
| Tensile Strength | Yield Strength | |||||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 in. (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion (IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ ft2-h-°F) |
| Super Duplex 2507 | S32950 | A789, A790 | 100,000 | 690 | 100 | 70,000 | 485 | 70 | 20 | - | 30.5 Rc | - | - | - |
| Super Duplex 2507 | S32750 | A789, A790 | 116,000 | 800 | 116 | 80,000 | 550 | 80 | 15 | - | 32 Rc | 27.5 | 7.2 | 98 |
| Density, lb/in3 | 0.28 |
| Modulus of Elasticity, psi | 29.0x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 7.5 x 10-6 |
| Thermal Conductivity, Btu/ft hr ˚F | 8 |
| Specific Heat, Btu/lb ˚F | 0.12 |
| Electrical Resistivity, Microhm-in | 31.5 |
Our forming capabilities include cutting-edge radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills for manufacturing titanium rods. Additionally, we employ a unique hydroforming process for creating high-precision parts.
Our advanced heat treatment furnace equipment ensures the stability and high performance of our stainless steel rods.
Utilizing the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace, Daxun Stainless Steel minimizes impurities during smelting, thereby improving the performance of finished products.
Our premium stainless steel products are fully certified, meticulously traceable, and meet the highest industry standards. We proudly supply top-notch stainless steel materials to a wide array of leading industries, including aerospace, industrial, medical, marine, and military sectors.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
Can you provide SS grinding bars and rods?
Yes, we specialize in SS grinding bars and rods, known for their precise dimensions, exceptional roundness, and straightness, outperforming standard polished bars. Please note, however, that the processing costs are higher.
Q1: What products can you offer?
A: We can provide a variety of general steel types, including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L, 300 series, and more.
Additionally, we offer 400 series and duplex stainless steel such as 2205, 2304, 2101, 2507, and high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you manufacture products based on my drawings?
Yes, we can create products tailored to your drawings, ensuring they meet your highest satisfaction.
Q3. How does your factory maintain quality control?
Quality is our top priority. We consistently emphasize stringent quality control throughout the entire production process.
Q4. Can I request a change in packaging and transportation methods?
Yes, we can customize the packaging and transportation methods according to your specifications,
although you will need to cover any additional costs and differences incurred.
Q5. How does your factory maintain quality control?
Quality is our top priority. We consistently emphasize stringent quality control throughout the entire production process.
Q6. What is the delivery time?
A: The delivery time is 7 to 20 working days after payment confirmation.
For urgent orders, we can expedite the production process to meet your deadlines.
Q7. What are your payment terms?
A: 100% T/T in advance, Western Union for small orders,
B: 30% T/T deposit and the remaining 70% before shipment,
C: 100% Irrevocable LC at sight for large orders.
Q8: Can you produce DDQ (Deep Drawing Quality) materials?
A: Yes, we can. Our materials are suitable for stainless steel pots, sinks, bowls, and more. Inform us of your specific needs, and we will adjust the mechanical properties accordingly.
Q9: How can I obtain a sample?
A: FREE samples are available for inspection and testing. For small pieces, we may bear the courier cost, depending on the situation.
Q10: Which countries have you exported to?
A: To date, we have exported stainless steel materials to Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
){kind=link}