| Customization: | Available |
|---|---|
| Type: | Stainless Steel Bars |
| Standard: | ASTM, AISI, GB, JIS, DIN, EN |
|
Still deciding? Get samples of US$ 1/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Product Parameters: Stainless Steel rod | |
| Material | 201 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Chemical Composition: 201 Stainless Steel Rod
Chemical Composition (wt%) limits as specified in ASTM A240 and ASME SA240*
| Element | 201 |
| Carbon | 0.15 |
| Chromium | 16.0-18.0 |
| Nickel | 3.5-5.5 |
| Manganese | 5.50-7.50 |
| Silicon | 1.00 |
| Nitrogen | 0.25 |
| Phosphorus | 0.060 |
| Sulfur | 0.030 |
Mechanical Properties: 201 Stainless Steel Rod
Mechanical property requirements for annealed products as specified in ASTM A240 and ASME SA240
| Property | 201 |
| Yield Strength, min. (ksi) | 45 |
| Tensile Strength, min. (ksi) | 95 |
| Elongation, min. (%) | 40 |
| Hardness, max. (Rb) | 100 |
At Jiangsu Daxun Alloy Co., Ltd., we adhere to stringent mechanical property requirements for cold-worked flat-rolled products, ensuring superior quality and performance. Discover the exceptional quality of our Baosteel 201 Stainless Steel Rod, crafted to perfection.
| Condition | Yield Strength (ksi) min. |
Tensile Strength (ksi) min. |
Elongation % min. in 2 in. | |
| <0.015 in. | ≥0.015 in. | |||
| ¼ Hard | 75 | 125 | 25 | 25 |
| ½ Hard | 110 | 150 | 15 | 18 |
| ¾ Hard | 135 | 175 | 10 | 12 |
| Full Hard | 140 | 185 | 8 | 9 |
Exquisite Physical Properties
Our Type 201 Stainless Steel Rod boasts unparalleled physical properties, offering durability and strength.
| Property | 201 |
| Density, lb/in3 | 0.283 |
| Modulus of Elasticity, psi | 28.6 x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 9.2 x 10-6 |
| Thermal Conductivity, Btu/ft hr ˚F | 9.4 |
| Specific Heat, Btu/lb ˚F | 0.12 |
| Electrical Resistivity, Microohm-in | 27.0 |
Our forming prowess includes cutting-edge radial forging machines, sophisticated heat treatment and melting furnaces, and state-of-the-art rolling mills for crafting titanium rods. Additionally, our unique hydroforming process sets the benchmark for part manufacturing.
Our stainless steel rod heat treatment process utilizes advanced furnace equipment, guaranteeing material stability and high performance.
Jiangsu Daxun Alloy harnesses the world's leading vacuum induction furnace, vacuum consumable furnace, and electroslag furnace technologies to significantly reduce impurities during smelting, thereby enhancing the performance of our stainless steel rods.
Our stainless steel products are not just fully certified but also meticulously traceable. We deliver top-tier stainless steel to prominent sectors such as aerospace, industrial, medical, marine, and military.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
Can you manufacture SS grinding bars and rods?
Yes, we excel in producing SS grinding bars and rods with precise dimensions, roundness, and straightness, which are superior to traditional stainless steel polished bars. However, please note that the processing cost is higher.
Q1: What products can you offer?
A: We offer a wide range of steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L, and 300 series.
Furthermore, we provide 400 series and duplex stainless steels such as 2205, 2304, 2101, 2507, along with high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce products according to my drawings?
Yes, we can manufacture products based on your drawings to ensure they meet your utmost satisfaction.
Q3. How does your factory manage quality control?
Quality is our top priority. We implement stringent quality control measures from the beginning to the end of the production process.
Q4. Can I request changes in packaging and transportation?
Yes, we can adjust the packaging and transportation methods according to your requests.
However, please be aware that you will need to cover any additional costs and differences incurred.
Q5. How does your factory manage quality control?
Quality is our top priority. We implement stringent quality control measures from the beginning to the end of the production process.
Q6. What is your delivery time?
A: Delivery time ranges from 7 to 20 working days after payment confirmation.
For urgent orders, we prioritize and expedite production in our workshop.
Q7. What are your payment terms?
A: 100% T/T in advance, or Western Union for small orders.
B: 30% T/T deposit and the remaining 70% before shipment.
C: 100% Irrevocable LC at sight for large orders.
Q8: Can you produce DDQ (Deep Drawing Quality) materials?
A: Yes, we can. Our materials are suitable for manufacturing stainless steel pots, sinks, bowls, and more. Inform us of your specific use, and we will adjust the mechanical properties accordingly.
Q9: How can I get a sample?
A: We offer FREE samples for your evaluation and testing. If you require a small piece, we may cover courier costs depending on the situation.
Q10: Which countries have you exported to?
A: We have exported stainless steel materials to Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
){kind=link}