| Customization: | Available |
|---|---|
| Type: | Stainless Steel Bars |
| Standard: | ASTM, AISI, GB, JIS, DIN, EN |
|
Still deciding? Get samples of US$ 1/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Product Parameters: Stainless Steel rod | |
| Material | 310 310S S31008 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Daxun Alloys stands as a distinguished manufacturer of premium SS 310 / 310S Round Bars, renowned for their superior characteristics. Our Stainless Steel 310 / 310S Round Bars, crafted from chromium and nickel-based austenitic stainless steel, offer unparalleled durability, flexibility, workability, machinability, weldability, ductility, fabricability, high strength, and hardness. These versatile rods excel in industrial chemistry and nut manufacture, and their anti-corrosion properties make them a market favorite. Engineered to endure extreme temperatures, they perform impeccably even at annealing temperatures without deformation. We provide these high-quality Stainless Steel Round Bars to our esteemed clients at competitive market rates, with customization options available in various finishes, lengths, and shapes to meet specific requirements. Our round bars are ideally suited for a wide range of industrial applications.
For detailed insights on our stainless steel rods, please contact Daxun.
310S Stainless Steel Rod Chemical Composition
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Fe |
| SS 310 | 0.015 max | 2.0 max | 0.15 max | 0.020 max | 0.015 max | 24.00 - 26.00 | 0.10 max | 19.00 - 21.00 | 54.7 min |
| SS 310S | 0.08 max | 2.0 max | 1.00 max | 0.045 max | 0.030 max | 24.00 - 26.00 | 0.75 max | 19.00 - 21.00 | 53.095 min |
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Property | At | Value | unit |
| Density | 8,000 | kg/m³ | |
| Melting Range | 1400 - 1450 | °C | |
| Modulus of Elasticity | 20°C | 200 | GPa |
| Shear Modulus | 20°C | 77 | GPa |
| Poisson's Ratio | 20°C | 0.3 | |
| Thermal Conductivity | 100°C | 14.2 | W / m. °C |
| Electrical Resistivity | 25°C | 0.78 | micro-ohm . m |
| Electrical Conductivity | 25°C | 1.25 | % IACS |
| Specific Heat | 500 | J/kg. °C | |
| Relative Magnetic Permeability | 1.02 | ||
| Coefficient of Expansion | 0 - 100°C | 15.9 | /°C |
| 0 - 315°C | 16.2 | /°C | |
| 0 - 540°C | 17 | /°C |
Our forming capabilities feature state-of-the-art radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills for titanium rods, complemented by a unique hydroforming process for part manufacturing.
Our advanced heat treatment furnace equipment ensures the stability and high performance of our stainless steel rods, providing optimal material properties.
At Jiangsu Daxun Alloy Co., Ltd., our stainless steel rods are forged using the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace. This cutting-edge technology significantly reduces impurities during the smelting process, thereby enhancing the performance and durability of our Precision Polished 310S Stainless Steel Round Rods (ASTM A276 Hot Rolled). Experience superior quality and exceptional performance with Daxun's state-of-the-art smelting capabilities.
Our stainless steel products boast full certification and traceability. We deliver premium-grade stainless steel to leading sectors such as aerospace, industrial, medical, marine, and military.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
Stainless Steel Alloy 310 rods and pipes exhibit superb resistance to both corrosion and heat, making them ideal for the most challenging environments.
Daxun Alloys offers an extensive range of stainless steel round bars, suitable for a myriad of applications from construction to automotive parts. With various grades and sizes available, and our advanced cutting services, we ensure precise fulfillment of your specific requirements each and every time.
Our stainless steel round bars offer unparalleled versatility and can be conveniently ordered in an extensive range of sizes tailored to your precise needs. Choose your desired steel grade, and we will supply you with bars in lengths spanning from 500mm to 6 meters, and diameters ranging from a delicate 3mm to a robust 500mm. Additionally, you have the flexibility to order in both metric and imperial measurements, ensuring a seamless fit for any application.
Seeking a non-standard size? Look no further. We deliver unlimited free cuts to your specified length with precision. Utilizing cutting-edge bandsaws, we guarantee exceptional accuracy and repeatability, crafting each piece to meet your exact requirements. Simply inform us of your unique needs when placing your order, and we will handle the rest, ensuring a perfect fit every time.
Can you manufacture SS grinding bars and rods?
Absolutely, we specialize in producing SS grinding bars and rods that excel in precision, roundness, and straightness. They outperform typical stainless steel polished bars, albeit with higher processing costs.
Q1: What products do you offer?
A: We provide a versatile range of steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, and 316. Additionally, we offer 316L 300 series, 400 series, and duplex stainless steels such as 2205, 2304, 2101, and 2507, alongside high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce products based on my drawings?
Yes, we can manufacture products precisely according to your drawings, ensuring they meet your highest satisfaction.
Q3. What are your quality control measures?
Quality is our top priority. We rigorously control quality at every stage, from inception to final delivery.
Q4. Can I request changes in packaging and transportation?
Yes, we can accommodate changes in packaging and transportation as per your request.
However, please note that you will be responsible for any additional costs incurred during this process.
Q5. What are your quality control practices?
Quality is paramount for us. We maintain stringent quality control from start to finish.
Q6. What is your delivery time frame?
A: Typically, delivery takes 7 to 20 working days after payment confirmation.
If your order is urgent, we will expedite the process to meet your timeframe.
Q7. What payment terms do you offer?
A: 100% T/T in advance, or Western Union for small orders.
B: 30% T/T upfront and 70% balance before shipment.
C: 100% Irrevocable LC at sight for large orders.
Q8: Can you produce DDQ (Deep Drawing Quality) materials?
A: Indeed, we can. Our materials are suitable for manufacturing stainless steel pots, sinks, bowls, etc. Inform us of your specific use, and we will adjust the mechanical properties accordingly.
Q9: How can I obtain a sample?
A: We offer FREE samples for your evaluation. For small pieces, we might cover the courier cost, depending on the circumstance.
Q10: Which countries have you exported to?
A: To date, we have exported stainless steel materials to countries such as Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
){kind=link}