| Customization: | Available |
|---|---|
| Type: | Stainless Steel Bars |
| Standard: | ASTM, AISI, GB, JIS, DIN, EN |
|
Still deciding? Get samples of US$ 1/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Product Parameters: Stainless Steel rod | |
| Material | 304 304L |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
For more details on stainless steel rods, please reach out to Daxun.
304 Stainless Steel Rod Chemical Composition
Chemical Composition (wt%) Limits as Specified in ASTM A240 and ASME SA240*
| Element | 304 | 304L |
| Carbon | 0.07 | 0.03 max |
| Chromium | 18.0-19.5 | 18.0-19.5 |
| Nickel | 8.0-10.5 | 8.0-12.0 |
| Manganese | 2.00 | 2.00 |
| Silicon | 0.75 | 0.75 |
| Nitrogen | 0.10 | 0.10 |
| Phosphorus | 0.045 | 0.045 |
| Sulfur | 0.030 | 0.030 |
304 Stainless Steel Rod Mechanical Properties
Mechanical Property Requirements for Annealed Products as Specified in ASTM A240 and ASME SA240
| Property | 304 | 304L |
| Yield Strength, min. (ksi) | 30 | 25 |
| Tensile Strength, min. (ksi) | 75 | 70 |
| Elongation, min. (%) | 40 | 40 |
| Hardness, max. (Rb) | 92 | 92 |
304 Stainless Steel Rod Physical Properties
Physical Properties for Type 304/304L Stainless Steel
| Property | 304/304LData |
| Density, lb/in3 | 0.285 |
| Modulus of Elasticity, psi | 28 x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 9.2 x 10-6 |
| Thermal Conductivity, Btu/ft hr ˚F | 9.4 |
| Specific Heat, Btu/lb ˚F | 0.12 |
| Electrical Resistivity, Microohm-in | 28.3 |
Our forming capabilities include cutting-edge radial forging machines, advanced heat treatment and melting furnaces, rolling mills, and a unique hydroforming process for manufacturing titanium rods and parts.
Our advanced heat treatment furnace equipment ensures the stability and high performance of our stainless steel rods.
Daxun Stainless Steel boasts an exceptional edge with its state-of-the-art smelting technologies. Utilizing the world's most advanced vacuum induction furnace, alongside a cutting-edge vacuum consumable furnace and superior electroslag furnace, we effectively minimize impurities during the smelting process. This ensures that our finished stainless steel rods exhibit unparalleled performance and reliability.
Our stainless steel products are fully certified and traceable, ensuring top-notch quality and reliability. We proudly supply the highest-grade stainless steel to leading industries including aerospace, industrial, medical, marine, and military sectors.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
The DAUXN 304/304L Stainless Steel RODS are integral in a myriad of household and commercial applications, including:
Can you provide stainless steel grinding bars and rods?
Yes, we offer stainless steel grinding bars and rods characterized by precise dimension, exceptional roundness, and perfect straightness. Our grinding bars surpass the quality of stainless steel polished bars, although the processing costs are higher.
Q1: What products are available from your company?
A: We offer a variety of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L, and 300 series.
Additionally, we provide 400 series stainless steels and duplex stainless steels such as 2205, 2304, 2101, 2507, along with high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you manufacture products based on my drawings?
Yes, we can produce products according to your custom drawings, ensuring your utmost satisfaction.
Q3. How does your factory ensure quality control?
Quality is our top priority. We consistently prioritize quality control throughout the entire production process, from start to finish.
Q4. Can I request changes in packaging and transportation methods?
Yes, we can modify the packaging and transportation methods according to your requests.
However, you will need to cover any additional costs and the price differences incurred during this process.
Q5. How does your factory manage quality control?
Quality is our top priority. We consistently prioritize quality control throughout the entire production process, from start to finish.
Q6. What is your typical delivery time?
A: The delivery time ranges from 7 to 20 working days after payment confirmation.
For urgent orders, we expedite the process to meet your timeline.
Q7. What are your payment terms?
A: 100% T/T in advance, or Western Union for small orders.
B: 30% T/T upfront and 70% balance before shipment.
C: 100% Irrevocable LC at sight for large orders.
Q8: Do you provide Deep Drawing Quality (DDQ) material?
A: Yes, we do. Our materials are suitable for manufacturing stainless steel pots, sinks, bowls, etc. Share your specific requirements, and we will adjust the mechanical properties to meet your needs.
Q9: How can I obtain a sample?
A: We provide FREE samples for checking and testing. For small pieces, we may cover the courier cost, depending on the situation.
Q10: Which countries have you exported your products to?
A: To date, we have exported stainless steel materials to various countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
){kind=link}