| Customization: | Available |
|---|---|
| Type: | Stainless Steel Bars |
| Standard: | ASTM, AISI, GB, JIS, DIN, EN |
|
Still deciding? Get samples of US$ 1/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Product Parameters: Stainless Steel rod | |
| Material | 310 310S S31008 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Daxun Alloys is a renowned manufacturer of premium quality SS 310 / 310S Round Bars, offering a versatile range of characteristics. These austenitic stainless steel rods, based on chromium and nickel, exhibit unparalleled attributes such as durability, flexibility, workability, machinability, weldability, ductility, fabricability, high strength, and hardness. They are particularly valuable in industrial chemistry and nut manufacturing applications, and are exceedingly popular in the market due to their superior anti-corrosion properties. Engineered to withstand extreme temperatures, these rods can be effortlessly deployed at annealing temperatures without deformation. At Daxun, we offer Stainless Steel Round Bars to our esteemed clients at highly competitive prices, with the capability to customize bars in various finishes, lengths, and shapes to meet precise specifications. Our circular bars are ideally suited for diverse industrial applications, ensuring reliability and performance.
For more detailed information on our stainless steel rods, please contact Daxun
310S Stainless Steel Rod Chemical Composition
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Fe |
| SS 310 | 0.015 max | 2.0 max | 0.15 max | 0.020 max | 0.015 max | 24.00 - 26.00 | 0.10 max | 19.00 - 21.00 | 54.7 min |
| SS 310S | 0.08 max | 2.0 max | 1.00 max | 0.045 max | 0.030 max | 24.00 - 26.00 | 0.75 max | 19.00 - 21.00 | 53.095 min |
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Property | At | Value | unit |
| Density | 8,000 | kg/m³ | |
| Melting Range | 1400 - 1450 | °C | |
| Modulus of Elasticity | 20°C | 200 | GPa |
| Shear Modulus | 20°C | 77 | GPa |
| Poisson's Ratio | 20°C | 0.3 | |
| Thermal Conductivity | 100°C | 14.2 | W / m. °C |
| Electrical Resistivity | 25°C | 0.78 | micro-ohm . m |
| Electrical Conductivity | 25°C | 1.25 | % IACS |
| Specific Heat | 500 | J/kg. °C | |
| Relative Magnetic Permeability | 1.02 | ||
| Coefficient of Expansion | 0 - 100°C | 15.9 | /°C |
| 0 - 315°C | 16.2 | /°C | |
| 0 - 540°C | 17 | /°C |
Our forming capabilities include advanced radial forging machines, high-performance heat treatment furnaces, cutting-edge melting furnaces, and precision rolling mills for manufacturing titanium rods. Additionally, we employ a unique hydroforming process for the production of diverse parts.
Our stainless steel rod heat treatment process utilizes advanced furnace equipment to ensure the material's exceptional stability and high performance.
Daxun Stainless Steel leverages the world's most cutting-edge vacuum induction furnace, vacuum consumable furnace, and electroslag furnace. This state-of-the-art technology significantly minimizes impurities during the smelting process, thereby dramatically enhancing the quality and performance of our Precision Polished 310S Stainless Steel Round Rods. Experience superior strength and durability tailored for high-temperature furnaces, crafted to meet the stringent ASTM A276 standards.
Our stainless steel products come with full certification and traceability, meeting the highest standards of quality. We proudly supply premium stainless steel to leading sectors such as aerospace, industrial, medical, marine, and military.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
Stainless Steel Alloy 310 rods and pipes deliver outstanding resistance to both corrosion and heat, making them reliable even in the toughest environments.
Daxun Alloys' stainless steel round bars are essential across various industries, from construction to automotive parts. To cater to this diversity, we offer bars in multiple grades and sizes, precisely cut to your requirements with our free advanced cutting service.
Stainless steel round bars can be effortlessly ordered in an extensive range of sizes tailored to your specific needs. Select the exact grade of steel you require, and we will provide bars in lengths from 500mm to 6 meters, with diameters spanning from 3mm to 500mm. Additionally, we offer the flexibility of ordering in either metric or imperial sizes, ensuring a perfect fit for your project.
If your specifications call for a non-standard size, rest assured, we have you covered. We provide unlimited complimentary cuts to length. Utilizing cutting-edge bandsaws, we guarantee precision and consistency, precisely meeting your requirements every single time. Simply communicate your needs at the time of ordering, and we will handle the rest seamlessly.
Can you manufacture stainless steel grinding bars and rods?
Yes, we specialize in producing stainless steel grinding bars and rods, which boast precise dimensions, roundness, and straightness. These are superior to standard stainless steel polished bars, though they come with higher processing costs.
Q1: What types of products can you offer?
A: We offer a variety of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, and 316L.
In addition, we provide 400 series and duplex stainless steels such as 2205, 2304, 2101, and 2507. We also supply high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce products according to my custom drawings?
Absolutely, we can manufacture products based on your drawings to meet your highest satisfaction.
Q3. How does your factory ensure quality control?
Quality is our top priority. We meticulously control quality throughout every stage of production, from start to finish.
Q4. Can I request changes to the packaging and transportation methods?
Yes, we can modify packaging and transportation methods according to your request.
However, you will need to cover any additional costs and differences that arise during this period.
Q5. How does your factory ensure consistent quality control?
Quality is our top priority. We meticulously control quality throughout every stage of production, from start to finish.
Q6. What is your standard delivery time?
A: Standard delivery time is 7 to 20 working days after payment confirmation.
For urgent orders, we will expedite production to meet your deadlines.
Q7. What payment methods do you accept?
A: 100% T/T in advance, or Western Union for small orders.
B: 30% T/T upfront with the remaining 70% due before shipment.
C: 100% Irrevocable LC at sight for large orders.
Q8: Can you provide Deep Drawing Quality (DDQ) materials?
A: Yes, we can. Our materials are suitable for making stainless steel pots, sinks, bowls, etc. Let us know your specific needs, and we'll adjust the mechanical properties to meet your requirements.
Q9: How can I obtain a sample?
A: Free samples are available for your evaluation. If you need a small piece, we may cover the courier cost depending on the situation.
Q10: Which countries have you exported to?
A: We have exported our stainless steel materials to various countries, including Vietnam, Thailand, Turkey, Russia, Morocco, South Korea, India, Pakistan, UAE, Ukraine, and more.
){kind=link}