| Type: | Stainless Steel Bars |
|---|---|
| Standard: | ASTM, AISI, GB, JIS, DIN, EN |
| Grade: | 310 310S S31008 |
| Certification: | ISO, RoHS, IBR, AISI, ASTM, GB, EN, DIN, JIS |
| Shape: | Round |
| Technique: | Hot Rolled |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier
| Product Parameters: Stainless Steel rod | |
| Material | 310 310S S31008 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Daxun Alloys stands as a reputable manufacturer of premium-quality SS 310/310S Round Bars, offering a range of exceptional characteristics. These austenitic stainless steel bars, based on chromium and nickel, are celebrated for their remarkable properties, including durability, flexibility, workability, machinability, weldability, ductility, fabricability, high strength, and hardness. SS310/310S Round Bars are particularly suited for industrial chemistry applications and nut manufacturing, renowned for their unparalleled anti-corrosion properties and ability to endure extreme temperatures without deformation. Our Stainless Steel Round Bars are offered at competitive market prices and can be customized in various finishes, lengths, and shapes to meet specific client needs. These versatile round bars are ideal for a wide array of industrial applications.
For more information on stainless steel rods, please contact Daxun.
310S Stainless Steel Rod Chemical Composition
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Fe |
| SS 310 | 0.015 max | 2.0 max | 0.15 max | 0.020 max | 0.015 max | 24.00 - 26.00 | 0.10 max | 19.00 - 21.00 | 54.7 min |
| SS 310S | 0.08 max | 2.0 max | 1.00 max | 0.045 max | 0.030 max | 24.00 - 26.00 | 0.75 max | 19.00 - 21.00 | 53.095 min |
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Property | At | Value | unit |
| Density | 8,000 | kg/m³ | |
| Melting Range | 1400 - 1450 | °C | |
| Modulus of Elasticity | 20°C | 200 | GPa |
| Shear Modulus | 20°C | 77 | GPa |
| Poisson's Ratio | 20°C | 0.3 | |
| Thermal Conductivity | 100°C | 14.2 | W / m. °C |
| Electrical Resistivity | 25°C | 0.78 | micro-ohm . m |
| Electrical Conductivity | 25°C | 1.25 | % IACS |
| Specific Heat | 500 | J/kg. °C | |
| Relative Magnetic Permeability | 1.02 | ||
| Coefficient of Expansion | 0 - 100°C | 15.9 | /°C |
| 0 - 315°C | 16.2 | /°C | |
| 0 - 540°C | 17 | /°C |
Our forming capabilities feature state-of-the-art radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills for titanium rod manufacturing. We also offer a unique hydroforming process for part fabrication.
Our advanced heat treatment furnace equipment guarantees the stability and high performance of stainless steel rods, ensuring they meet the stringent requirements of various applications.
Daxun Stainless Steel leverages the world's most cutting-edge technology in vacuum induction furnaces, vacuum consumable furnaces, and electroslag furnaces. This advanced equipment significantly minimizes impurities during the smelting process, thereby elevating the performance and quality of our finished 310S stainless steel rods. Trust in Daxun for superior materials engineered to withstand high temperatures and demanding environments.
Our stainless steel products come with full certification and traceability. We proudly supply the highest quality stainless steel to top-tier industries, including aerospace, industrial, medical, marine, and military sectors.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
Stainless Steel Alloy 310 rods and pipes are engineered to deliver exceptional resistance to both corrosion and heat, thriving even in the harshest environments.
Stainless steel round bars are indispensable across various sectors, from construction to automotive parts. Recognizing the diverse demands, Daxun Alloys provides stainless steel round bars in multiple grades and sizes. Our advanced cutting service ensures precise customization to meet your exact specifications.
Experience unparalleled convenience with our stainless steel round bars, available in a comprehensive range of sizes to suit your specific needs. Choose from an array of steel grades and secure bars in lengths that span from 500mm to a substantial 6 meters, with diameters meticulously crafted between 3mm and 500mm. Whether you prefer metric or imperial measurements, we accommodate your every preference.
Looking for custom dimensions? We've got you covered. Benefit from our complimentary unlimited cuts to length, executed with precision using cutting-edge bandsaws. This ensures both accuracy and consistency, tailored perfectly to your specifications. Just provide your requirements when placing an order and leave the rest to us.
Do you offer stainless steel grinding bars and rods?
Absolutely! We provide stainless steel grinding bars and rods that boast precise dimensions, impeccable roundness, and superior straightness. These qualities surpass those of standard polished stainless steel bars. Please note, however, the processing costs are higher.
Q1: What products do you offer?
A: Our offerings include a wide range of general steel types such as 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L, and the 300 series.
Additionally, we provide 400 series stainless steel and duplex stainless steel grades like 2205, 2304, 2101, and 2507. We also carry high-nickel alloys including 904L, 800H, and 600H.
Q2: Can you manufacture products according to my custom drawings?
Yes, we can. We tailor our production process to meet your specific drawings, ensuring complete satisfaction.
Q3: How does your factory ensure quality control?
Quality is our top priority. From inception to final delivery, we maintain stringent quality control measures at every production stage.
Q4: Can I request changes in packaging and transportation?
Certainly! We can modify the packaging and transportation methods to suit your needs.
However, please note that you will need to cover any additional costs and differences incurred during this period.
Q5: How does your factory ensure quality control?
Quality is our top priority. From inception to final delivery, we maintain stringent quality control measures at every production stage.
Q6: What is your delivery time frame?
A: Our standard delivery time is 7 to 20 working days after payment confirmation.
For urgent orders, we expedite the process to ensure early completion.
Q7: What are your payment options?
A: We offer 100% T/T advance payment or Western Union for small orders.
B: For larger orders, we accept a 30% T/T advance with the remaining 70% due before shipment.
C: We also accept 100% Irrevocable LC at sight for substantial orders.
Q8: Can you provide Deep Drawing Quality (DDQ) materials?
A: Yes, we can. Our DDQ materials are ideal for manufacturing stainless steel pots, sinks, bowls, and more. Share your intended use, and we'll adjust the mechanical properties to meet your specific requirements.
Q9: How can I obtain a sample?
A: We offer FREE samples for your assessment and testing. For small pieces, we may cover the courier cost, contingent on the specifics.
Q10: Which countries have you exported to thus far?
A: To date, our stainless steel materials have been exported to countries including Vietnam, Thailand, Turkey, Russia, Morocco, South Korea, India, Pakistan, UAE, Ukraine, and many more.