| Product Parameters: Stainless Steel rod | |
| Material | 17-4PH 630 Precipitation Hardened Steel Bars |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Daxun is a world-renowned manufacturer of SS 17-4PH/630 Round Bar/Rod range. We proudly serve as a trusted supplier, exporter, and reputable distributor of top-tier bars and rods.
We provide our customers with premium bars and rods in a variety of parameters including surface treatment, end finish, dimensions, shapes, and sizes.
SS 17-4PH is a high-performance martensitic stainless steel that can be hardened through precipitation. This alloy is enriched with elements like nickel, copper, and chromium, making it indispensable in the aerospace sector for fasteners and structural components. With a unique microstructure obtained during the remelting process, UNS S17400 boasts enhanced toughness.
Stainless Steel 17-4PH Round Bar is a versatile and highly sought-after material in manufacturing and engineering industries, celebrated for its outstanding corrosion resistance, superior strength, and ease of fabrication. The 'PH' in 17-4PH signifies precipitation hardening, a heat treatment method that amplifies the material's mechanical properties.
For more information on stainless steel rods, please contact Daxun.
17-4PH Stainless Steel Rod Chemical Composition
| Carbon | 0.07% (Max) |
| Silicon | 1.00% (Max) |
| Manganese | 1.00% (Max) |
| Phosphorous | 0.040% (Max) |
| Sulfur | 0.030% (Max) |
| Chromium | 15%-17.5% |
| Molybdenum | 0.50% (Max) |
| Nickel | 3%-5% |
| Copper | 3%-5% |
| Material Type | Condition | Ultimate Tensile Strength (PSI) | 0.2% Yield Strength (PSI) | Elongation (% In 2in.) | Reduction Of Area (%) | Hardness Brinell | Hardness Rockwell |
| 17-4 PH | H900 | 190,000 | 170,000 | 10 | 40 | 388 | C40 |
| H1025 | 155,000 | 145,000 | 12 | 45 | 331 | C35 | |
| H1075 | 145,000 | 125,000 | 13 | 45 | 311 | C32 | |
| H1150 | 135,000 | 105,000 | 16 | 50 | 277 | C28 | |
| H1150-M | 115,000 | 75,000 | 18 | 55 | 255 | C24 | |
| H1150-D | 125,000 | 105,000 | 16 | 50 | 255 min - 311 max | C24 - 33 |
| Heat Treated Condition | H900 |
| Density, lbs/in3 | 0.282 |
| Electrical Resistivity, microhm-cm | 77 |
| Specific Heat, BTU/lb/°F (32-212°F) | 0.1 |
| Thermal Conductivity, BTU/hr/ft2/in/°F | |
| 300°F | 124 |
| 500°F | 135 |
| 860°F | 156 |
| 900°F | 157 |
| Mean Coefficient of Thermal Expansion, in/in/°F | |
| -100 to 70°F | 5.8 x 10^-6 |
| 70 - 200°F | 6.0 x 10^-6 |
| 70 - 400°F | 6.0 x 10^-6 |
| 70 - 600°F | 6.3 x 10^-6 |
| 70 - 800°F | 6.5 x 10^-6 |
| 70 - 900°F | - |
| Modulus of Elasticity, ksi | 28.5 x 10^3 |
| Modulus of Rigidity, ksi | 11.2 x 10^3 |
| Poisson's Ratio (all conditions) | 0.272 |
Our state-of-the-art forming capabilities include advanced radial forging machines, heat treatment furnaces, melting furnaces, and rolling mills for titanium rod production. We also offer a unique hydroforming process for manufacturing high-quality parts.
Our high-performance stainless steel rod undergoes precise heat treatment utilizing state-of-the-art furnace equipment, ensuring unmatched stability and superior material performance.
At Jiangsu Daxun Alloy Co., Ltd., we leverage the world's leading vacuum induction furnace, vacuum consumable furnace, and electroslag furnace technologies. These advanced systems significantly reduce impurities during the smelting process, resulting in superior performance for our premium stainless steel rods.
At Jiangsu Daxun Alloy Co., Ltd., our stainless steel products are meticulously certified and traceable. We provide the pinnacle of stainless steel quality to premier industries, including aerospace, industrial sectors, medical fields, marine applications, and military use.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
17-4PH stainless steel round bars find extensive application across various industries, from construction to automotive parts. Given the diverse range of applications, Jiangsu Daxun Alloy Co., Ltd. offers these bars in numerous grades and sizes. With our complimentary advanced cutting service, we ensure precise fulfillment of your requirements every time.
Can you offer stainless steel grinding bars and rods?
Yes, we specialize in stainless steel grinding bars and rods featuring precise dimensions, exceptional roundness, and impeccable straightness. These attributes surpass those of standard polished bars, though they do incur a higher processing cost.
Q1: What products can you offer?
A: We offer a wide range of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L 300,
400 series, and duplex stainless steels such as 2205, 2304, 2101, 2507, etc. We also provide high-nickel alloys like 904L, 800H, and 600H.
Q2: Can you produce products according to my own drawings?
Yes, we can manufacture products tailored to your drawings to ensure they meet your highest expectations.
Q3: How does your factory handle quality control?
Quality is our top priority. We implement rigorous quality control measures from the beginning to the end of the production process.
Q4: Can I request changes to the form of packaging and transportation?
Yes, we can adjust the packaging and transportation methods according to your preferences,
though any additional costs and variances incurred during this period will be your responsibility.
Q5: How does your factory handle quality control?
Quality is our top priority. We implement rigorous quality control measures from the beginning to the end of the production process.
Q6: What is the delivery time?
A: Our standard delivery time is 7-20 working days after payment confirmation.
For urgent orders, we can expedite the production process.
Q7: What are your payment terms?
A: 100% T/T in advance, or Western Union (for small orders).
B: 30% T/T in advance with the balance 70% before shipment.
C: 100% Irrevocable LC at sight (for large orders).
Q8: Can you produce Deep Drawing Quality (DDQ) stainless steel?
A: Yes, we can. Our materials are suitable for stainless steel pots, sinks, bowls, etc. Let us know your specific application, and we will adjust the mechanical properties to meet your requirements.
Q9: How can I obtain a sample?
A: We provide FREE samples for your evaluation. For small pieces, we may cover the courier cost, depending on the request.
Q10: Which countries have you exported to?
A: To date, we have exported stainless steel materials to Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, among others.
){kind=link}