Type: | Titanium Pipes |
---|---|
Application: | Industrial, Medical |
Technique: | Hot Rolled |
Grade: | Gr1 Grade1 |
Shape: | Round |
Standards: | Astmb861 B862 B338 ASME Sb861 Sb862 Sb338 |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Grade 1 Titanium pipe & Tubes Specification | ASTM B338 / ASTM B861 / ASTM B862 / ASME SB338 / ASME SB861 / ASME SB862 |
Grade 1 Titanium pipe & Tubes Grades | Commercially pure titanium Grade 1- TA1- USN 50250 |
Grade 1 Titanium pipe & Tubes Type | ot Rolled / Cold Drawn / Welded / ERW |
Grade 1 Titanium pipe & Tubes Outer Diameter Size | Titanium seamless pipe - φ1.0mm to φ508.3mm |
Titanium welded pipe - φ6.0mm to φ1219mm | |
Grade 1 Titanium pipe & Tubes Wall Thickness | 0.3mm-50mm (customizable wall thickness) |
Grade 1 Titanium pipe & Tubes Length | 5 to 7 Meters, 09 to 13 Meters, Single Random Length, Double Random Length And Customize Size. |
Titanium pipe Form | ' Hollow, U' bent, LSAW, Hydraulic, Straight Tube, Boiler, Round, Tube Coil, Square, Rectangular Etc |
Marking | All Titanium Tubes Tubing are marked as follows: Grade, Standard, Thickness, OD, Heat No., Length (Or according to the customer's request.) |
Uses of Titanium Alloy Tubes | Gas pipes, oil pipes, heat exchanger tubes, boiler tubes, fluid pipes, titanium exhaust pipes. |
Grade 1 Titanium pipe & Tubes Pipe Ends | Plain Ends / Beveled Ends |
Grade 1 Titanium pipe & Tubes Delivery Conditions | As Rolled, Cold Drawn, Hot Finish, Stress Relieved, Annealed, Hardened, Tempered |
Grade 1 Titanium pipe & Tubes Coating | Electropolish, Mechanical Polish, Satin Finish, Passivated |
Grade 1 Titanium pipe & Tubes Other Testing | ardness Test, Hydrostatic Test, Eddy Current test, Eddy Current, Tensile Test, Flattening, Flare Test, Annealed, Hydrostatic Test, Tempered, Stress Relieved etc. |
Grade 1 Titanium pipe & Tubes Dimension | All Pipes Is Manufactured and Inspected / Tested to the Relevant standards including ASTM And ASME |
Grade 1 Titanium pipe & Tubes Value Added Services | Draw / Expansion / Machining / Sand Blasting / Shot Blasting / Heat Treatment |
Grade 1 Titanium pipe & Tubes Packaging | Loose / Bundle / Wooden Pallet / Wooden box-a / Plastic Cloth Wraps / Plastic End Caps / Beveled Protector |
Grade 1 Titanium pipe & Tubes Shipment & Transportation | By Road - Truck / Train, By Sea - Break-bulk Conventional Vessel / FCL (Full Container Load) / LCL (Less Container Load) / 20 Feet Container / 40 Feet Container / 45 Feet Container / High Cube Container / Open Top Container, By Air - Freighter Civil Passenger and Cargo Planes |
Grade 1 Titanium pipe & Tubes Material Test Certificate | Manufacturer Test Certificate As Per EN10204 3.1, 3.2 / Laboratory Test Certificate From NABL Approved Lab. / Under Third Party Inspection Agency Like SGS, TUV, DNV, LLOYDS, ABS ETC |
Daxun performs several quality assurance tests, these tests include flattening test, flaring test, ultrasonic flaw detection test, pitting and resistance test, mechanical test, hardness test, material positive identification, expansion test, etc. All these tests ensure that the Grade 1 Titanium Welded Pipe and Grade 1 Titanium Seamless Pipe materials are suitable for the required application. During the production process, we measure the diameter, thickness and surface of the products. Our standard delivery time is 5-7 days and the delivery time for special size products is 15-20 days.
Grade 1 Titanium Tube is the softest form of titanium and has the highest ductility. It has good cold forming characteristics and offers excellent corrosion resistance. It also has excellent welding properties and high impact toughness.
Commercially Pure Titanium Grade 1 Tube is one of the softest and most ductile types with excellent formability. Grade 1 Titanium Tube is primarily used in the maritime and chemical industries where parts are exposed to extremely harsh conditions. The ultimate tensile strength of SB 338 Gr 1 Tube is 35 KSI min (240 MPa min), while the yield strength (0.2% variation) of Cp Grade 1 Tube is 25 - 45 KSI (170 - 310 MPa). Ti Cp Grade 1 Seamless Tube is also known as TA1, Titan Grade 1, and Gr 1. Grade 1 Titanium Tube is a non-alloyed, low-strength titanium tube product with low oxygen concentration and excellent formability; it is used in the chemical industry, heat exchangers, and desalination facilities.
Grade 1 Titanium Tube is also well suited for manufacturing exhaust systems, charge air pipes, and water pipes. We offer Titanium Tube with a thickness equivalent to 1.2 mm and diameters ranging from 51 mm to 102 mm (the most common exhaust system sizes). Therefore, these tubes are more stable and stronger even at higher exhaust gas temperatures.
Daxun certifies and tests titanium alloy tubes according to ASME SB/ASTM, B861 and B862, including hardness testing, hydrostatic testing, eddy current testing, ultrasonic defect identification, tensile testing, flattening, expansion testing, annealing, tempering, stress relief, etc.
Titanium Grade 1 Tube, Titanium UNS R50250 Tube, Titanium Alloy DIN 3.7025 Seamless Tube, Titanium Alloy Grade 1 Tube, Titanium Grade 1 Seamless Tube, Titanium UNS R50250 Seamless Tube, Titanium Alloy Grade 1 Tube, Titanium Tube Suppliers, Welded Titanium Tubes, Titanium Tubes for Sale, Titanium Seamless Tubes, Titanium Tube Suppliers, Titanium Werkstoff Nr. 3.7025 Tube, Titanium UNS R50250 Seamless Tube, Titanium Alloy R50250 Tube, Titanium R50250 Welded Tube, Titanium Gr1 Tube, Titanium Alloy DIN 3.7025 Welded Tube, Titanium Gr.1 Tube Suppliers in China.
Titanium Seamless Tubes
Daxun produces:
Hot-finished Titanium Tubes
These tubes are supplied in the form of hot-rolled or hot-extruded, straightened, machined inside and outside diameters, and surface polished. Titanium tubes are available in heat-treated or non-heat-treated forms. Our company has 100% ultrasonic flaw detection capabilities.
Titanium Tube Materials Available:
Hot-rolled Titanium Tubes: OD 19mm to 325mm, wall thickness 9mm to 30mm, length up to 5000mm (to be agreed on a case-by-case basis between the manufacturer and the customer); - Hot-extruded Titanium Tubes: OD 50mm to 160mm, wall thickness 7mm to 35mm, length up to 3000 (to be agreed on a case-by-case basis between the manufacturer and the customer).
Cold-finished Titanium Tubes
Cold-finished Titanium Tubes are supplied in the form of heat-treated, surface-etched, hydrostatically tested, or ultrasonically tested, depending on the requirements of the manufacturing specifications. Tubes Supplied:- OD 6mm to 89mm, wall thickness 0.5mm to 11mm, length up to 6000mm (to be agreed on a case-by-case basis between the manufacturer and the customer).
Titanium Welded Pipes
DaXun manufactures and supplies titanium pipes with diameters from 100 mm. 12.7 to 38.1 mm (0.47 in to 1.5 in), wall thickness from 0.4 to 1.65 mm (0.016 in to 0.065 in, depending on diameter), lengths up to 25000 mm, electrical Gr1, Gr2 and Gr12 titanium alloy pipes for engineering and chemical industries. Titanium welded pipes are made from flat rolled raw material (kelp) by automatic tungsten inert gas (argon) welding on electric pipe welders and heat treated on the mill line. Finished titanium welded pipes undergo mechanical testing, geometrical measurements, 100% ultrasonic and eddy current testing, pneumatic or hydrostatic testing; pipes are packed as per customer specifications. Manufacturing processes and inspection test equipment ensure thin wall welded pipes comply with ASTM B 338, ASME SB 338 standards.
CP GR1 Titanium tube PHYSICAL PROPERTIES | |||
Physical Properties | Metric | English | Comments |
Density | 4.50 g/cc | 0.163 lb/in³ | |
a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
Mechanical Properties | Metric | English | Comments |
Hardness, Brinell | 120 | 120 | annealed |
Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
Hardness, Rockwell B | 70 | 70 | annealed |
Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
Elongation at Break | 24% | 24% | |
25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
Reduction of Area | 35% | 35% | |
Tensile Modulus | 103 GPa | 14900 ksi | |
Compressive Modulus | 110 GPa | 16000 ksi | |
Poissons Ratio | 0.37 | 0.37 | |
Shear Modulus | 45.0 GPa | 6530 ksi | |
Charpy Impact | 310 J | 229 ft-lb | V-notch |
Impact Test | 136 J | 100 ft-lb | Impact Strength |
Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
0.8 | 0.8 | Ti sliding on Ti; 40 m/min |
CP GR2 Titanium tube PHYSICAL PROPERTIES | |
Density | Magnetic Permeability |
0.163 lbs/in-3 | Nonmagnetic |
4.51 g/cm-3 | Electrical Resistivity |
Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
1680°F | 0.53 µΩ/m |
915°C | Elastic Modulus |
Thermal Conductivity | 15.2-17.4 Msi |
12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
GR5 TI6AL4V Titanium tube PHYSICAL PROPERTIES | |||
Physical Properties | Metric | English | Comments |
Density | 4.43 g/cc | 0.16 lb/in³ | |
Mechanical Properties | |||
Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
Hardness, Rockwell C | 36 | 36 | |
Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
Tensile strength | min. 895MPa | 129810 psi | |
Yield strength | min. 828MPa | 120090 psi | |
Elongation at Break | min.10 % | 10 % | |
Reduction of Area | min.25 % | 25 % | |
Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
Compressive Yield Strength | 970 MPa | 141000 psi | |
Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
Poisson's Ratio | 0.342 | 0.342 | |
Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
Shear Modulus | 44 GPa | 6380 ksi | |
Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
Electrical Properties | |||
Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
Thermal Properties | |||
CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
Solidus | 1604 °C | 2920 °F | |
Liquidus | 1660 °C | 3020 °F | |
Beta Transus | 980 °C | 1800 °F |
This is the most often used titanium tube for industrial applications, providing a superb balance of moderate strength and reasonable ductility. It offers excellent corrosion resistance in both highly oxidising and slightly reducing conditions (including chlorides). It provides good corrosion protection in the chemical and offshore industries, as well as aircraft manufacture, where strength and ease of forming are required. It's also utilised in heat exchangers, hypochlorite systems, fire water systems, ballast water systems, industrial and aerospace components, CPI equipment, and pipes.
Q1: What products can you offer?
A: We can offer you general steel types like 310S, 316L,304.304L.201,904L, 316H, 316,316L 300and
400 series, and duplex stainless steel like 2205, 2304,2101,2507,etc. 904L, 800H, 600H high-nickel alloy.
Q2. Can you produce the products according to my own drawings?
Yes, we can produce the products according to your drawings that will be most satisfy you.
Q3. How does your factory do regarding quality control?
Quality is a priority. We always attach great importance to quality controlling from the beginning to end.
Q4. Can I request to change the form of packaging and transportation?
Yes, We can change the form of the packaging and transportation according to your request,
but you have to bear their own costs incurred during this period and the spreads.
Q5. How does your factory do regarding quality control?
Quality is a priority. We always attach great importance to quality controlling from the beginning to end.
Q6. How long is the delivery time?
A: 7~20 working days after confirming the payment.
If the order is urgent, we will push our workshop finish in advance.
Q7. What is your Payment?
A: 100% T/T advance, Western Union (For Small Order)
B: 30% T/T and balance 70% before the shipment
C: 100% Irrevocable LC at sight (For Big Order)
Q8: Can you make DDQ ( Deep Drawing Quality)?
A: Yes, we can. Our material can be used for stainless steel pots, stainless steel sinks, stainless steel bowls etc. U can tell us your usage, and we will adjust the mechanical propertise to meet your requirement.
Q9: How to get a sample?
A: FREE samples are available for your checking and testing.If you require for a small piece,we can afford courier cost,it depends.
Q10:Which country have you exported to?
A:Until now,we have exported stainless steel material to following countries: Vietnam,Thailand,Turkey,Russia,Maroc,Korea,India,Pakistan,UAE,Ukraine and so on.
Q11: How to visit your company?
A:By flight to Guangzhou Baiyun International airport,then we will pick you up.
Suppliers with verified business licenses