| Customization: | Available |
|---|---|
| Type: | Stainless Steel Bars |
| Standard: | ASTM, AISI, GB, JIS, DIN, EN |
|
Still deciding? Get samples of US$ 1/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Product Parameters: Stainless Steel rod | |
| Material | 201 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Chemical Composition of 201 Stainless Steel Rod
Chemical Composition (wt%) Limits as Specified in ASTM A240 and ASME SA240*
| Element | 201 |
| Carbon | 0.15 |
| Chromium | 16.0-18.0 |
| Nickel | 3.5-5.5 |
| Manganese | 5.50-7.50 |
| Silicon | 1.00 |
| Nitrogen | 0.25 |
| Phosphorus | 0.060 |
| Sulfur | 0.030 |
Mechanical Properties of 201 Stainless Steel Rod
Mechanical property requirements for annealed products as specified in ASTM A240 and ASME SA240
| Property | 201 |
| Yield Strength, min. (ksi) | 45 |
| Tensile Strength, min. (ksi) | 95 |
| Elongation, min. (%) | 40 |
| Hardness, max. (Rb) | 100 |
Discover the unparalleled mechanical property standards for cold worked flat rolled products as specified in Experience the exceptional quality of 201 Stainless Steel Rod
| Condition | Yield Strength (ksi) min. |
Tensile Strength (ksi) min. |
Elongation % min. in 2 in. | |
| <0.015 in. | ≥0.015 in. | |||
| ¼ Hard | 75 | 125 | 25 | 25 |
| ½ Hard | 110 | 150 | 15 | 18 |
| ¾ Hard | 135 | 175 | 10 | 12 |
| Full Hard | 140 | 185 | 8 | 9 |
Key Physical Properties
Comprehensive Physical Properties for Type 201 Stainless Steel Rod
| Property | 201 |
| Density, lb/in3 | 0.283 |
| Modulus of Elasticity, psi | 28.6 x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 9.2 x 10-6 |
| Thermal Conductivity, Btu/ft hr ˚F | 9.4 |
| Specific Heat, Btu/lb ˚F | 0.12 |
| Electrical Resistivity, Microohm-in | 27.0 |
Our state-of-the-art forming capabilities include cutting-edge radial forging machines, advanced heat treatment furnaces, high-efficiency melting furnaces, and precision rolling mills for titanium rods. Additionally, we offer a unique hydroforming process to craft intricate parts.
Our stainless steel rod heat treatment process employs advanced furnace technology to ensure unparalleled stability and superior material performance.
Daxun Stainless Steel leverages the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace. This sophisticated technology significantly reduces impurities during smelting, thereby enhancing the performance and quality of our stainless steel rods.
Our top-tier stainless steel products come with full certification and traceability. We proudly supply the highest quality stainless steel to distinguished industries such as aerospace, industrial manufacturing, medical sectors, marine applications, and military operations.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
Can you manufacture SS grinding bars & rods?
Yes, we specialize in producing SS grinding bars & rods, characterized by impeccable precision in dimension, roundness, and straightness. These attributes surpass those of standard stainless steel polished bars. However, please note that the enhanced processing quality comes with a higher cost.
Q1: What products can you offer?
A: We offer a wide range of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, and 316L, among others.
Additionally, we provide 400 series stainless steel and duplex stainless steels such as 2205, 2304, 2101, 2507, as well as high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce products according to my own drawings?
Absolutely, we can manufacture products tailored to your specific drawings, ensuring your utmost satisfaction.
Q3. How does your factory manage quality control?
Quality is our top priority. We consistently emphasize stringent quality control from the inception to the final stages of production.
Q4. Can I request changes to the form of packaging and transportation?
Yes, we can alter the packaging and transportation methods according to your specifications.
Please note that you will be responsible for any additional costs incurred during this process.
Q5. How does your factory manage quality control?
Quality is our top priority. We consistently emphasize stringent quality control from the inception to the final stages of production.
Q6. How long is the delivery time?
A: The delivery time ranges from 7 to 20 working days after payment confirmation.
For urgent orders, we expedite the process to ensure timely completion.
Q7. What are your payment terms?
A: 100% T/T in advance, or Western Union for small orders.
B: 30% T/T upfront and the remaining 70% before shipment.
C: 100% Irrevocable LC at sight for large orders.
Q8: Can you produce DDQ (Deep Drawing Quality) materials?
A: Yes, we can. Our materials are ideal for manufacturing stainless steel pots, sinks, bowls, and more. Let us know your specific application, and we will adjust the mechanical properties to meet your needs.
Q9: How can I obtain a sample?
A: FREE samples are available for your evaluation and testing. For smaller pieces, we can cover the courier costs, depending on the situation.
Q10: To which countries have you exported your products?
A: We have exported stainless steel materials to numerous countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many more.
){kind=link}