| Type: | Titanium Sheets |
|---|---|
| Application: | Industrial |
| Technique: | Hot Rolled |
| Grade: | Gr5 Ti-6al-4V Gr7 Gr9 Gr23 |
| Shape: | Square |
| Thickness: | 0.3mm-120mm |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier
| Titanium Plate and sheet Type | Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate |
| Grade | ASME SB265,AMS 4911,AMS 4919,AMS 4914,ASTM F67,ASTM F136, MSRR, AMS, BS |
| Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate Length | 1000mm-13000mm or as required |
| Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Titanium Plate Width | 1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required |
| UNS Plate Thickness | 0.3 to 120mm or as required |
| ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate Process | Hot/ Cold Rolled/forging |
| UNS Plate surface | No.1, No. 2D, No. 2B, BA, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc. |
| ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate, Sheet and Strip | JIS: N0, N2, N1, NW2200, NW2201, NW4400, NW5500, NW6002, etc |
| DIN:H-Ni99.96, H-Ni99.95, H-Ni99.92, H-Ni99.90, H-Ni99.5, H-Ni99, etc | |
| Titanium Gr1 Gr2 Gr3 Gr4 Gr5 Sheet ASTM | ASTM B265 |
| Titanium Gr1 Gr2 Gr3 Gr4 Gr5 Sheet AMS | AMS 4902 |
| Tolerances of width and thickness | EN 10258 (formerly DIN 59381),EN 10151 ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 strip for springs,EN 10088 ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 strip (general) |
| Cp Gr1 Gr2 Gr3 Gr4 Gr5 Titanium Plate standards and approvals | EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID |
DAXUN is your go-to source for commercially pure titanium plates Gr1, Gr2, Gr3, and Gr4 (UNS), available in thicknesses from 0.5 mm to 120 mm. These grades are the workhorses of the commercially pure titanium family, offering a combination of high strength, ductility, and unparalleled corrosion resistance, making them indispensable for a wide array of industrial applications.
Our Gr1, Gr2, Gr3, and Gr4 titanium plates are renowned for their superb balance between strength and ductility. Easy to weld and boasting excellent impact strength, these plates exhibit remarkable corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, weakly reducing environments, and wet ***. Additionally, they offer exceptional resistance to seawater and salt solutions.
Our Grade 5 Ti-6Al-4V titanium alloy plate is a marvel of engineering, containing 90% titanium, 6% aluminum, and 4% vanadium. As an α-β type alloy, aluminum stabilizes the α phase, while vanadium stabilizes the β phase. This results in a material with outstanding comprehensive performance and excellent process capabilities. Known for its room temperature and high-temperature strength, good creep resistance, thermal stability, and high fatigue performance, Grade 5 is ideal for applications requiring high fracture toughness and resistance to hot salt stress corrosion. It is also highly processable and suitable for various welding and machining methods.
About the Chemical Composition of (Ti 6Al-4V) Grade 5 Titanium Sheet
| Chemical Composition: | |||
| Symbol | Element | Min % | Max % |
| Al | Aluminum | 5.50% | 6.75% |
| V | Vanadium | 3.50% | 4.50% |
| Fe | Iron | 0.30% | |
| O | Oxygen | 0.20% | |
| C | Carbon | 0.08% | |
| N | Nitrogen | 0.05% | |
| H | Hydrogen | 0.01% | |
| Y | Yttrium | 0.01% | |
| Other, each | 0.10% | ||
| Other, total | 0.40% | ||
| Ti | Titanium | Remainder | |
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
About the Chemical Composition of Grade 2 TitaniumSheet
| Element | Weight % |
| C | ≤0.08 |
| O | ≤0.25 |
| N | ≤0.03 |
| H | ≤0.015 |
| Fe | ≤0.30 |
| *OEE | ≤0.10 |
| *OET | ≤0.40 |
| Ti | Remaining |
About the Mechanical Properties of Grade 2 Titanium Sheet
| Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
| psi | MPa | ksi | psi | MPa | ksi | % | |||||||
| Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
| 50,000 | |||||||||||||
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
| Fe | 0.2 | ||
| O | 0.18 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
| Density | |
| lb/in3 | g/cm3 |
| 0.163 | 4.51 |
| Tensile Strength | |
| ksi | MPa |
| 35 min | 240 min |
| Yield Strength | |
| ksi | MPa |
| 20 min | 138 min |
| Hardness | |
| 70 HRC max | |
| Elongation | |
| 24% min |
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
|---|---|---|---|
| Al | 2.5 | 3.5 | |
| V | 2.0 | 3.0 | |
| Fe | 0.25 | ||
| O | 0.15 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
1. Cold-Rolled Titanium Plate: This premium plate is meticulously crafted through plate rolling, with the final step being cold rolling. Available in work-hardened or heat-treated conditions, it can be further processed mechanically or chemically based on customer specifications for exceptional strength and durability. 2. Hot-Rolled Titanium Plate: Produced via longitudinal and transverse rolling, this plate boasts a thickness range of 3.0mm to 155mm. Delivered in a heat-treated condition, it can undergo creep flattening to eliminate internal stress and achieve precise flatness. Available in custom-cut blanks, it meets the highest standards of quality and performance, adapting to unique customer requirements.3. Forged Titanium Plate: Created by forging steel ingots on a vertical hydraulic press followed by rolling, or through open die forging. Offering slabs with thickness up to 580mm, width up to 2000mm, and length up to 6000mm, the dimensions and weights are customizable to meet client specifications. This method ensures superior strength and tailored dimensions.
| CP GR1 Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium plate PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
DAXUN, a premier Ti 6AL 4V-Grade 5-TC4 UNS R56400 Alloy Titanium Plate Manufacturer and Supplier from China, is committed to creating the world's finest high-performance titanium alloy plates. We ensure expedient worldwide delivery of ASTM B265 Grade 2 and Grade 5 Titanium Plates. DAXUN produces and maintains an extensive stock of alloy titanium plates Grade 5 (UNS R56400) with thicknesses ranging from 0.5mm to 300mm. Plates from 0.5mm to 6.0mm are cold rolled, 6.0mm to 50mm are hot rolled, and those over 50mm are forged. The Grade 5 titanium plate (Ti-6Al-4V), often referred to as the 'workhorse' of titanium alloys, boasts high strength, ductility, excellent corrosion and high-temperature resistance, making it indispensable across general and military industries. Our products comply with standards such as ASTM, ASME, AMS, GB, GJB, MIL, JIS, and EN.
Ti-6Al-4V grade 5 titanium plate is predominantly utilized in aerospace, military industry, power industry, vehicle armor, rocket precision guidance parts, and marine industry.
Grade 1
Today, DAXUN Alloys stands as a leading global producer and supplier of high-quality Grade 1 titanium plate.
Our pure Grade 1 titanium plate is renowned for its exceptional ductility and cold formability, making it ideal for deep drawing applications. Grade 1 titanium offers outstanding general and seawater corrosion resistance, along with resistance to oxidizing, neutral, and mildly reducing media, including chlorides. Its low density, about half that of nickel-based alloys, coupled with a high strength-to-weight ratio and superb corrosion resistance, makes it an excellent choice for various harsh chemical conditions. Commercially pure Grade 1 titanium is the softest and most ductile, providing excellent cold formability, corrosion resistance, weldability, and good impact hardness.
We specialize in ASTM B265 Titanium Gr 1 Plates, Titanium Gr 1 Sheets, Titanium Gr 1 Finished Plates, ASTM B265 Titanium Grade 1 Coils, Pure Titanium Grade 1 Hot Rolled Plates, Cold Rolled Plates, Titanium ASTM B265 Grade 1 Sheets, Patterned Plates, Perforated Plates, and more. As leading manufacturers in China, we cater to all your Titanium Grade 1 Sheets and Plates needs.
Grade 2
DAXUN produces and stocks commercially pure titanium plates Grade 2 (UNS R50400) with thicknesses ranging from 0.5mm to 120mm. The Grade 2 Titanium Plate (UNS R50400) serves as the 'workhorse' of the commercially pure titanium family, offering an ideal combination of strength, ductility, and excellent corrosion resistance for numerous industrial applications.
Grade 2 Titanium Plate is a commercially pure titanium plate that provides an excellent balance of strength and ductility. It boasts good impact strength, easy weldability, and impressive corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, weakly reducing environments, and wet ***. Additionally, it excels in seawater and salt solutions.
With titanium's low density, high strength-to-weight ratio, and superior corrosion resistance, it is the perfect material for a diverse array of applications. It effectively resists stress corrosion cracking, pitting, and crevice corrosion in chloride solutions below 70°C. Boasting a melting point of 1660°C, Grade 2 Titanium Plate is the preferred alloy for most industrial applications requiring excellent ductility and corrosion resistance.
DAXUN is your go-to metal expert for both small and large titanium plate projects. As your reference point and long-term partner, we are prepared to supply you with titanium plates and provide any technical assistance you may need. Consider DAXUN not only as your supplier of industrial pure titanium plates and titanium alloy plates but also as your strategic partner, helping you navigate any challenges and meet your project goals.
Experience unparalleled efficiency with DAXUN's dedicated service center in China! Our extensive inventory of premium titanium plate products guarantees swift order processing. Leveraging advanced techniques like basic processing, precision water jet cutting, and meticulous plate nesting, we add significant value to your operations, ultimately saving you precious time and reducing costs.
Our relentless commitment to excellence is underscored by DAXUN's continuous investment in state-of-the-art production facilities and strategic capacity agreements with esteemed partners. This proactive approach ensures that DAXUN remains a pioneer in titanium plate quality, both today and in the foreseeable future.
Engage with DAXUN today to access the most competitive titanium plate prices and comprehensive technical information available. Let us help you elevate your projects to new heights with our top-tier products.
Q1: What products can you offer?
A: We proudly provide an extensive range of steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L 300 series.
Additionally, we offer 400 series stainless steel and premium duplex stainless steel such as 2205, 2304, 2101, 2507, and high-nickel alloys like 904L, 800H, 600H.
Q2. Can you produce the products according to my own drawings?
A: Yes, we meticulously craft products to your exact drawings, ensuring your utmost satisfaction.
Q3. How does your factory do regarding quality control?
A: Quality is our highest priority. We consistently emphasize rigorous quality control from inception to completion.
Q4. Can I request to change the form of packaging and transportation?
A: Yes, we can modify packaging and transportation forms based on your requests.
However, please note that you will need to cover any additional costs and differences incurred.
Q5. How does your factory do regarding quality control?
A: Quality is our highest priority. We consistently emphasize rigorous quality control from inception to completion.
Q6. How long is the delivery time?
A: Delivery time ranges from 7 to 20 working days post-payment confirmation.
In urgent cases, we can expedite production for earlier completion.
Q7. What is your Payment?
A: 100% T/T in advance, Western Union (For Small Orders)
B: 30% T/T deposit and balance of 70% before shipment.
C: 100% Irrevocable LC at sight (For Large Orders)
Q8: Can you make DDQ (Deep Drawing Quality)?
A: Yes, we specialize in DDQ materials suitable for stainless steel pots, sinks, bowls, etc. Share your requirements, and we will tailor the mechanical properties to meet your needs.
Q9: How to get a sample?
A: FREE samples are available for your inspection and testing. We can cover the courier cost for small pieces, depending on the situation.
Q10: Which countries have you exported to?
A: We have proudly exported our stainless steel materials worldwide, including countries like Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, and Ukraine, among others.
Q11: How to visit your company?
A: Fly to Guangzhou Baiyun International Airport, and we will arrange a pickup for your convenience.
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}