| Product Parameters: Stainless Steel rod |
| Material |
904L 1.4539 N08904 Super Austenite Round Bar |
| Specifications |
ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions |
EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars |
Outside Diameter in the range of 4mm to 500mm |
| Bright Bars |
Outside Diameter in the range of 4mm to 100mm |
| Hex Bars |
18mm - 57mm (11/16″ to 2-3/4″) |
| Finish |
Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length |
1 to 6 Meters, Custom Cut Lengths |
| Form |
Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability |
Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate |
Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. |
| Under Third Party Inspection |
| Testing & Inspection |
Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Hot Rolled Stainless Steel Rod
Our meticulously hot-rolled stainless steel rods undergo multiple precise passes through the rolling mill. Boasting comprehensive specifications, their performance effortlessly meets and often exceeds industry standards and requirements.
Cold Drawn Bright Stainless Steel Rods
Cold-drawn stainless steel rods undergo meticulous drawing under cold working conditions, resulting in a smooth and superior surface that can also be expertly polished and ground for enhanced finish and utility.
Forged Stainless Steel Rod and Bar
Our forged stainless steel rods are repeatedly forged to significantly improve mechanical properties, offering unparalleled strength and durability.
General Properties
Our extensive network of service centers stocks a vast range of stainless steel bar products for immediate supply. We also offer custom-sized bars and can arrange a stocking program for quantities below factory minimums to ensure a prompt turnaround. Daxun Alloys provides round bars from 1/16" to 26" in diameter, available in nearly every stainless steel grade, including 302, 303, 304/L, 309/S, 310/S, 316/L, 317/L, 321, 321/H, 347, 347H, 410, 416, 420, 440C, 17-4PH, Duplex 2205, and Alloy 20.
Additional Services
Our extensive inventory primarily features our specialized processed bar grade of stainless steel round bars, consistently melted to enhance machinability and reduce overall part costs. Daxun Alloys' advanced bar processing machinery allows us to meet the precise specifications of our clientele.
1. Heat Treatments: Daxun can perform precise heat treatments on our stainless steel bars, tailored to the specific chemistry of the metal being processed. 2. Positive Material Identification (PMI): Additional PMI testing can be conducted in-house or via an independent lab to ensure material integrity. 3. Ultrasonic Testing (UT): Utilizing high-frequency sound energy, our UT services help detect defects, evaluate dimensions, and ensure the quality of our stainless steel bar products.
For more details on our premium stainless steel rods, please contact Daxun.
904L Stainless Steel Rod Chemical Composition
| Element |
% Present (in product form) |
| Carbon (C) |
0.02 |
| Silicon (Si) |
0.7 |
| Manganese (Mn) |
2 |
| Phosphorous (P) |
0.03 |
| Sulfur (S) |
0.01 |
| Chromium (Cr) |
19.00 - 21.00 |
| Nickel (Ni) |
24.00 - 26.00 |
| Nitrogen (N) |
0.15 |
| Molybdenum (Mo) |
4.00 - 5.00 |
| Copper (Cu) |
1.20 - 2.00 |
| Iron (Fe) |
Balance |
904L Stainless Steel Rod Mechanical Properties
| Product Form |
|
|
|
| |
C |
H |
P |
L |
L |
TW/TS |
| Thickness (mm) Max. |
8 |
13.5 |
75 |
160 |
2502) |
60 |
| Yield Strength |
Rp0.2N/mm2 |
2403) |
2203) |
2203) |
2304) |
2305) |
2306) |
| Rp1.0N/mm2 |
2703) |
2603) |
2603) |
2603) |
2603) |
2503) |
| Tensile Strength |
RmN/mm2 |
530 - 7303) |
530 - 7303) |
520 - 7203) |
530 - 7304) |
530 - 7305) |
520 - 7206) |
| Elongation min. in % |
Jmin(Longitudinal) |
- |
100 |
100 |
100 |
- |
120 |
| Jmin(Transverse) |
- |
60 |
60 |
- |
60 |
90 |
904L Stainless Steel Rod Physical Properties
| Density at 20°C kg/m3 |
8 |
| Thermal Conductivity W/m K at |
20°C |
12 |
| Modulus of Elasticity kN/mm2 at |
20°C |
195 |
| 200°C |
182 |
| 400°C |
166 |
| 500°C |
158 |
| Specific Thermal Capacity at 20°C J/kg K |
450 |
| Electrical Resistivity at 20°C mm2/m |
1 |
Daxun's Stainless Steel Rods Manufacturing Capabilities
Our advanced forming capabilities include state-of-the-art radial forging machines, heat treatment furnaces, cutting-edge melting furnaces, and high-precision rolling mills. Additionally, we deploy a unique hydroforming process ideal for manufacturing premium titanium parts.
Daxun's Heat Treatment Furnace
Our sophisticated heat treatment furnaces ensure the stability and high performance of stainless steel rods, guaranteeing unparalleled material quality.
Daxun's Smelting Ability
Daxun Stainless Steel employs the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace. These cutting-edge technologies minimize impurities during the smelting process, significantly enhancing the performance of the finished stainless steel rods.
Let us be your trustworthy stainless steel rod supplier
Our stainless steel products are fully certified and traceable. We supply the highest quality stainless steel to leading industries including aerospace, industrial, medical, marine, and military.
Mechanical properties of various grades of stainless steel bars
| |
Tensile Strength |
Yield Strength |
|
|
|
|
|
|
| Alloy |
UNS Designation |
Spec. |
psi |
MPa |
ksi |
psi |
MPa |
ksi |
Elongation in 2 inches (min.) % |
Grain Size Req. |
Max. Hardness |
Modulus of Elasticity (x106 psi) |
| 304 |
S30400 |
A249, A312 |
75,000 |
515 |
75 |
30,000 |
205 |
30 |
35 |
- |
90 Rb |
28 |
| 304L |
S30403 |
A270 A312 |
70,000 |
485 |
70 |
25,000 |
170 |
25 |
35 |
- |
90 Rb |
28 |
| 304LN |
S30453 |
A249, A688 |
75,000 |
515 |
75 |
30,000 |
205 |
30 |
35 |
- |
90 Rb |
28 |
| 304H |
A30409 |
A249, A312 |
75,000 |
515 |
75 |
30,000 |
205 |
30 |
35 |
7 or coarser |
90 Rb |
28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. |
| Grade |
Tensile Str |
Yield Str |
Elong |
Hardness |
| (MPa) min |
0.2% Proof |
(% in 50mm) min |
| |
(MPa) min |
|
Rockwell B (HR B) max |
Brinell (HB) max |
| 316 |
515 |
205 |
40 |
95 |
217 |
| 316L |
485 |
170 |
40 |
95 |
217 |
| 316H |
515 |
205 |
40 |
95 |
217 |
| |
Tensile Strength |
Yield Strength |
|
|
|
| Alloy |
UNS Designation |
Spec. |
psi |
MPa |
ksi |
psi |
MPa |
ksi |
Elongation in 2 inches (min.) % |
| 321 |
S32100 |
- |
75,000 |
515 |
- |
30,000 |
205 |
- |
35 |
| 321H |
S32109 |
- |
75,000 |
515 |
- |
30,000 |
205 |
- |
35 |
| Grade |
Density |
Melting Point |
Tensile Strength |
Yield Strength (0.2%Offset) |
Elongation |
| 310S |
7.9 g/cm3 |
1402 °C (2555 °F) |
Psi - 75000 , MPa - 515 |
Psi - 30000 , MPa - 205 |
40% |
| Grade |
Tensile Strength |
Yield Strength |
Elongation |
Hardness |
| (MPa) min |
0.2% Proof |
(% in 50mm) min |
| |
(MPa) min |
|
Rockwell C (HR C) |
Brinell (HB) |
| UNS S31803 / 2205 |
621 |
448 |
25 |
31 max |
293 max |
| UNS S32205 / 2205 |
621 |
448 |
25 |
31 max |
293 max |
| Grade |
Property |
Value |
2507/
S32750 |
Density (g/cm3) |
7.8 |
| 0.2% Offset Yield Strength |
80 ksi |
| Ultimate Tensile Strength |
116 ksi |
| 0.1% Offset Yield Strength 0.2% |
91 ksi |
| Elongation in 2 inches, % |
15% |
| Hardness Rockwell C |
32 |
| Impact Energy |
74 ft.-lbs |
| Density |
0.28 lb per inch3 |
| Modulus of elasticity |
28 x 10(6) psi |
| Coefficient of thermal expansion |
7.2 x 10(-6) per of at 68 to 212 of |
| Thermal conductivity |
8.7 Btu/hr ftoF |
| Heat capacity |
0.12 Btu/ lb oF |
| Electrical resistivity |
31.5 x10(-6) ohm-inch |
For more information on stainless steel rods, please contact Daxun