| Type: | Titanium Sheets |
|---|---|
| Application: | Industrial |
| Technique: | Hot Rolled |
| Grade: | GR1 |
| Shape: | Square |
| Thickness: | 0.3mm-120mm |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier
| CP Grade 1 Titanium Plate and sheet Type | Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate |
| Grade | ASME SB265,AMS 4911,AMS 4919,AMS 4914,ASTM F67,ASTM F136, MSRR, AMS, BS |
| Titanium Alloy Gr 1 Plate Length | 1000mm-13000mm or as required |
| Gr 1 Titanium Plate Width | 1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required |
| UNS R50400 Plate Thickness | 0.3 to 120mm or as required |
| ASTM B265 Titanium Alloy Gr 1 Plate Process | Hot/ Cold Rolled/forging |
| UNS R50400 Plate surface | No.1, No. 2D, No. 2B, BA, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled ASTM B265 Titanium Alloy Gr 1 Plate, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc. |
| ASTM B265 Titanium Alloy Gr 1 Plate, Sheet and Strip | JIS: N0, N2, N1, NW2200, NW2201, NW4400, NW5500, NW6002, etc |
| Titanium Grade 1 Sheet ASTM | ASTM B265 |
| Titanium Grade 1 Sheet AMS | AMS 4902 |
| Tolerances of width and thickness | EN 10258 (formerly DIN 59381),EN 10151 ASTM B265 Titanium Alloy Gr 1 strip for springs,EN 10088 ASTM B265 Titanium Alloy Gr 1 strip (general) |
| Ti 6Al 4v Grade 1 Titanium Plate standards and approvals | EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID |
| Standard Grade 1 ALLOY Plate & Sheet Sizes | 1000 x 2000 mm, 1220 x 2440 mm, 1500 x 3000 mm, 2000 x 2000 mm, 2000 x 4000 mm |
| Cold rolled Gr 1 Titanium Plate 0.5-6.4 mm | |
| Hot rolled Gr 1 Titanium Plate 3.0-60.0 mm | |
| UNS R50400 Plate Hardness | Soft, Hard, Half Hard, Quarter Hard, Spring Hard ASTM B265 Titanium Alloy Gr 1 Sheet suppliers |
| Availability of Titanium Alloy Gr 1 Foil sizes | Thickness : 8-100 microns (0.00031-0.004 in) |
| Width: Up to 500 mm (19.5 in) | |
| Weight (in rolls) : Up to 50 kg (110 lb); e.g. approxi- mately 1400 m at 8 microns and ap- proximately 112 m at 100 microns. | |
| Cutting | To provide a comprehensive service, we use a variety of cutting methods, including: |
| Laser Plate Cutting,Plasma Plate Cutting,Oxy-propane Flame Cutting | |
| Plasma profiles | As per customer's drawings |
| Value added services for Cp Grade 1 Titanium Plate | Laser cutting, Waterjet cutting, Plasma cutting, Bending and mechanical processing, edge preparation, welding, sawing and shearing. |
| China Grade 1 Titanium Plate Manufacturer | ASTM B265 Titanium Alloy Gr 1 Plate: material 3/16″ [5.00 mm] and over in thickness and over 10″ [250 mm] in width;Gr 1 Titanium Sheet: material under 3/16″ [5.00 mm] in thickness and 24″ [600 mm] and over in width;Alloy Titanium Grade 1 Clad plate: Alloy Titanium Grade 1 Clad plate is a composite steel plate made by bonding UNS R50400 Titanium Grade 1 Plate, etc.ASTM B265 Titanium Alloy Gr 1 Strip: cold-rolled material under 3/16″ [5.00 mm] in thickness and under 24″ [600 mm] in width. |
| UNS R50400 Plate Origin | CHINA |
| Packing of Grade 1 plate | Bundles with waterproof cloth outside or plywood box |
| Test | UT, SGS testing, TUV etc |
| Why buy UNS R50400 Sheet from DAXUN? | Free quote,Free sample,EN 10204 3.1,Mill Test Certificate is supplied with shipment.,NABL Approved Lab Reports,Any third party inspection is accepted.,Tested to ASTM A923 Method "C" or ASTM G48 Method "A".Minimum Nitrogen content and Ferrite Count Test |
Today, DAXUN Alloys stands as a preeminent global producer and supplier of top-tier Grade 1 titanium plates.
Pure Grade 1 titanium plate boasts exceptional ductility and cold formability, making it perfect for deep drawing applications. Renowned for its superb resistance to general and seawater corrosion, Grade 1 titanium also withstands oxidizing, neutral, and mildly reducing media, including chlorides. With titanium's low density, approximately half that of nickel-based alloys, and an outstanding strength-to-weight ratio, it offers unparalleled resilience in severe chemical environments. As the most pliable and softest commercially pure titanium, Grade 1 is also known for excellent cold formability, corrosion resistance, weldability, and impact hardness.
ASTM B265 Titanium Gr 1 Plate Producers, Titanium Gr 1 Sheets, Titanium Gr 1 Finished Plates, ASTM B265 Titanium Grade 1 Coil Suppliers, Pure Titanium Gr 1 Hot Rolled Plates, Gr 1 Cold Rolled Plates, Titanium ASTM B265 Gr 1 Sheets, Gr 1 Titanium Patterned Plates Dealers, Titanium Gr 1 Perforated Plates, Titanium Grade 1 Sheets and Plates Manufacturers in China.
We ensure swift and prompt delivery of Grade 1 titanium plate products. Our efficient system streamlines production capacity, information flow, logistics, and capital flow. For instance, Daxun's order data integrates seamlessly with our logistics system in real time. Our processing centers, conveniently located near highways, rivers, and seaports, facilitate quick response, efficient scheduling, and coordinated storage and transportation, guaranteeing timely task completion.
Grade 1 titanium plate, known for its lower density and ductility, is perfect for industries prioritizing weight and deep drawing processes. Key industries include medical, chemical equipment, and aerospace sectors. The plate's strength and corrosion resistance make it ideal for marine, chemical processing, and desalination applications. Typical uses include oil and gas components, reaction and pressure vessels, piping systems, power, heat exchangers, linings, and flue gas desulfurization systems. Common standards: ASTM B265, ASTM F67, AMS4911, AMS4928, AMS4943, AMS4944, AMS4945, AMS4967, AMS4972.
The cold rolled thickness range for Grade 1 Titanium Plates spans from 0.3 mm to 6.0 mm, available in hot rolled or heat-treated conditions. The hot rolled thickness range extends from 4.76 mm to 155 mm, produced through longitudinal and transverse rolling. Plates can undergo creep flattening to relieve internal stresses and meet special flatness requirements. Available as cut blanks or complex shapes, the plates can be further processed mechanically or chemically based on customer specifications.
About the chemical composition of(Ti 6AL-4V) grade 5 titanium sheet
| Chemical Composition: | |||
| Symbol | Element | Min % | Max % |
| Al | Aluminum | 5.50% | 6.75% |
| V | Vanadium | 3.50% | 4.50% |
| Fe | Iron | 0.30% | |
| O | Oxygen | 0.20% | |
| C | Carbon | 0.08% | |
| N | Nitrogen | 0.05% | |
| H | Hydrogen | 0.01% | |
| Y | Yttrium | 0.01% | |
| Other, each | 0.10% | ||
| Other, total | 0.40% | ||
| Ti | Titanium | Remainder | |
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
About the chemical composition of grade 2 titanium sheet
| Element | Weight % |
| C | ≤0.08 |
| O | ≤0.25 |
| N | ≤0.03 |
| H | ≤0.015 |
| Fe | ≤0.30 |
| *OEE | ≤0.10 |
| *OET | ≤0.40 |
| Ti | Remaining |
About the mechanical properties of grade 2 titanium sheet
| Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
| psi | MPa | ksi | psi | MPa | ksi | % | |||||||
| Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
| 50,000 | |||||||||||||
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
| Fe | 0.2 | ||
| O | 0.18 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
| Density | |
| lb/in3 | g/cm3 |
| 0.163 | 4.51 |
| Tensile Strength | |
| ksi | MPa |
| 35 min | 240 min |
| Yield Strength | |
| ksi | MPa |
| 20 min | 138 min |
| Hardness | |
| 70 HRC max | |
| Elongation | |
| 24% min |
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
|---|---|---|---|
| Al | 2.5 | 3.5 | |
| V | 2.0 | 3.0 | |
| Fe | 0.25 | ||
| O | 0.15 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
DAXUN is a distinguished leader in the titanium industry, specializing in both small-scale and large-scale titanium plate projects. As your trusted reference point and dedicated long-term partner, DAXUN is committed to providing exceptional titanium plates and comprehensive technical assistance to elevate your business. Beyond being just a supplier of industrial pure titanium plates and titanium alloy plates, DAXUN stands as your strategic ally, poised to help you tackle any challenges and fulfill every need. Our mission is to empower you to achieve your project goals with unparalleled support and expertise.
At DAXUN's premier service center in China, we maintain an extensive inventory of titanium plate products to ensure swift order processing. Our value-added services include basic processing, precision water jet cutting, and plate nesting, all designed to save you time and reduce costs. We are dedicated to delivering not just products, but comprehensive solutions that enhance your operational efficiency.
DAXUN's relentless investment in state-of-the-art production facilities and strategic capacity agreements with our partners guarantee that we remain at the pinnacle of titanium plate quality, now and in the future. This commitment ensures that our customers receive products that meet the highest standards of excellence.
Reach out to DAXUN today to discover the latest titanium plate prices and access a wealth of technical information. Our team is ready to provide you with the insights and solutions you need to excel in your projects.
| CP GR1 Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium plate PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
DAXUN, a premier Ti 6AL 4V-Grade 5-TC4 UNS R56400 Alloy Titanium Plate Manufacturer and Supplier from China, is committed to creating the highest-performance titanium alloy plates worldwide. We offer rapid global delivery of ASTM B265 Grade 2 and Grade 5 Titanium Plates. Our extensive inventory includes Grade 5 (UNS R56400) alloy titanium plates with thicknesses ranging from 0.5mm to 300mm (0.5mm-6.0mm is cold rolled, 6.0-50mm is hot rolled, and thicknesses above 50mm are forged). Known as the 'workhorse' of titanium alloys, Grade 5 titanium plate (Ti-6Al-4V) offers a superb combination of strength, ductility, and exceptional corrosion and high-temperature resistance, making it highly sought after in both general and military industries. Compliance with standards such as ASTE, ASME, AMS, GB, GJB, MIL, JIS, and EN ensures top-quality performance.
Ti-6Al-4V Grade 5 titanium plate is predominantly utilized in aerospace, military applications, power industry, vehicle armor, rocket precision guidance components, and the marine sector.
Grade 1
Today, DAXUN Alloys stands as a global leader in producing and supplying top-tier Grade 1 titanium plates.
Commercially pure Grade 1 titanium plate is renowned for its excellent ductility and cold formability, making it perfect for deep drawing applications. Grade 1 titanium offers outstanding general and seawater corrosion resistance, as well as resistance to oxidizing, neutral, and mildly reducing media (solutions), including chlorides. Its low density (approximately half that of nickel-based alloys), high strength-to-weight ratio, and superior corrosion resistance make it an excellent choice for a variety of harsh chemical environments. The softness and ductility of Grade 1 make it the most workable form of titanium, with exceptional cold formability, corrosion resistance, weldability, and impressive impact hardness.
We are distinguished producers of ASTM B265 Titanium Gr 1 Plates, offering a comprehensive range of products including Titanium Gr 1 Sheets, Finished Plates, Coils, Hot Rolled Plates, Cold Rolled Plates, Patterned Plates, Perforated Plates, and more. As leading manufacturers in China, our Titanium Grade 1 products meet the highest industry standards.
Grade 2
DAXUN specializes in producing and stocking commercially pure titanium plates Grade 2 (UNS R50400), available in thicknesses from 0.5mm to 120mm. Grade 2 Titanium Plate (UNS R50400) is integral within the commercially pure titanium family, offering a balanced mix of strength, ductility, and superb corrosion resistance for numerous industrial applications.
Grade 2 Titanium Plate is known for its commercial purity and excellent balance of strength and ductility. It provides good impact strength, is easily weldable, and boasts strong corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, mildly reducing environments, and wet ***. Additionally, it performs exceptionally well in seawater and salt solutions.
With its low density, high strength-to-weight ratio, and outstanding corrosion resistance, Grade 2 Titanium Plate is an ideal material for a diverse range of applications. It effectively combats stress corrosion cracking, pitting, and crevice corrosion in chloride solutions below 70°C. With a melting point of 1660°C, Grade 2 Titanium Plate is the preferred choice for industrial applications demanding good ductility and corrosion resistance.
As metal experts, DAXUN specializes in both small and large titanium plate projects. We are your reliable partner, providing titanium plates and technical assistance to meet your needs. DAXUN is not just a supplier of industrial pure titanium and titanium alloy plates but also your strategic partner in overcoming challenges and achieving your project goals.
DAXUN's premier service center in China boasts a robust inventory of titanium plate products, enabling swift and efficient order processing. With our suite of advanced services, including basic processing, precision water jet cutting, and optimized plate nesting, we deliver unparalleled value to our clients, significantly reducing both time and costs.
Through relentless investment in cutting-edge production facilities and strategic capacity agreements with our trusted partners, DAXUN consistently leads the market in titanium plate quality, setting industry benchmarks now and for the future.
Reach out to DAXUN today to access the most competitive titanium plate prices and comprehensive technical information tailored to your needs.
Q1: What products can you offer?
A: We proudly offer a diverse range of steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, and 316. Our selection also includes 316L 300 series and various 400 series steels, along with duplex stainless steels such as 2205, 2304, 2101, and 2507. In addition, we supply high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
Yes, we specialize in custom production and can meticulously manufacture products based on your precise drawings to ensure your utmost satisfaction.
Q3. How does your factory ensure quality control?
Quality is our top priority. We implement stringent quality control measures from inception to completion to guarantee superior standards.
Q4. Can I request to change the form of packaging and transportation?
Certainly. We can adapt the packaging and transportation methods to meet your specific requirements.
Please note that any additional costs incurred during this process will be your responsibility.
Q5. How does your factory ensure quality control?
Quality is our top priority. We implement stringent quality control measures from inception to completion to guarantee superior standards.
Q6. How long is the delivery time?
A: Delivery typically takes 7 to 20 working days after payment confirmation.
For urgent orders, we expedite production to meet your deadlines.
Q7. What payment methods do you accept?
A: We accept 100% T/T in advance or Western Union for small orders.
B: For larger orders, 30% T/T in advance and the remaining 70% before shipment.
C: We also accept 100% Irrevocable LC at sight for significant orders.
Q8: Can you produce Deep Drawing Quality (DDQ) materials?
A: Absolutely. Our materials are suitable for manufacturing stainless steel pots, sinks, and bowls. Share your specific usage, and we'll tailor the mechanical properties to meet your needs.
Q9: How can I obtain a sample?
A: We provide FREE samples for your evaluation and testing. For small pieces, we may cover the courier cost, depending on circumstances.
Q10: Which countries have you exported to?
A: To date, we have exported our stainless steel materials to countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
Q11: How can I visit your company?
A: Fly to Guangzhou Baiyun International Airport, and we will arrange to pick you up.
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}