| Product Parameters: Stainless Steel rod | |
| Material | 201 |
| Specifications | ASTM A276, ASME SA276 / ASTM A479 ASME SA479 |
| Dimensions | EN, DIN, JIS, ASTM, BS, ASME, AISI |
| Round Bars | Outside Diameter in the range of 4mm to 500mm |
| Bright Bars | Outside Diameter in the range of 4mm to 100mm |
| Hex Bars | 18mm - 57mm (11/16″ to 2-3/4″) |
| Finish | Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish |
| Length | 1 to 6 Meters, Custom Cut Lengths |
| Form | Round, Square, Hex (A/F), Rectangle, Billet, Ingot, Forging Etc. |
| Marking & Traceability | Each Stainless Steel rod is traceable to its producing mill and heat by an identification number etched within 24″ (610mm) of one end. |
| Test Certificate | Manufacturer Test Certificate according to EN 10204 3.1 B |
| Laboratory Test Certificate from Govt. Approved Lab. | |
| Under Third Party Inspection | |
| Testing & Inspection | Visual inspection • Surface roughness measurement • Helium-leak testing • Scanning Electron Microscopy (SEM) • Auger Electron Microscopy (AES) • Election Spectroscopy for Chemical Analysis (ESCA or XPS) • Particle testing • Moisture testing |
Chemical Composition of 201 Stainless Steel Rod
Chemical Composition (wt%) limits as per ASTM A240 and ASME SA240 standards*
| Element | 201 |
| Carbon | 0.15 |
| Chromium | 16.0-18.0 |
| Nickel | 3.5-5.5 |
| Manganese | 5.50-7.50 |
| Silicon | 1.00 |
| Nitrogen | 0.25 |
| Phosphorus | 0.060 |
| Sulfur | 0.030 |
Mechanical Properties of 201 Stainless Steel Rod
Mechanical property requirements for annealed products as per ASTM A240 and ASME SA240 standards
| Property | 201 |
| Yield Strength, min. (ksi) | 45 |
| Tensile Strength, min. (ksi) | 95 |
| Elongation, min. (%) | 40 |
| Hardness, max. (Rb) | 100 |
Mechanical property requirements for cold worked flat rolled products as specified in The robust and versatile 201 Stainless Steel Rod
| Condition | Yield Strength (ksi) min. |
Tensile Strength (ksi) min. |
Elongation % min. in 2 in. | |
| <0.015 in. | ≥0.015 in. | |||
| ¼ Hard | 75 | 125 | 25 | 25 |
| ½ Hard | 110 | 150 | 15 | 18 |
| ¾ Hard | 135 | 175 | 10 | 12 |
| Full Hard | 140 | 185 | 8 | 9 |
Unparalleled Physical Properties
Outstanding physical properties of Type 201 stainless steel rod
| Property | 201 |
| Density, lb/in3 | 0.283 |
| Modulus of Elasticity, psi | 28.6 x 106 |
| Coefficient of Thermal Expansion, 68-212˚F, /˚F | 9.2 x 10-6 |
| Thermal Conductivity, Btu/ft hr ˚F | 9.4 |
| Specific Heat, Btu/lb ˚F | 0.12 |
| Electrical Resistivity, Microohm-in | 27.0 |
Our forming capabilities include cutting-edge radial forging machines, advanced heat treatment furnaces, high-precision melting furnaces, and efficient rolling mills for manufacturing titanium rods. Additionally, we employ a unique hydroforming process for crafting intricate parts.
Our stainless steel rod heat treatment leverages advanced furnace technology to guarantee material stability and superior performance.
Utilizing the world's most advanced vacuum induction furnace, vacuum consumable furnace, and electroslag furnace, Daxun reduces impurities during the smelting process to enhance the performance of our stainless steel rods.
Our stainless steel products are fully certified and traceable. We supply the highest quality stainless steel to leading industries including aerospace, industry, medical, marine, and military sectors.
| Tensile Strength | Yield Strength | |||||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % | Grain Size Req. | Max. Hardness | Modulus of Elasticity (x106 psi) |
| 304 | S30400 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304L | S30403 | A270 A312 | 70,000 | 485 | 70 | 25,000 | 170 | 25 | 35 | - | 90 Rb | 28 |
| 304LN | S30453 | A249, A688 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | - | 90 Rb | 28 |
| 304H | A30409 | A249, A312 | 75,000 | 515 | 75 | 30,000 | 205 | 30 | 35 | 7 or coarser | 90 Rb | 28 |
| The Mechanical Properties of grade 316L Stainless Steel are displayed in the following table. | |||||
| Grade | Tensile Str | Yield Str | Elong | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell B (HR B) max | Brinell (HB) max | |||
| 316 | 515 | 205 | 40 | 95 | 217 |
| 316L | 485 | 170 | 40 | 95 | 217 |
| 316H | 515 | 205 | 40 | 95 | 217 |
| Tensile Strength | Yield Strength | ||||||||
| Alloy | UNS Designation | Spec. | psi | MPa | ksi | psi | MPa | ksi | Elongation in 2 inches (min.) % |
| 321 | S32100 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| 321H | S32109 | - | 75,000 | 515 | - | 30,000 | 205 | - | 35 |
| Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 310S | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi - 75000 , MPa - 515 | Psi - 30000 , MPa - 205 | 40% |
| Grade | Tensile Strength | Yield Strength | Elongation | Hardness | |
| (MPa) min | 0.2% Proof | (% in 50mm) min | |||
| (MPa) min | Rockwell C (HR C) | Brinell (HB) | |||
| UNS S31803 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| UNS S32205 / 2205 | 621 | 448 | 25 | 31 max | 293 max |
| Grade | Property | Value |
| 2507/ S32750 |
Density (g/cm3) | 7.8 |
| 0.2% Offset Yield Strength | 80 ksi | |
| Ultimate Tensile Strength | 116 ksi | |
| 0.1% Offset Yield Strength 0.2% | 91 ksi | |
| Elongation in 2 inches, % | 15% | |
| Hardness Rockwell C | 32 | |
| Impact Energy | 74 ft.-lbs | |
| Density | 0.28 lb per inch3 | |
| Modulus of elasticity | 28 x 10(6) psi | |
| Coefficient of thermal expansion | 7.2 x 10(-6) per of at 68 to 212 of | |
| Thermal conductivity | 8.7 Btu/hr ftoF | |
| Heat capacity | 0.12 Btu/ lb oF | |
| Electrical resistivity | 31.5 x10(-6) ohm-inch |
Can you manufacture SS grinding bars & rods?
Yes, we specialize in producing SS grinding bars & rods that boast precise dimensions, impeccable roundness, and unwavering straightness. These qualities surpass those of standard stainless steel polished bars, albeit at a higher processing cost.
Q1: What products do you offer?
A: We offer a variety of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, and 316L.
Additionally, we provide 400 series and duplex stainless steel like 2205, 2304, 2101, and 2507, as well as high-nickel alloys such as 904L, 800H, and 600H.
Q2: Can you produce products based on my drawings?
Yes, we can meticulously craft products according to your precise drawings, ensuring your utmost satisfaction.
Q3: How does your factory handle quality control?
Quality is our top priority. We consistently prioritize rigorous quality control from start to finish.
Q4: Can I request changes to the packaging and transportation methods?
Yes, we can adapt the packaging and transportation methods to meet your specific requests,
though you must bear any additional costs incurred during this period, including any price differences.
Q5: How does your factory handle quality control?
Quality is our top priority. We consistently prioritize rigorous quality control from start to finish.
Q6: What is your delivery time?
A: Our delivery time ranges from 7 to 20 working days after payment confirmation.
For urgent orders, we expedite production to meet your deadlines.
Q7: What are your payment terms?
A: For small orders, 100% T/T in advance or Western Union.
B: For larger orders, 30% T/T upfront and 70% balance before shipment.
C: For significant orders, 100% Irrevocable LC at sight.
Q8: Can you produce DDQ (Deep Drawing Quality) material?
A: Absolutely. Our materials are ideal for deep drawing applications such as stainless steel pots, sinks, and bowls. Provide your specific usage, and we will adjust the mechanical properties to meet your requirements.
Q9: How can I obtain a sample?
A: We provide FREE samples for your inspection and testing. For small pieces, we may cover the courier cost, depending on the situation.
Q10: To which countries have you exported?
A: To date, we have exported our stainless steel materials to Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many more.
){kind=link}