| Material | Titanium rod and bar Grade 5 Ti6Al4V |
| Standard | ASTM B348, ASTM SB348, AMS 4921, AMS 4902 |
| Dimensions | EN, ASTM, JIS, ASME, BS, AISI |
| Diameter Range | 0.125″ - 14″ (3.175mm - 355.6mm), custom |
| Length Range | Up to 240″ (6096mm), custom |
| Finish | Cold (bright) drawn, centreless ground, hot rolled, smooth turned, peeled, slit rolled edge, hot rolled annealed, Rough Turned, Bright, Polish, Grinding, Centreless Ground & Black |
| Surface Finish | Cold drawn, Centerless Ground, Polished, Or Rough Turned, Black, NO.4 Finish, BA Finish, Matt Finish, etc. |
| Condition | Hardened & tempered, annealed |
| Tolerance | Diameter tolerance: +/- 0.005″ (0.127mm), length tolerance: +/- 0.125″ (3.175mm) |
| Form | Titanium square bars, titanium ingots, titanium round bars, rectangular titanium bars, triangular titanium bars, forged titanium bars, titanium hexagonal bars, etc. |
Grade 5 titanium alloy rod (titanium aluminum vanadium alloy) is the most widely utilized α-β titanium alloy, representing 50% of global titanium alloy usage. Renowned for its full heat treatability, this alloy excels at temperatures up to 400°C. It boasts a low density (4.43 kg/dm), superior corrosion resistance, and exceptional mechanical strength. Grade 5 titanium delivers remarkable tensile strength at ambient temperature and outstanding creep resistance up to 300°C. With substantial *** and fatigue resistance, the 6AL-4V titanium alloy rod is ideal for diverse applications, including fasteners and components in severe conditions. Its age-hardening capability, combined with high machinability and weldability, makes it a versatile solution for various industrial uses.
DAXUN® Ti Grade 5 is a titanium alloy bar (6al-4v) distinguished by:
Daxun produces premium titanium bars with exemplary performance, also offering customization per customer's specifications:
Daxun's stringent quality assurance includes mechanical tests (e.g., area tensile), chemical analysis, PMI testing, micro and macro examination, IGC test, ultrasonic flaw detection, pitting and resistance tests, hardness tests, and more. These tests certify the suitability of Grade 2 Titanium Rod and Grade 2 Titanium Round Bar for their intended applications. Throughout production, we meticulously measure the product's diameter, thickness, and surface.
Chemical Composition of (Ti 6AL-4V) Grade 5 Titanium Rods
| Chemical Composition: | |||
| Symbol | Element | Min % | Max % |
| Al | Aluminum | 5.50% | 6.75% |
| V | Vanadium | 3.50% | 4.50% |
| Fe | Iron | 0.30% | |
| O | Oxygen | 0.20% | |
| C | Carbon | 0.08% | |
| N | Nitrogen | 0.05% | |
| H | Hydrogen | 0.01% | |
| Y | Yttrium | 0.01% | |
| Other, each | 0.10% | ||
| Other, total | 0.40% | ||
| Ti | Titanium | Remainder | |
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
Chemical Composition of Grade 2 Titanium Rods
| Element | Weight % |
| C | ≤0.08 |
| O | ≤0.25 |
| N | ≤0.03 |
| H | ≤0.015 |
| Fe | ≤0.30 |
| *OEE | ≤0.10 |
| *OET | ≤0.40 |
| Ti | Remaining |
Mechanical Properties of Grade 2 Titanium Rods
| Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
| psi | MPa | ksi | psi | MPa | ksi | % | |||||||
| Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
| 50,000 | |||||||||||||
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
| Fe | 0.2 | ||
| O | 0.18 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
| Density | |
| lb/in3 | g/cm3 |
| 0.163 | 4.51 |
| Tensile Strength | |
| ksi | MPa |
| 35 min | 240 min |
| Yield Strength | |
| ksi | MPa |
| 20 min | 138 min |
| Hardness | |
| 70 HRC max | |
| Elongation | |
| 24% min |
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
|---|---|---|---|
| Al | 2.5 | 3.5 | |
| V | 2.0 | 3.0 | |
| Fe | 0.25 | ||
| O | 0.15 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
Daxun Alloys proudly stocks a comprehensive range of Titanium Rods, including Grade 1, Grade 2, and the highly sought-after Grade 5. Available in diameters ranging from 1mm to 300mm, we cater to a diverse array of projects, from general industrial uses to advanced military aerospace applications. For sizes beyond our standard range, custom orders are welcome. Contact Daxun for a competitive quote. Each rod is meticulously certified to ASTM B348 and ASTM B381 standards, ensuring unmatched quality. Explore our high-caliber selection of pure titanium and titanium alloy rods, and reach out for expert advice and seamless purchasing experience.
Daxun boasts a sophisticated technology cycle that spans from raw material processing to the production of meticulously finished products. Our bar products are readily available across our extensive service center network, facilitating rapid, off-the-shelf delivery for common sizes and alloys. We also specialize in custom size manufacturing and offer flexible stocking programs to ensure quick turnaround, perfectly suited for just-in-time deliveries even for quantities below the mill minimum.
| CP GR1 Titanium rods PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium rods PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium rods PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
Daxun At Jiangsu Daxun Alloy Co., Ltd., we produce highly competitive, high-precision Grade 1 titanium bars within our state-of-the-art production facilities in China. Boasting excellent surface finishes, tight tolerances, superior straightness, and unparalleled material quality, we provide technological leadership and consistent production processes suitable for a vast range of diameters and materials. Additionally, our comprehensive stocking program at our service center ensures just-in-time delivery to meet your specific needs.
We produce bars tailored to your specific requirements.
Delivering excellent surface finishes, perfect straightness, ideal roundness, and the tightest diameter tolerances (according to ISO 286-2, up to h5). Available in straightened, ground, and polished conditions.
Sawing
Band saws (up to Ø510 mm)
Bench band saws (up to 6,000 x 3,000 x 400 mm)
High-performance sawing machines for precise cuts
Single or double-sided
Chamfer 90° (45°)
Point 60° (30°)
Flat end
Centered
ASTM - American Society for Testing and Materials Standards
AMS - American Aerospace Materials Standards
NACE - American Association of Corrosion Engineers International Standards
ASME - American Society of Mechanical Engineers Standards
GB - Chinese National Standards
GJB - Chinese National Military Standards
ISO - International Standards
DIN - German Standards
EN - European Standards
API - American Petroleum Institute Standards
Non-destructive testing > 100% testing
Testing Methods
Eddy current testing/eddy current *** testing
Defect-free surface verification (level 4)
Flat bottom hole diameters: 0.7 mm and 0.4 mm
Blind areas can be cut off to fixed lengths >Testing to the end of the bar
Full diameter ultrasonic testing
Ensure your purchase orders include: quantity, grade, type or category, API5L reference, thickness, width, length, and all additional requirements related to chemical composition, mechanical properties, heat treatment, additional testing, manufacturing process, surface coating, or end finish. Contact Daxun now, and expect a prompt email response.
Grade 5 Titanium Rod
Daxun boasts a cutting-edge production facility in China. We produce highly competitive, precision-engineered Grade 5 titanium bars featuring exceptional surface finish, tolerance, straightness, and material quality. These attributes ensure technological leadership and consistent production processes across various diameters and materials. Our comprehensive stock program at our service center further enables just-in-time delivery.
AMS 4928 - Bars, Forgings, and Forging Stock (Annealed)
AMS 4965 - Bars, Forgings (Solution treated and aged)
AMS 4967 - Bars, Forgings (Annealed, Heat Treatable)
In the solution treated and aged condition, rapid quenching of small sections ensures optimal properties, while larger sections or delayed quenching may result in reduced properties.
In the annealed condition, typical hardness ranges from Rockwell C 30-34. In the solution and aged condition, hardness typically ranges from Rockwell C 35-39.
The Ti-6Al-4V, Grade 5 alloy bar can be expertly machined using techniques designed for austenitic stainless steel, requiring slow machining speeds, high feeds, rigid tools, and an ample amount of non-chlorinated cutting fluids for optimal results.
The Ti-6Al-4V, Grade 5 alloy rod boasts excellent weldability in both annealed and solution/partially aged conditions, with post-weld heat treatment completing the aging process. Special care is necessary to avoid contamination by oxygen, nitrogen, and hydrogen. Fusion welding should be carried out in an inert gas-filled chamber or with inert gas shielding to protect the molten metal and adjacent zones. Spot, seam, and flash welding can be performed without a protective atmosphere.
When working with Ti-6Al-4V, Grade 5 titanium alloy rod, it is crucial to prevent contamination by hydrogen during pickling, and by oxygen, nitrogen, and carbon during processes such as forging, heat treating, and brazing. Such contamination can reduce ductility, negatively impacting notch sensitivity and forming characteristics.
We manufacture bars tailored to your specifications.
Achieve exceptional surface quality and straightness with perfect roundness and the tightest diameter tolerances (ISO 286-2 up to h5). Available in straightened, ground, and polished conditions.
Sawing
Band saws (up to Ø510 mm)
Bench band saws (up to 6,000 x 3,000 x 400 mm)
High-performance sawing machines ensure precise cuts
Single or double-sided
Chamfer 90° (45°)
Point 60° (30°)
Flat end
Centered
ASTM American Society for Testing and Materials Standards
AMS: The Premier Benchmark for American Aerospace Materials Standards
NACE: The Gold Standard from the American Association of Corrosion Engineers International
ASME: Gold Standard by the American Society of Mechanical Engineers
GB: The Pillar of Chinese National Standards
GJB: The Benchmark for Chinese National Military Standards
ISO: The Global Standard of Excellence
DIN: Precision and Reliability in German Standards
EN: Synonymous with Excellence in European Standards
API: The Paragon of American Petroleum Institute Standards
Non-Destructive Testing: Ensuring 100% Integrity
Sophisticated Testing Methods
Eddy Current Testing/ Eddy Current *** Testing: Precision at Its Best
Defect-Free Surface Assurance (Level 4)
Flat Bottom Hole Diameters: 0.7 mm and 0.4 mm for Ultimate Precision
Blind Area Elimination: Custom Cuts for Thorough Testing to the End of the Bar
Comprehensive Full Diameter Ultrasonic Testing
Your purchase order should detail the quantity, grade, type, API5L reference, dimensions, and any specific requirements regarding chemical composition, mechanical properties, heat treatment, additional testing, manufacturing processes, surface coating, or end finish. Reach out to Daxun for prompt email responses.
Note: Titanium should not be used with strong reducing acids, fluoride solutions, pure oxygen, or anhydrous ***.
Table 1 illustrates the general corrosion rates for Grade 2 titanium in various media. CP titanium demonstrates excellent corrosion resistance in a multitude of environments, including:
CP titanium offers remarkable resistance to crevice corrosion in salt solutions compared to stainless steels. It withstands crevice corrosion at temperatures below 80°C (176°F) irrespective of pH, even in highly chlorinated conditions.
Grade 2 titanium exhibits superior resistance to stress corrosion cracking (SCC) in hot chloride solutions and remains immune to SCC in seawater.
Titanium exhibits outstanding resistance to erosion in flowing environments.
Seawater with velocities up to 130 ft/sec (40 m/sec) has a negligible effect on the material. Even the presence of abrasive particles like sand has only a minimal impact on corrosion.
Titanium shows no significant absorption of hydrogen even in seawater at elevated temperatures. Hydrogen absorption typically occurs only under the following three conditions:
Titanium alloys exhibit unique immunity to microbiologically influenced corrosion. Although they do not display toxicity toward marine organisms, biofouling can occur in seawater, which can be minimized by chlorination or increasing water velocity through the heat exchanger.
Unlike many materials, titanium does not experience reduced fatigue performance in seawater. Fatigue endurance limits and *** growth rates remain consistent whether tested in air or seawater.
Titanium sits near the noble end in the galvanic series, close to stainless steels, and generally acts as the cathode when coupled with other metals. This means titanium itself is not affected by galvanic corrosion but can accelerate the corrosion of the other metal. Pairing titanium with more noble metals, like graphite, only enhances its passivity.
Grade 2 Titanium Rod maintains its fatigue properties in seawater, showing no degradation. Its fatigue endurance limits and *** growth rates are consistent whether tested in air or seawater.
CP2 Grade Titanium Rod is highly weldable with proper precautions. Due to its reactivity, an inert gas shield must be used on both the outer and inner diameters. The material must be clean, free of grease or oil contamination.
Grade 2 Titanium Rod is typically welded using TIG welding, either manually or automatically, with or without filler wire. Low heat input is recommended to minimize the heat-affected zone, and post-weld heat treatment is usually not necessary.
| Working material: | 3.7035 / UNS R50400 |
| Diameter: | 3 - 400 mm |
| Lengths: | 2.000 - 4.000 mm |
| Versions: | Rolled, forged, annealed |
| Surfaces: | Turned, peeled, polished |
| Standards: | ASTM B 348, ASME SB 348, DIN 17862, ASTM F 67, NACE MR 0175, ISO 1515156-3, ISO 5832-2 |
Looking for round rod material made of Grade 2 Titanium Alloy Rod-3,7035? At Daxun, we offer customized titanium rods to meet your project's needs as an experienced supplier.
We provide Grade 2 Titanium bars in diameters ranging from 2.0 mm to 400 mm. Note that execution and tolerances may vary: small diameters are delivered centerless ground with h7 tolerances, while larger diameters come with h9 or h11 tolerances.
To place an order, please include the following details: quantity, grade, type or category, API5L reference, thickness, width, length, and any relevant attachments or specific requirements pertaining to chemical composition, mechanical properties, heat treatment, additional testing, manufacturing process, surface coating, or end finish. Reach out to Jiangsu Daxun Alloy Co., Ltd. today, and we will respond to your email promptly.
Q1: What products can you offer?
A: We offer a comprehensive range of general steel types, including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L, and 300 series.
Additionally, we provide 400 series and duplex stainless steel, such as 2205, 2304, 2101, 2507, and high-nickel alloys like 904L, 800H, and 600H.
Q2: Can you produce products according to my own drawings?
A: Yes, we can manufacture products that adhere to your specific drawings, ensuring they meet your utmost satisfaction.
Q3: How does your factory handle quality control?
A: Quality is our top priority. We consistently emphasize stringent quality control measures from start to finish.
Q4: Can I request to change the form of packaging and transportation?
A: Yes, we can modify packaging and transportation to suit your preferences.
However, any additional costs and discrepancies incurred during this process will be your responsibility.
Q5: How does your factory handle quality control?
A: Quality is our top priority. We consistently emphasize stringent quality control measures from start to finish.
Q6: How long is the delivery time?
A: The delivery time ranges from 7 to 20 working days after payment confirmation.
If the order is urgent, we will expedite the production process to meet your timeline.
Q7: What are your payment terms?
A: For small orders, we accept 100% T/T in advance or Western Union.
B: For larger orders, a 30% T/T deposit and the remaining 70% before shipment are required.
C: For substantial orders, we accept a 100% Irrevocable LC at sight.
Q8: Can you produce Deep Drawing Quality (DDQ) materials?
A: Yes, we can. Our materials are suitable for manufacturing stainless steel pots, sinks, bowls, etc. Inform us of your specific use case, and we will adjust the mechanical properties to meet your requirements.
Q9: How can I obtain a sample?
A: FREE samples are available for inspection and testing. For small pieces, we may cover the courier cost, depending on the circumstances.
Q10: Which countries have you exported to?
A: We have exported stainless steel materials to Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
Q11: How can I visit your company?
A: Fly to Guangzhou Baiyun International Airport, and we will arrange for your pickup.
){kind=link}