| Type: | Titanium Sheets |
|---|---|
| Application: | Industrial |
| Technique: | Hot Rolled |
| Grade: | Gr5 Ti-6al-4V Gr7 Gr9 Gr23 |
| Shape: | Square |
| Thickness: | 0.3mm-120mm |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier
| Titanium Plate and sheet Type | Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate |
| Grade | ASME SB265,AMS 4911,AMS 4919,AMS 4914,ASTM F67,ASTM F136, MSRR, AMS, BS |
| Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate Length | 1000mm-13000mm or as required |
| Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Titanium Plate Width | 1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required |
| UNS Plate Thickness | 0.3 to 120mm or as required |
| ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate Process | Hot/ Cold Rolled/forging |
| UNS Plate surface | No.1, No. 2D, No. 2B, BA, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc. |
| ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate, Sheet and Strip | JIS: N0, N2, N1, NW2200, NW2201, NW4400, NW5500, NW6002, etc |
| DIN:H-Ni99.96, H-Ni99.95, H-Ni99.92, H-Ni99.90, H-Ni99.5, H-Ni99, etc | |
| Titanium Gr1 Gr2 Gr3 Gr4 Gr5 Sheet ASTM | ASTM B265 |
| Titanium Gr1 Gr2 Gr3 Gr4 Gr5 Sheet AMS | AMS 4902 |
| Tolerances of width and thickness | EN 10258 (formerly DIN 59381),EN 10151 ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 strip for springs,EN 10088 ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 strip (general) |
| Cp Gr1 Gr2 Gr3 Gr4 Gr5 Titanium Plate standards and approvals | EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID |
DAXUN offers an extensive range of commercially pure titanium plates, featuring Gr1, Gr2, Gr3, and Gr4 (UNS) grades. These plates, available in thicknesses from 0.5 mm to 120 mm, are the epitome of versatility within the titanium family. Known as the 'workhorse' of commercially pure titanium, they embody exceptional strength, ductility, and unparalleled corrosion resistance, making them indispensable for numerous industrial applications.
Gr1, Gr2, Gr3, and Gr4 titanium plates are renowned for their exemplary balance of strength and ductility. They boast impressive impact strength, effortless weldability, and superior corrosion resistance, even in highly oxidizing environments, alkaline media, brine solutions, weakly reducing environments, and wet ***. Their outstanding resistance to seawater and salt solutions makes them a prime choice for diverse applications.
The Grade 5 Ti-6Al-4V titanium plate, an α-β titanium alloy, consists of 90% titanium, 6% aluminum, and 4% vanadium. This composition ensures aluminum stabilizes the α phase while vanadium stabilizes the β phase, leading to excellent comprehensive and process performance. TC4 titanium alloy is celebrated for its high strength at room and high temperatures, exceptional creep resistance, and thermal stability. It excels in fatigue performance, *** growth resistance in seawater, and provides satisfactory fracture toughness and hot salt stress corrosion performance. Additionally, the Gr5 Ti-6Al-4V plate offers superb process plasticity and superplasticity, making it ideal for various processing, welding, and machining methods.
In-depth Information on the Chemical Composition of Grade 5 Titanium Sheets (Ti 6Al-4V)
| Chemical Composition: | |||
| Symbol | Element | Min % | Max % |
| Al | Aluminum | 5.50% | 6.75% |
| V | Vanadium | 3.50% | 4.50% |
| Fe | Iron | 0.30% | |
| O | Oxygen | 0.20% | |
| C | Carbon | 0.08% | |
| N | Nitrogen | 0.05% | |
| H | Hydrogen | 0.01% | |
| Y | Yttrium | 0.01% | |
| Other, each | 0.10% | ||
| Other, total | 0.40% | ||
| Ti | Titanium | Remainder | |
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
Insight into the Chemical Composition of Grade 2 TitaniumSheets
| Element | Weight % |
| C | ≤0.08 |
| O | ≤0.25 |
| N | ≤0.03 |
| H | ≤0.015 |
| Fe | ≤0.30 |
| *OEE | ≤0.10 |
| *OET | ≤0.40 |
| Ti | Remaining |
Details on the Mechanical Properties of Grade 2 Titanium Sheets
| Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
| psi | MPa | ksi | psi | MPa | ksi | % | |||||||
| Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
| 50,000 | |||||||||||||
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
| Fe | 0.2 | ||
| O | 0.18 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
| Density | |
| lb/in3 | g/cm3 |
| 0.163 | 4.51 |
| Tensile Strength | |
| ksi | MPa |
| 35 min | 240 min |
| Yield Strength | |
| ksi | MPa |
| 20 min | 138 min |
| Hardness | |
| 70 HRC max | |
| Elongation | |
| 24% min |
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
|---|---|---|---|
| Al | 2.5 | 3.5 | |
| V | 2.0 | 3.0 | |
| Fe | 0.25 | ||
| O | 0.15 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
1. Cold-Rolled Titanium Plate: This titanium plate is meticulously crafted through plate rolling, with the final step being cold rolling. Available in work-hardened or heat-treated conditions, these sheets can be further processed according to your specific requirements. Choose from mechanical or chemical processing to tailor the product to your needs. 2. Hot-Rolled Titanium Plate: Produced via longitudinal and transverse rolling, these plates come in thicknesses ranging from 3.0mm to 155mm and are supplied in a heat-treated condition. For special flatness requirements, creep flattening can be utilized to eliminate internal stress. Available as cut blanks, offering complex shaped parts derived from parent metal. Further processing will be tailored to meet your specific requirements.3. Forged Titanium Plate: Produced by forging steel ingots on a vertical hydraulic press followed by rolling, or through open die forging. Standard slab dimensions include thickness up to 580mm, width up to 2000mm, and length up to 6000mm. The dimensions and weight of the forged plates are customizable, agreed upon between the manufacturer and the customer.
| CP GR1 Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium plate PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
DAXUN is a premier manufacturer and supplier of Ti 6AL 4V-Grade 5-TC4 UNS R56400 Alloy Titanium Plates from China! With an unwavering commitment to delivering the world's highest-performance titanium alloy plates, we offer rapid worldwide shipping for ASTM B265 Grade 2 and Grade 5 Titanium Plates. At DAXUN, we maintain a robust inventory of alloy titanium plates Grade 5 (UNS R56400) with thicknesses spanning 0.5mm to 300mm. Our offerings include cold rolled (0.5mm-6.0mm), hot rolled (6.0-50mm), and forged plates (50mm and above). Grade 5 titanium plate (Ti-6Al-4V) is celebrated as the 'workhorse' of titanium alloys, boasting high strength, ductility, and superior corrosion and high-temperature resistance. These traits make it a preferred choice across general and military industries. Our products meet stringent standards including ASTE, ASME, AMS, GB, GJB, MIL, JIS, EN, and more.
Ti-6Al-4V grade 5 titanium plates are integral to aerospace, military, power industry, vehicle armor, rocket precision guidance parts, and marine industry applications.
Grade 1
DAXUN Alloys proudly stands as a leading global producer and supplier of top-tier Grade 1 titanium plates.
Pure Grade 1 titanium plates from DAXUN exhibit exceptional ductility and cold formability, making them ideal for deep drawing applications. Renowned for outstanding general and seawater corrosion resistance, Grade 1 titanium also excels in oxidizing, neutral, and mildly reducing environments, including chloride solutions. The low density (approximately half that of nickel-based alloys), high strength-to-weight ratio, and corrosion resistance make it an optimal choice for challenging chemical environments. As the softest and most ductile commercially pure titanium, Grade 1 offers excellent cold formability, corrosion resistance, weldability, and good impact hardness.
DAXUN is a trusted producer of ASTM B265 Titanium Gr 1 Plates and Sheets, offering a range of products including Titanium Gr 1 Finished Plates, Hot Rolled Plates, Cold Rolled Plates, Titanium ASTM B265 Gr 1 Sheets, Patterned Plates, Perforated Plates, and Coils. We are your go-to manufacturers and dealers for Pure Titanium Gr 1 products in China.
Grade 2
DAXUN specializes in producing and stocking commercially pure titanium plates Grade 2 (UNS R50400) with thicknesses from 0.5mm to 120mm. Known as the 'workhorse' of commercially pure titanium, the Grade 2 Titanium Plate (UNS R50400) is prized for its high strength, ductility, and excellent corrosion resistance across numerous industrial applications.
Grade 2 Titanium Plate is a commercially pure titanium offering that presents an excellent balance of strength and ductility. With robust impact strength and ease of welding, it exhibits superior corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, weakly reducing environments, and wet ***. Moreover, it performs exceptionally well in seawater and salt solutions.
With titanium's low density, high strength-to-weight ratio, and superior corrosion resistance, Grade 2 Titanium Plate is a versatile material suitable for numerous applications. It effectively combats stress corrosion cracking, pitting, and crevice corrosion in chloride solutions below 70°C. Featuring a melting point of 1660°C, Grade 2 Titanium Plate is the preferred alloy for industrial applications requiring a combination of ductility and corrosion resistance.
As experts in the field, DAXUN is dedicated to both small and large titanium plate projects. We are your go-to reference and long-term partner, offering not only products but also essential technical assistance. Trust DAXUN as your strategic partner to help you overcome challenges, meet your needs, and achieve your project objectives with our high-quality industrial pure titanium plates and titanium alloy plates.
At Jiangsu Daxun Alloy Co., Ltd., our state-of-the-art service center in China ensures that titanium plate products are readily available for swift order fulfillment. We add unparalleled value through essential processing techniques, precise water jet cutting, and efficient plate nesting solutions. Our commitment saves customers both time and money, providing a seamless experience.
Thanks to continuous investment in our advanced production facilities and strategic capacity agreements with esteemed partners, Daxun remains a leader in titanium plate quality. This unwavering dedication ensures that Jiangsu Daxun Alloy Co., Ltd. sets the benchmark for excellence now and in the future.
Reach out to Jiangsu Daxun Alloy Co., Ltd. today to access competitive titanium plate pricing and comprehensive technical details. Experience the pinnacle of quality and service with Daxun.
Q1: What products can you offer?
A: We offer a comprehensive range of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L, along with the 300 series.
We also specialize in 400 series and duplex stainless steel varieties like 2205, 2304, 2101, 2507. Our portfolio includes high-nickel alloys such as 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
Absolutely! We can manufacture products precisely based on your drawings, ensuring they meet your utmost satisfaction.
Q3. How does your factory do regarding quality control?
Quality is our top priority. We consistently emphasize stringent quality control measures from the inception of production to its completion.
Q4. Can I request to change the form of packaging and transportation?
Yes, we can customize the packaging and transportation methods according to your requirements.
Please note that additional costs and any incurred differences will be your responsibility.
Q5. How does your factory do regarding quality control?
Quality is our top priority. We consistently emphasize stringent quality control measures from the inception of production to its completion.
Q6. How long is the delivery time?
A: Standard delivery time is 7~20 working days post payment confirmation.
For urgent orders, we can expedite the production process to meet your timeline.
Q7. What are your payment terms?
A: 100% T/T in advance, Western Union for small orders.
B: 30% T/T upfront and the remaining 70% before shipment.
C: 100% Irrevocable LC at sight for bulk orders.
Q8: Can you produce Deep Drawing Quality (DDQ) products?
A: Yes, we specialize in DDQ materials suitable for producing stainless steel pots, sinks, bowls, etc. Share your specific needs, and we will tailor the mechanical properties accordingly.
Q9: How can I get a sample?
A: FREE samples are available for your evaluation. For small-sized samples, we may cover the courier cost depending on the situation.
Q10: Which countries have you exported to?
A: We have exported stainless steel materials to numerous countries, including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
Q11: How can I visit your company?
A: Fly into Guangzhou Baiyun International Airport, and we will arrange to pick you up.
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}