| Type: | Titanium Sheets |
|---|---|
| Application: | Industrial, Medical, Aerospace |
| Technique: | Hot Rolled |
| Grade: | GR2 |
| Shape: | Square |
| Transport Package: | Wooden Pallet |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
| Titanium Plate and sheet Type | Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate |
| Grade | ASME SB265,AMS 4911,AMS 4919,AMS 4914,ASTM F67,ASTM F136, MSRR, AMS, BS |
| Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al 4V Plate Length | 1000mm-13000mm or as required |
| Gr1 Gr2 Gr3 Gr4 Gr5 6Al 4V Titanium Plate Width | 1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required |
| UNS Plate Thickness | 0.3 to 120mm or as required |
| ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al 4V Plate Process | Hot/ Cold Rolled/forging |
| UNS Plate surface | No.1, No. 2D, No. 2B, BA, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al 4V Plate, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc. |
| ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al 4V Plate, Sheet and Strip | JIS: N0, N2, N1, NW2200, NW2201, NW4400, NW5500, NW6002, etc |
| DIN:H-Ni99.96, H-Ni99.95, H-Ni99.92, H-Ni99.90, H-Ni99.5, H-Ni99, etc | |
| Titanium Gr1 Gr2 Gr3 Gr4 Gr5 Sheet ASTM | ASTM B265 |
| Titanium Gr1 Gr2 Gr3 Gr4 Gr5 Sheet AMS | AMS 4902 |
| Tolerances of width and thickness | EN 10258 (formerly DIN 59381),EN 10151 ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al 4V strip for springs,EN 10088 ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al 4V strip (general) |
| Cp Gr1 Gr2 Gr3 Gr4 Gr5 Titanium Plate standards and approvals | EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID |
DAXUN produces and stocks commercially pure titanium plates Gr1 Gr2 Gr3 Gr4 (UNS) with thicknesses ranging from 0.5 mm to 120 mm. Gr1 Gr2 Gr3 Gr4 titanium plate (UNS) is the "workhorse" in the commercially pure titanium family. It combines high strength, ductility and excellent corrosion resistance for many industrial applications.
Gr1 Gr2 Gr3 Gr4 titanium plate is a commercially pure titanium plate. It achieves an excellent balance between strength and ductility. It has good impact strength and is easy to weld. It has good corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, weakly reducing environments and wet chlorine. It also has excellent resistance to seawater and salt solutions.
Gr5 grade5 Ti6al4v titanium plate is a titanium alloy plate Gr5 Ti-6Al-4V titanium alloy plate contains 90% titanium, 6% aluminum and 4% vanadium, and is an α-β type titanium alloy, in which aluminum plays the role of stabilizing the α phase and vanadium plays the role of stabilizing the β phase. The main features of Gr5 Ti-6Al-4V titanium alloy plate are excellent comprehensive performance and good process performance. TC4 titanium alloy has excellent room temperature and high temperature strength, good creep resistance and thermal stability, high fatigue performance and crack growth resistance in seawater, as well as satisfactory fracture toughness and hot salt stress corrosion performance. Gr5 Ti-6Al-4V titanium alloy plate also has excellent process plasticity and superplasticity, suitable for various processing methods, as well as various welding and machining methods.
About the chemical composition of(Ti 6AL-4V) grade 5 titanium sheet
| Chemical Composition: | |||
| Symbol | Element | Min % | Max % |
| Al | Aluminum | 5.50% | 6.75% |
| V | Vanadium | 3.50% | 4.50% |
| Fe | Iron | 0.30% | |
| O | Oxygen | 0.20% | |
| C | Carbon | 0.08% | |
| N | Nitrogen | 0.05% | |
| H | Hydrogen | 0.01% | |
| Y | Yttrium | 0.01% | |
| Other, each | 0.10% | ||
| Other, total | 0.40% | ||
| Ti | Titanium | Remainder | |
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
About the chemical composition of grade 2 titanium sheet
| Element | Weight % |
| C | ≤0.08 |
| O | ≤0.25 |
| N | ≤0.03 |
| H | ≤0.015 |
| Fe | ≤0.30 |
| *OEE | ≤0.10 |
| *OET | ≤0.40 |
| Ti | Remaining |
About the mechanical properties of grade 2 titanium sheet
| Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
| psi | MPa | ksi | psi | MPa | ksi | % | |||||||
| Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
| 50,000 | |||||||||||||
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
| Fe | 0.2 | ||
| O | 0.18 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
| Density | |
| lb/in3 | g/cm3 |
| 0.163 | 4.51 |
| Tensile Strength | |
| ksi | MPa |
| 35 min | 240 min |
| Yield Strength | |
| ksi | MPa |
| 20 min | 138 min |
| Hardness | |
| 70 HRC max | |
| Elongation | |
| 24% min |
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
|---|---|---|---|
| Al | 2.5 | 3.5 | |
| V | 2.0 | 3.0 | |
| Fe | 0.25 | ||
| O | 0.15 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
| CP GR1 Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium plate PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
DAXUN is a Ti 6AL 4V-Grade 5-TC4 UNS R56400 Alloy Titanium Plate Manufacturer and Supplier from China! With the goal of creating the world's high-performance titanium alloy plates. We deliver quickly worldwide - ASTM B265 Grade 2, Grade 5 Titanium Plates. DAXUN produces and stocks alloy titanium plates Grade 5 (UNS R56400) with thicknesses ranging from 0.5mm to 300mm (0.5mm-6.0mm is cold rolled. 6.0-50mm is hot rolled, and 50mm and above are forged). Grade 5 titanium plate (Ti-6Al-4V) is the "workhorse" of titanium alloy materials. It combines high strength, ductility and excellent corrosion resistance, high temperature resistance, thus being favored by many general and military industries. Compliant with: ASTE, ASME, AMS, GB, GJB, MIL, JIS, EN, etc.
Ti-6Al-4V grade 5 titanium plate is mainly used in aerospace, military industry, power industry, vehicle armor, rocket precision guidance parts, marine industry, etc.
Grade 1
Today, DAXUN Alloys is a leading global producer and supplier of high-quality Grade 1 titanium plate.
Pure Grade 1 titanium plate has excellent ductility and cold formability, making it ideal for deep drawing. Grade 1 titanium is known for its excellent general and seawater corrosion resistance, as well as its resistance to oxidizing, neutral and mildly reducing media (solutions), including chlorides. Titanium's low density (about half that of nickel-based alloys), high strength-to-weight ratio and corrosion resistance make it an excellent choice for a wide range of harsh chemical conditions. Commercially pure Grade 1 titanium is the softest and most ductile. It has good cold formability and excellent corrosion resistance. It also has excellent weldability and good impact hardness.
ASTM B265 Titanium Gr 1 Plate Producers, Titanium Gr 1 Sheets, Titanium Gr 1 Finished Plates, ASTM B265 Titanium Grade 1 Coil Suppliers, Pure Titanium Titanium Gr 1 Hot Rolled Plates, Titanium Gr 1 Cold Rolled Plates, Titanium ASTM B265 Gr 1 Sheets, Gr 1 Titanium Patterned Plates Dealers, Titanium Gr 1 Perforated Plates, Titanium Grade 1 Sheets and Plates Manufacturers in China.
Grade2
DAXUN produces and stocks commercially pure titanium plates Grade 2 (UNS R50400) in thicknesses ranging from 0.5mm to 120mm. Grade 2 Titanium Plate (UNS R50400) is the "workhorse" of the commercially pure titanium family. It combines high strength, ductility, and excellent corrosion resistance for many industrial applications.
Grade 2 Titanium Plate is a commercially pure titanium plate. It offers an excellent balance between strength and ductility. It has good impact strength and is easily weldable. It has good corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, weakly reducing environments, and wet chlorine. It also has excellent resistance to seawater and salt solutions.
Titanium's low density, high strength-to-weight ratio, and corrosion resistance make it an ideal material for a wide range of applications, and it effectively resists stress corrosion cracking, pitting, and crevice corrosion in chloride solutions below 70°C. With a melting point of 1660°C, Grade 2 Titanium Plate is the alloy of choice for most industrial applications requiring good ductility and corrosion resistance.
DAXUN is a metal expert focused on small and large titanium plate projects. DAXUN is your reference point and long-term partner, ready to provide you and your business with titanium plates and any technical assistance you may need. You can consider DAXUN not only as your supplier of industrial pure titanium plates and titanium alloy plates, but also as your strategic partner to help you meet any challenges and needs you may encounter, ultimately allowing you to achieve your project goals.
DAXUN's service center in China has titanium plate products in stock for fast order processing. Through basic processing, water jet cutting and plate nesting products, we provide added value to our customers, saving them time and costs.
Continuous investment in DAXUN's production facilities and capacity agreements with our partners ensure that DAXUN is at the forefront of titanium plate quality now and in the future.
Contact DAXUN today to get the latest titanium plate prices and technical information.
Q1: What products can you offer?
A: We can offer you general steel types like 310S, 316L,304.304L.201,904L, 316H, 316,316L 300and
400 series, and duplex stainless steel like 2205, 2304,2101,2507,etc. 904L, 800H, 600H high-nickel alloy.
Q2. Can you produce the products according to my own drawings?
Yes, we can produce the products according to your drawings that will be most satisfy you.
Q3. How does your factory do regarding quality control?
Quality is a priority. We always attach great importance to quality controlling from the beginning to end.
Q4. Can I request to change the form of packaging and transportation?
Yes, We can change the form of the packaging and transportation according to your request,
but you have to bear their own costs incurred during this period and the spreads.
Q5. How does your factory do regarding quality control?
Quality is a priority. We always attach great importance to quality controlling from the beginning to end.
Q6. How long is the delivery time?
A: 7~20 working days after confirming the payment.
If the order is urgent, we will push our workshop finish in advance.
Q7. What is your Payment?
A: 100% T/T advance, Western Union (For Small Order)
B: 30% T/T and balance 70% before the shipment
C: 100% Irrevocable LC at sight (For Big Order)
Q8: Can you make DDQ ( Deep Drawing Quality)?
A: Yes, we can. Our material can be used for stainless steel pots, stainless steel sinks, stainless steel bowls etc. U can tell us your usage, and we will adjust the mechanical propertise to meet your requirement.
Q9: How to get a sample?
A: FREE samples are available for your checking and testing.If you require for a small piece,we can afford courier cost,it depends.
Q10:Which country have you exported to?
A:Until now,we have exported stainless steel material to following countries: Vietnam,Thailand,Turkey,Russia,Maroc,Korea,India,Pakistan,UAE,Ukraine and so on.
Q11: How to visit your company?
A:By flight to Guangzhou Baiyun International airport,then we will pick you up.
Suppliers with verified business licenses
){kind=link}
){kind=link}