Type: | Titanium Sheets |
---|---|
Application: | Industrial |
Technique: | Hot Rolled |
Grade: | Gr5 Ti-6al-4V Gr7 Gr9 Gr23 |
Shape: | Square |
Thickness: | 0.3mm-120mm |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Titanium Plate and sheet Type | Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate |
Grade | ASME SB265,AMS 4911,AMS 4919,AMS 4914,ASTM F67,ASTM F136, MSRR, AMS, BS |
Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate Length | 1000mm-13000mm or as required |
Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Titanium Plate Width | 1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required |
UNS Plate Thickness | 0.3 to 120mm or as required |
ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate Process | Hot/ Cold Rolled/forging |
UNS Plate surface | No.1, No. 2D, No. 2B, BA, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc. |
ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate, Sheet and Strip | JIS: N0, N2, N1, NW2200, NW2201, NW4400, NW5500, NW6002, etc |
DIN:H-Ni99.96, H-Ni99.95, H-Ni99.92, H-Ni99.90, H-Ni99.5, H-Ni99, etc | |
Titanium Gr1 Gr2 Gr3 Gr4 Gr5 Sheet ASTM | ASTM B265 |
Titanium Gr1 Gr2 Gr3 Gr4 Gr5 Sheet AMS | AMS 4902 |
Tolerances of width and thickness | EN 10258 (formerly DIN 59381),EN 10151 ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 strip for springs,EN 10088 ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 strip (general) |
Cp Gr1 Gr2 Gr3 Gr4 Gr5 Titanium Plate standards and approvals | EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID |
DAXUN offers and stocks a wide range of commercially pure titanium plates, including Gr1, Gr2, Gr3, and Gr4 (UNS), with thicknesses from 0.5 mm to 120 mm. These grades are the mainstay of the commercially pure titanium family, providing an outstanding combination of high strength, ductility, and exceptional corrosion resistance, ideal for numerous industrial applications.
Gr1, Gr2, Gr3, and Gr4 titanium plates represent the essence of commercially pure titanium, striking a superb balance between strength and ductility. They exhibit excellent impact strength, weldability, and corrosion resistance. These plates perform exceptionally well in highly oxidizing environments, alkaline media, brine solutions, mildly reducing environments, and wet ***. Additionally, they offer superior resistance to seawater and salt solutions.
Gr5 Grade 5 Ti-6Al-4V titanium plate is an α-β type titanium alloy, comprising 90% titanium, 6% aluminum, and 4% vanadium. Aluminum stabilizes the α phase, while vanadium stabilizes the β phase. Gr5 Ti-6Al-4V titanium alloy plate stands out for its excellent overall performance and processability. Known for its strength at both room and high temperatures, it also boasts good creep resistance, thermal stability, and fatigue performance. Furthermore, it offers superior *** growth resistance in seawater, fracture toughness, and hot salt stress corrosion performance. With impressive process plasticity and superplasticity, this alloy is well-suited for various processing and welding methods.
Chemical Composition of (Ti 6AL-4V) Grade 5 Titanium Sheet
Chemical Composition: | |||
Symbol | Element | Min % | Max % |
Al | Aluminum | 5.50% | 6.75% |
V | Vanadium | 3.50% | 4.50% |
Fe | Iron | 0.30% | |
O | Oxygen | 0.20% | |
C | Carbon | 0.08% | |
N | Nitrogen | 0.05% | |
H | Hydrogen | 0.01% | |
Y | Yttrium | 0.01% | |
Other, each | 0.10% | ||
Other, total | 0.40% | ||
Ti | Titanium | Remainder |
Physical Properties | Metric | English | Comments |
Density | 4.43 g/cc | 0.16 lb/in³ | |
Mechanical Properties | |||
Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
Hardness, Rockwell C | 36 | 36 | |
Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
Tensile strength | min. 895MPa | 129810 psi | |
Yield strength | min. 828MPa | 120090 psi | |
Elongation at Break | min.10 % | 10 % | |
Reduction of Area | min.25 % | 25 % |
Chemical Composition of Grade 2 TitaniumSheet
Element | Weight % |
C | ≤0.08 |
O | ≤0.25 |
N | ≤0.03 |
H | ≤0.015 |
Fe | ≤0.30 |
*OEE | ≤0.10 |
*OET | ≤0.40 |
Ti | Remaining |
Mechanical Properties of Grade 2 Titanium Sheet
Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
psi | MPa | ksi | psi | MPa | ksi | % | |||||||
Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
50,000 |
Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
Fe | 0.2 | ||
O | 0.18 | ||
C | 0.08 | ||
N | 0.03 | ||
H | 0.015 | ||
Ti | Balance |
Density | |
lb/in3 | g/cm3 |
0.163 | 4.51 |
Tensile Strength | |
ksi | MPa |
35 min | 240 min |
Yield Strength | |
ksi | MPa |
20 min | 138 min |
Hardness | |
70 HRC max | |
Elongation | |
24% min |
Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
---|---|---|---|
Al | 2.5 | 3.5 | |
V | 2.0 | 3.0 | |
Fe | 0.25 | ||
O | 0.15 | ||
C | 0.08 | ||
N | 0.03 | ||
H | 0.015 | ||
Ti | Balance |
1. Cold-Rolled Titanium Plate: This premium plate is crafted through a meticulous plate rolling process, culminating in the final cold-rolling step. These sheets are available in both work-hardened and heat-treated conditions. Tailored to the specific requirements of our customers, further processing can include precise mechanical or chemical treatments. 2. Hot-Rolled Titanium Plate: These high-quality plates are produced through longitudinal rolling, or a combination of longitudinal and transverse rolling. Available thickness ranges from 3.0mm to 155mm, and they are supplied in heat-treated conditions. For specialized needs, creep flattening can be employed to eliminate internal stress and achieve exact flatness. We offer sheets as cut blanks, allowing for complex shapes to be derived from the parent metal. Further processing is customized based on client specifications.3. Forged Titanium Plate: This robust plate is forged from steel ingots using a vertical hydraulic press, followed by rolling, or through open die forging, with an option of subsequent rolling. Standard slab dimensions include thicknesses up to 580mm, widths up to 2000mm, and lengths up to 6000mm. Specific dimensions and weights of the forged plates are agreed upon between Jiangsu Daxun Alloy Co., Ltd. and the customer.
CP GR1 Titanium plate PHYSICAL PROPERTIES | |||
Physical Properties | Metric | English | Comments |
Density | 4.50 g/cc | 0.163 lb/in³ | |
a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
Mechanical Properties | Metric | English | Comments |
Hardness, Brinell | 120 | 120 | annealed |
Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
Hardness, Rockwell B | 70 | 70 | annealed |
Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
Elongation at Break | 24% | 24% | |
25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
Reduction of Area | 35% | 35% | |
Tensile Modulus | 103 GPa | 14900 ksi | |
Compressive Modulus | 110 GPa | 16000 ksi | |
Poissons Ratio | 0.37 | 0.37 | |
Shear Modulus | 45.0 GPa | 6530 ksi | |
Charpy Impact | 310 J | 229 ft-lb | V-notch |
Impact Test | 136 J | 100 ft-lb | Impact Strength |
Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
0.8 | 0.8 | Ti sliding on Ti; 40 m/min |
CP GR2 Titanium plate PHYSICAL PROPERTIES | |
Density | Magnetic Permeability |
0.163 lbs/in-3 | Nonmagnetic |
4.51 g/cm-3 | Electrical Resistivity |
Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
1680°F | 0.53 µΩ/m |
915°C | Elastic Modulus |
Thermal Conductivity | 15.2-17.4 Msi |
12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
GR5 TI6AL4V Titanium plate PHYSICAL PROPERTIES | |||
Physical Properties | Metric | English | Comments |
Density | 4.43 g/cc | 0.16 lb/in³ | |
Mechanical Properties | |||
Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
Hardness, Rockwell C | 36 | 36 | |
Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
Tensile strength | min. 895MPa | 129810 psi | |
Yield strength | min. 828MPa | 120090 psi | |
Elongation at Break | min.10 % | 10 % | |
Reduction of Area | min.25 % | 25 % | |
Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
Compressive Yield Strength | 970 MPa | 141000 psi | |
Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
Poisson's Ratio | 0.342 | 0.342 | |
Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
Shear Modulus | 44 GPa | 6380 ksi | |
Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
Electrical Properties | |||
Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
Thermal Properties | |||
CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
Solidus | 1604 °C | 2920 °F | |
Liquidus | 1660 °C | 3020 °F | |
Beta Transus | 980 °C | 1800 °F |
DAXUN is a Ti 6AL 4V-Grade 5-TC4 UNS R56400 Alloy Titanium Plate Manufacturer and Supplier from China! With the goal of creating the world's high-performance titanium alloy plates. We deliver quickly worldwide - ASTM B265 Grade 2, Grade 5 Titanium Plates. DAXUN produces and stocks alloy titanium plates Grade 5 (UNS R56400) with thicknesses ranging from 0.5mm to 300mm (0.5mm-6.0mm is cold rolled. 6.0-50mm is hot rolled, and 50mm and above are forged). Grade 5 titanium plate (Ti-6Al-4V) is the "workhorse" of titanium alloy materials. It combines high strength, ductility and excellent corrosion resistance, high temperature resistance, thus being favored by many general and military industries. Compliant with: ASTE, ASME, AMS, GB, GJB, MIL, JIS, EN, etc.
Ti-6Al-4V grade 5 titanium plate is mainly used in aerospace, military industry, power industry, vehicle armor, rocket precision guidance parts, marine industry, etc.
Grade 1
Today, DAXUN Alloys is a leading global producer and supplier of high-quality Grade 1 titanium plate.
Pure Grade 1 titanium plate has excellent ductility and cold formability, making it ideal for deep drawing. Grade 1 titanium is known for its excellent general and seawater corrosion resistance, as well as its resistance to oxidizing, neutral and mildly reducing media (solutions), including chlorides. Titanium's low density (about half that of nickel-based alloys), high strength-to-weight ratio and corrosion resistance make it an excellent choice for a wide range of harsh chemical conditions. Commercially pure Grade 1 titanium is the softest and most ductile. It has good cold formability and excellent corrosion resistance. It also has excellent weldability and good impact hardness.
ASTM B265 Titanium Gr 1 Plate Producers, Titanium Gr 1 Sheets, Titanium Gr 1 Finished Plates, ASTM B265 Titanium Grade 1 Coil Suppliers, Pure Titanium Titanium Gr 1 Hot Rolled Plates, Titanium Gr 1 Cold Rolled Plates, Titanium ASTM B265 Gr 1 Sheets, Gr 1 Titanium Patterned Plates Dealers, Titanium Gr 1 Perforated Plates, Titanium Grade 1 Sheets and Plates Manufacturers in China.
Grade2
DAXUN produces and stocks commercially pure titanium plates Grade 2 (UNS R50400) in thicknesses ranging from 0.5mm to 120mm. Grade 2 Titanium Plate (UNS R50400) is the "workhorse" of the commercially pure titanium family. It combines high strength, ductility, and excellent corrosion resistance for many industrial applications.
Grade 2 Titanium Plate is a commercially pure titanium plate. It offers an excellent balance between strength and ductility. It has good impact strength and is easily weldable. It has good corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, weakly reducing environments, and wet ***. It also has excellent resistance to seawater and salt solutions.
Titanium's low density, high strength-to-weight ratio, and corrosion resistance make it an ideal material for a wide range of applications, and it effectively resists stress corrosion cracking, pitting, and crevice corrosion in chloride solutions below 70°C. With a melting point of 1660°C, Grade 2 Titanium Plate is the alloy of choice for most industrial applications requiring good ductility and corrosion resistance.
DAXUN is a metal expert focused on small and large titanium plate projects. DAXUN is your reference point and long-term partner, ready to provide you and your business with titanium plates and any technical assistance you may need. You can consider DAXUN not only as your supplier of industrial pure titanium plates and titanium alloy plates, but also as your strategic partner to help you meet any challenges and needs you may encounter, ultimately allowing you to achieve your project goals.
DAXUN's premier service center in China maintains an extensive inventory of titanium plate products, ensuring rapid order fulfillment. By offering fundamental processing, precision water jet cutting, and efficient plate nesting services, we deliver exceptional value to our clients, significantly reducing their time and expenses.
DAXUN's relentless investment in state-of-the-art production facilities, coupled with strategic capacity agreements with our esteemed partners, guarantees that DAXUN remains a leader in the titanium plate industry, consistently delivering unparalleled quality today and in the years to come.
Reach out to DAXUN today to receive the most competitive prices and detailed technical insights on our titanium plate offerings.
Q1: What products can you offer?
A: We offer a wide variety of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L, and the 300 series.
We also provide the 400 series and high-performance duplex stainless steel such as 2205, 2304, 2101, 2507, along with high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
Yes, we can craft products precisely according to your drawings to ensure utmost satisfaction.
Q3. How does your factory do regarding quality control?
Quality is our top priority. We ensure stringent quality control measures are in place from start to finish.
Q4. Can I request to change the form of packaging and transportation?
Yes, we are flexible and can alter the packaging and transportation methods per your request.
However, you will need to cover any costs incurred during this adjustment period, including any price differences.
Q5. How does your factory do regarding quality control?
Quality is our top priority. We ensure stringent quality control measures are in place from start to finish.
Q6. How long is the delivery time?
A: Our delivery time is typically between 7 to 20 working days post-payment confirmation.
For urgent orders, we can expedite the process and prioritize your order in our workshop.
Q7. What is your Payment?
A: We offer various payment terms: 100% T/T in advance, Western Union for small orders.
B: 30% T/T in advance and the remaining 70% before shipment.
C: 100% Irrevocable LC at sight for large orders.
Q8: Can you make DDQ ( Deep Drawing Quality)?
A: Absolutely. Our materials are suitable for deep drawing applications, such as stainless steel pots, sinks, and bowls. Inform us of your specific needs, and we will tailor the mechanical properties accordingly.
Q9: How to get a sample?
A: We provide FREE samples for your evaluation and testing. For small pieces, we may cover the courier cost depending on the situation.
Q10: Which countries have you exported to?
A: We have proudly exported our stainless steel materials to Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many other countries.
Q11: How to visit your company?
A: You can fly to Guangzhou Baiyun International Airport, and we will arrange to pick you up from there.
Suppliers with verified business licenses