Type: | Titanium Sheets |
---|---|
Application: | Industrial |
Technique: | Hot Rolled |
Grade: | Gr5 Ti-6al-4V Gr7 Gr9 Gr23 |
Shape: | Square |
Thickness: | 0.3mm-120mm |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Titanium Plate and sheet Type | Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate |
Grade | ASME SB265,AMS 4911,AMS 4919,AMS 4914,ASTM F67,ASTM F136, MSRR, AMS, BS |
Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate Length | 1000mm-13000mm or as required |
Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Titanium Plate Width | 1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required |
UNS Plate Thickness | 0.3 to 120mm or as required |
ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate Process | Hot/ Cold Rolled/forging |
UNS Plate surface | No.1, No. 2D, No. 2B, BA, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc. |
ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate, Sheet and Strip | JIS: N0, N2, N1, NW2200, NW2201, NW4400, NW5500, NW6002, etc |
DIN:H-Ni99.96, H-Ni99.95, H-Ni99.92, H-Ni99.90, H-Ni99.5, H-Ni99, etc | |
Titanium Gr1 Gr2 Gr3 Gr4 Gr5 Sheet ASTM | ASTM B265 |
Titanium Gr1 Gr2 Gr3 Gr4 Gr5 Sheet AMS | AMS 4902 |
Tolerances of width and thickness | EN 10258 (formerly DIN 59381),EN 10151 ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 strip for springs,EN 10088 ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 strip (general) |
Cp Gr1 Gr2 Gr3 Gr4 Gr5 Titanium Plate standards and approvals | EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID |
DAXUN is a trusted provider of commercially pure titanium plates, including Gr1 Gr2 Gr3 Gr4 (UNS), available in a wide range of thicknesses from 0.5 mm to 120 mm. Known as the 'workhorse' of the titanium family, Gr1 Gr2 Gr3 Gr4 plates combine remarkable strength, exceptional ductility, and superb corrosion resistance, making them indispensable for numerous industrial applications.
Gr1 Gr2 Gr3 Gr4 titanium plates are commercially pure, offering an outstanding balance between strength and ductility. These plates exhibit excellent impact strength and weldability, with impressive corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, and wet ***. Additionally, they provide superior resistance to seawater and salt solutions.
Gr5 grade5 Ti6al4v titanium plates, known for their titanium alloy composition, consist of 90% titanium, 6% aluminum, and 4% vanadium. This α-β type titanium alloy benefits from aluminum stabilizing the α phase and vanadium stabilizing the β phase. Gr5 Ti-6Al-4V titanium alloy plates are renowned for their exceptional comprehensive performance and processability. TC4 titanium alloy features excellent strength at both room and high temperatures, superior creep resistance, outstanding thermal stability, and impressive fatigue performance. Additionally, it offers high *** growth resistance in seawater, satisfactory fracture toughness, and robust hot salt stress corrosion resistance. Gr5 Ti-6Al-4V titanium alloy plates boast excellent process plasticity and superplasticity, making them suitable for various processing and welding methods.
Chemical Composition of (Ti 6AL-4V) Grade 5 Titanium Sheet
Chemical Composition: | |||
Symbol | Element | Min % | Max % |
Al | Aluminum | 5.50% | 6.75% |
V | Vanadium | 3.50% | 4.50% |
Fe | Iron | 0.30% | |
O | Oxygen | 0.20% | |
C | Carbon | 0.08% | |
N | Nitrogen | 0.05% | |
H | Hydrogen | 0.01% | |
Y | Yttrium | 0.01% | |
Other, each | 0.10% | ||
Other, total | 0.40% | ||
Ti | Titanium | Remainder |
Physical Properties | Metric | English | Comments |
Density | 4.43 g/cc | 0.16 lb/in³ | |
Mechanical Properties | |||
Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
Hardness, Rockwell C | 36 | 36 | |
Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
Tensile strength | min. 895MPa | 129810 psi | |
Yield strength | min. 828MPa | 120090 psi | |
Elongation at Break | min.10 % | 10 % | |
Reduction of Area | min.25 % | 25 % |
Chemical Composition of Grade 2 TitaniumSheet
Element | Weight % |
C | ≤0.08 |
O | ≤0.25 |
N | ≤0.03 |
H | ≤0.015 |
Fe | ≤0.30 |
*OEE | ≤0.10 |
*OET | ≤0.40 |
Ti | Remaining |
Mechanical Properties of Grade 2 Titanium Sheet
Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
psi | MPa | ksi | psi | MPa | ksi | % | |||||||
Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
50,000 |
Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
Fe | 0.2 | ||
O | 0.18 | ||
C | 0.08 | ||
N | 0.03 | ||
H | 0.015 | ||
Ti | Balance |
Density | |
lb/in3 | g/cm3 |
0.163 | 4.51 |
Tensile Strength | |
ksi | MPa |
35 min | 240 min |
Yield Strength | |
ksi | MPa |
20 min | 138 min |
Hardness | |
70 HRC max | |
Elongation | |
24% min |
Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
---|---|---|---|
Al | 2.5 | 3.5 | |
V | 2.0 | 3.0 | |
Fe | 0.25 | ||
O | 0.15 | ||
C | 0.08 | ||
N | 0.03 | ||
H | 0.015 | ||
Ti | Balance |
1. Cold-rolled Titanium Plate: Our cold-rolled titanium plates are meticulously crafted through a plate rolling process, culminating in a precise cold rolling final step. These sheets are available in either a work-hardened or heat-treated state, tailored to the customer's preferences. Further processing, whether mechanical or chemical, is customized to meet your specific requirements. 2. Hot-rolled Titanium Plate: Expertly produced using longitudinal rolling or a combination of longitudinal and transverse rolling, our hot-rolled titanium plates range from 3.0mm to 155mm in thickness. Delivered in a heat-treated condition, these plates can undergo creep flattening for internal stress elimination and special flatness needs. They can be supplied as cut blanks, allowing for intricate shapes cut from the parent metal, with further processing customized to your requirements.3. Forged Titanium Plate: Our forged titanium plates are produced by forging steel ingots on a vertical hydraulic press, followed by rolling, or through open die forging (with or without subsequent rolling). We offer slabs with thicknesses up to 580 mm, widths up to 2000 mm, and lengths up to 6000 mm. Dimensions and weights of forged plates are meticulously agreed upon between the manufacturer and the customer, ensuring a perfect fit for your needs.
CP GR1 Titanium plate PHYSICAL PROPERTIES | |||
Physical Properties | Metric | English | Comments |
Density | 4.50 g/cc | 0.163 lb/in³ | |
a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
Mechanical Properties | Metric | English | Comments |
Hardness, Brinell | 120 | 120 | annealed |
Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
Hardness, Rockwell B | 70 | 70 | annealed |
Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
Elongation at Break | 24% | 24% | |
25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
Reduction of Area | 35% | 35% | |
Tensile Modulus | 103 GPa | 14900 ksi | |
Compressive Modulus | 110 GPa | 16000 ksi | |
Poissons Ratio | 0.37 | 0.37 | |
Shear Modulus | 45.0 GPa | 6530 ksi | |
Charpy Impact | 310 J | 229 ft-lb | V-notch |
Impact Test | 136 J | 100 ft-lb | Impact Strength |
Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
0.8 | 0.8 | Ti sliding on Ti; 40 m/min |
CP GR2 Titanium plate PHYSICAL PROPERTIES | |
Density | Magnetic Permeability |
0.163 lbs/in-3 | Nonmagnetic |
4.51 g/cm-3 | Electrical Resistivity |
Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
1680°F | 0.53 µΩ/m |
915°C | Elastic Modulus |
Thermal Conductivity | 15.2-17.4 Msi |
12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
GR5 TI6AL4V Titanium plate PHYSICAL PROPERTIES | |||
Physical Properties | Metric | English | Comments |
Density | 4.43 g/cc | 0.16 lb/in³ | |
Mechanical Properties | |||
Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
Hardness, Rockwell C | 36 | 36 | |
Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
Tensile strength | min. 895MPa | 129810 psi | |
Yield strength | min. 828MPa | 120090 psi | |
Elongation at Break | min.10 % | 10 % | |
Reduction of Area | min.25 % | 25 % | |
Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
Compressive Yield Strength | 970 MPa | 141000 psi | |
Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
Poisson's Ratio | 0.342 | 0.342 | |
Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
Shear Modulus | 44 GPa | 6380 ksi | |
Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
Electrical Properties | |||
Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
Thermal Properties | |||
CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
Solidus | 1604 °C | 2920 °F | |
Liquidus | 1660 °C | 3020 °F | |
Beta Transus | 980 °C | 1800 °F |
DAXUN is a premier Ti-6Al-4V Grade 5 (UNS R56400) Alloy Titanium Plate Manufacturer and Supplier from China! Dedicated to crafting the world's highest-performing titanium alloy plates, we ensure swift global delivery of ASTM B265 Grade 2 and Grade 5 Titanium Plates. DAXUN produces and maintains an extensive inventory of Grade 5 (UNS R56400) titanium plates in thicknesses ranging from 0.5mm to 300mm. Cold rolled plates span 0.5mm-6.0mm, hot rolled plates range from 6.0-50mm, while plates above 50mm are forged. Renowned as the 'workhorse' of titanium alloys, Grade 5 (Ti-6Al-4V) offers exceptional strength, ductility, and superior resistance to corrosion and high temperatures, making it a preferred choice for both general and military applications. Our plates adhere to standards including ASTE, ASME, AMS, GB, GJB, MIL, JIS, EN, and more.
Ti-6Al-4V Grade 5 titanium plate is primarily utilized in aerospace, military, power industries, vehicle armor, rocket precision guidance systems, and marine applications.
Grade 1
Today, DAXUN Alloys stands as a leading global producer and supplier of top-tier Grade 1 titanium plates.
Pure Grade 1 titanium plate is celebrated for its outstanding ductility and cold formability, perfect for deep drawing applications. Known for excellent resistance to general and seawater corrosion as well as oxidizing, neutral, and mildly reducing media, including chlorides, Grade 1 titanium is ideal for harsh chemical conditions. With a low density (approximately half that of nickel-based alloys), high strength-to-weight ratio, and superb corrosion resistance, commercially pure Grade 1 titanium is the softest and most ductile, excelling in cold formability, corrosion resistance, weldability, and impact hardness.
ASTM B265 Titanium Grade 1 Plate Producers, Titanium Grade 1 Sheets, Finished Plates, ASTM B265 Titanium Grade 1 Coil Suppliers, Pure Titanium Gr 1 Hot Rolled Plates, Gr 1 Cold Rolled Plates, Titanium ASTM B265 Grade 1 Sheets, Patterned Plates Dealers, Perforated Plates, Titanium Grade 1 Sheets and Plates Manufacturers in China.
Grade 2
DAXUN produces and stocks commercially pure titanium plates Grade 2 (UNS R50400) with thicknesses from 0.5mm to 120mm. Grade 2 Titanium Plate (UNS R50400) is the 'workhorse' of commercially pure titanium, offering a perfect blend of strength, ductility, and excellent corrosion resistance across various industrial applications.
Grade 2 Titanium Plate, a commercially pure titanium plate, balances strength and ductility with impressive corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, mildly reducing environments, and wet ***. The plate also boasts excellent resistance to seawater and salt solutions. High impact strength and weldability make it a preferred material for numerous industries.
Titanium's low density, high strength-to-weight ratio, and robust corrosion resistance make it an ideal choice for diverse applications. Grade 2 Titanium Plate effectively resists stress corrosion cracking, pitting, and crevice corrosion in chloride solutions below 70°C. With a melting point of 1660°C, it is the alloy of choice for industrial uses demanding superior ductility and corrosion resistance.
DAXUN, a metal expert in both small and large titanium plate projects, is your trusted partner for high-quality titanium plates and technical assistance. More than just a supplier of industrial pure titanium and titanium alloy plates, DAXUN is your strategic partner, dedicated to helping you overcome challenges and meet needs, ensuring your project's success and achievement of your goals.
At DAXUN's premier service center in China, we boast an extensive stock of titanium plate products, enabling rapid order fulfillment. With advanced basic processing, precise water jet cutting, and efficient plate nesting, we deliver exceptional value to our customers by significantly reducing their time and costs.
Strategic and continuous investments in our production facilities, coupled with robust capacity agreements with our esteemed partners, position DAXUN as a leader in titanium plate quality both now and in the future.
Reach out to DAXUN today to access the most competitive titanium plate prices and comprehensive technical information. Experience the pinnacle of product excellence and customer service.
Q1: What products can you offer?
A: We offer a diverse range of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L 300 series, and 400 series.
Additionally, we provide duplex stainless steel such as 2205, 2304, 2101, 2507, etc., and high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
A: Absolutely! We can produce products tailored to your drawings, ensuring complete satisfaction.
Q3. How does your factory handle quality control?
Quality is our top priority. We meticulously control quality from start to finish, ensuring superior products.
Q4. Can I request to change the form of packaging and transportation?
A: Yes, we can adjust the packaging and transportation forms to meet your request.
However, please note that any additional costs or differences incurred will be your responsibility.
Q5. How does your factory manage quality control?
Quality is paramount. We place great emphasis on stringent quality control throughout the entire process.
Q6. What is the delivery time?
A: Our standard delivery time is 7 to 20 working days after payment confirmation.
For urgent orders, we expedite production to meet your needs promptly.
Q7. What are your payment terms?
A: 100% T/T in advance, Western Union for small orders.
B: 30% T/T upfront and 70% balance before shipment.
C: 100% Irrevocable LC at sight for large orders.
Q8: Can you produce Deep Drawing Quality (DDQ) materials?
A: Yes, we specialize in DDQ materials suitable for stainless steel pots, sinks, bowls, etc. Share your requirements, and we will adjust the mechanical properties accordingly.
Q9: How can I get a sample?
A: We provide FREE samples for your evaluation and testing. For small pieces, we often cover the courier cost depending on the circumstances.
Q10: Which countries have you exported to?
A: We have exported stainless steel materials to numerous countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many more.
Q11: How can I visit your company?
A: Fly to Guangzhou Baiyun International Airport, and we will arrange to pick you up from there.