| Type: | Titanium Sheets |
|---|---|
| Application: | Industrial |
| Technique: | Hot Rolled |
| Grade: | Gr5 Ti-6al-4V Gr7 Gr9 Gr23 |
| Shape: | Square |
| Thickness: | 0.3mm-120mm |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier
| Titanium Plate and sheet Type | Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate |
| Grade | ASME SB265,AMS 4911,AMS 4919,AMS 4914,ASTM F67,ASTM F136, MSRR, AMS, BS |
| Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate Length | 1000mm-13000mm or as required |
| Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Titanium Plate Width | 1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required |
| UNS Plate Thickness | 0.3 to 120mm or as required |
| ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate Process | Hot/ Cold Rolled/forging |
| UNS Plate surface | No.1, No. 2D, No. 2B, BA, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc. |
| ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate, Sheet and Strip | JIS: N0, N2, N1, NW2200, NW2201, NW4400, NW5500, NW6002, etc |
| DIN:H-Ni99.96, H-Ni99.95, H-Ni99.92, H-Ni99.90, H-Ni99.5, H-Ni99, etc | |
| Titanium Gr1 Gr2 Gr3 Gr4 Gr5 Sheet ASTM | ASTM B265 |
| Titanium Gr1 Gr2 Gr3 Gr4 Gr5 Sheet AMS | AMS 4902 |
| Tolerances of width and thickness | EN 10258 (formerly DIN 59381),EN 10151 ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 strip for springs,EN 10088 ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 strip (general) |
| Cp Gr1 Gr2 Gr3 Gr4 Gr5 Titanium Plate standards and approvals | EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID |
DAXUN offers an extensive inventory of commercially pure titanium plates Gr1, Gr2, Gr3, and Gr4 (UNS) with thicknesses ranging from 0.5 mm to 120 mm. These grades are the cornerstone of the commercially pure titanium family, combining remarkable strength, ductility, and exceptional corrosion resistance, making them ideal for a wide array of industrial applications.
Gr1, Gr2, Gr3, and Gr4 titanium plates are the epitome of commercially pure titanium. They strike a perfect balance between strength and ductility, offering excellent impact resistance and weldability. These plates exhibit superior corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, mildly reducing environments, and wet ***. They are also highly resistant to seawater and salt solutions.
The Gr5 grade5 Ti6al4v titanium plate is an advanced titanium alloy plate. It comprises 90% titanium, 6% aluminum, and 4% vanadium, forming an α-β type titanium alloy where aluminum stabilizes the α phase, and vanadium stabilizes the β phase. Gr5 Ti-6Al-4V titanium alloy plate stands out with its superior comprehensive performance and process capability. This alloy boasts excellent strength at both room and high temperatures, remarkable creep resistance, thermal stability, and high fatigue and *** growth resistance in seawater. It also exhibits outstanding fracture toughness and hot salt stress corrosion resistance. The Gr5 Ti-6Al-4V titanium alloy plate is incredibly processable, suitable for various processing, welding, and machining methods.
About the chemical composition of (Ti 6AL-4V) grade 5 titanium sheet
| Chemical Composition: | |||
| Symbol | Element | Min % | Max % |
| Al | Aluminum | 5.50% | 6.75% |
| V | Vanadium | 3.50% | 4.50% |
| Fe | Iron | 0.30% | |
| O | Oxygen | 0.20% | |
| C | Carbon | 0.08% | |
| N | Nitrogen | 0.05% | |
| H | Hydrogen | 0.01% | |
| Y | Yttrium | 0.01% | |
| Other, each | 0.10% | ||
| Other, total | 0.40% | ||
| Ti | Titanium | Remainder | |
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
About the chemical composition of grade 2 titanium sheet
| Element | Weight % |
| C | ≤0.08 |
| O | ≤0.25 |
| N | ≤0.03 |
| H | ≤0.015 |
| Fe | ≤0.30 |
| *OEE | ≤0.10 |
| *OET | ≤0.40 |
| Ti | Remaining |
About the mechanical properties of grade 2 titanium sheet
| Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
| psi | MPa | ksi | psi | MPa | ksi | % | |||||||
| Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
| 50,000 | |||||||||||||
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
| Fe | 0.2 | ||
| O | 0.18 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
| Density | |
| lb/in3 | g/cm3 |
| 0.163 | 4.51 |
| Tensile Strength | |
| ksi | MPa |
| 35 min | 240 min |
| Yield Strength | |
| ksi | MPa |
| 20 min | 138 min |
| Hardness | |
| 70 HRC max | |
| Elongation | |
| 24% min |
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
|---|---|---|---|
| Al | 2.5 | 3.5 | |
| V | 2.0 | 3.0 | |
| Fe | 0.25 | ||
| O | 0.15 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
1. Cold-Rolled Titanium Plate: This premium plate is meticulously produced through the plate rolling process, with the final stage being cold rolling. The sheets are available in either a work-hardened or heat-treated condition. Subsequent processing can be tailored to your specific needs, whether mechanical or chemical. 2. Hot-Rolled Titanium Plate: Crafted by longitudinal rolling or a combination of longitudinal and transverse rolling, these plates boast thicknesses ranging from 3.0mm to a robust 155mm. Delivered in a heat-treated state, they can undergo creep flattening to eliminate internal stress and meet special flatness requirements. Available as cut blanks for complex shapes, further processing is customized based on your requirements.3. Forged Titanium Plate: Produced by forging steel ingots on a vertical hydraulic press followed by rolling or through open die forging, our forged titanium plates are designed to meet the highest standards. Standard slab dimensions include thickness up to 580 mm, width up to 2000 mm, and length up to 6000 mm. Dimensions and weight are customized per agreement between the customer and manufacturer.
| CP GR1 Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium plate PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
DAXUN is a premier Ti-6Al-4V Grade 5 (UNS R56400) Alloy Titanium Plate Manufacturer and Supplier from China! We aspire to create the world's finest high-performance titanium alloy plates. Offering swift global delivery of ASTM B265 Grade 2 and Grade 5 Titanium Plates, DAXUN produces and stocks alloy titanium plates of Grade 5 (UNS R56400) with thicknesses ranging from 0.5mm to 300mm. Our Grade 5 titanium plates cater to various industrial needs with unparalleled quality; 0.5mm-6.0mm are cold rolled, 6.0-50mm are hot rolled, and above 50mm are forged. Known as the 'workhorse' of titanium alloys, Grade 5 offers exceptional strength, ductility, corrosion resistance, and high-temperature stability, making it invaluable for both general and military industries. Compliant with ASTE, ASME, AMS, GB, GJB, MIL, JIS, EN, and more.
The versatile Ti-6Al-4V Grade 5 titanium plate finds extensive applications in aerospace, military, power industries, vehicle armor, rocket precision guidance parts, marine industries, and more.
Grade 1
Today, DAXUN Alloys stands as a distinguished global producer and supplier of top-tier Grade 1 titanium plates.
Our Pure Grade 1 titanium plates boast excellent ductility and cold formability, making them ideal for deep drawing applications. Renowned for its superior general and seawater corrosion resistance, Grade 1 titanium resists oxidizing, neutral, and mildly reducing media, including chlorides. With a low density (about half that of nickel-based alloys) and a high strength-to-weight ratio, it's an outstanding choice for challenging chemical environments. Commercially pure Grade 1 titanium is the softest and most ductile variant, offering excellent cold formability, weldability, and impact hardness.
We are leading producers of ASTM B265 Titanium Gr 1 Plates, offering a wide array of products including Titanium Gr 1 Sheets, Finished Plates, Coils, Hot Rolled and Cold Rolled Plates, Patterned Plates, Perforated Plates, and much more. All our products are manufactured in China, ensuring top-notch quality and reliability.
Grade 2
DAXUN excels in producing and stocking commercially pure titanium plates of Grade 2 (UNS R50400) with thicknesses from 0.5mm to 120mm. Grade 2 Titanium Plate (UNS R50400), considered the 'workhorse' of commercially pure titanium, offers an excellent combination of strength, ductility, and corrosion resistance, suitable for numerous industrial applications.
Grade 2 Titanium Plate is a commercially pure titanium plate that harmonizes strength and ductility. It excels with high impact strength and ease of welding. It provides robust corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, weakly reducing atmospheres, and wet ***. Moreover, it offers outstanding resistance to seawater and salt solutions.
With its low density, high strength-to-weight ratio, and exceptional corrosion resistance, titanium is ideal for a broad range of applications. Grade 2 Titanium Plate effectively resists stress corrosion cracking, pitting, and crevice corrosion in chloride solutions up to 70°C. With a melting point of 1660°C, it remains the preferred alloy for industrial applications demanding excellent ductility and corrosion resistance.
DAXUN is your expert partner for both small-scale and large-scale titanium plate projects. As a trusted reference point and long-term ally, DAXUN offers not only industrial pure titanium plates and titanium alloy plates but also crucial technical assistance. Position DAXUN as your strategic partner to overcome challenges, meet needs, and ultimately achieve your project objectives.
DAXUN's premier service center in China boasts an extensive stock of titanium plate products, ensuring rapid order fulfillment. By leveraging advanced processing methods such as water jet cutting and precision plate nesting, we deliver unparalleled value to our customers, streamlining their operations and significantly reducing both time and costs.
DAXUN's unwavering commitment to continuous investment in state-of-the-art production facilities, coupled with strategic capacity agreements with our trusted partners, guarantees that we remain at the pinnacle of titanium plate quality, now and for the foreseeable future.
Reach out to DAXUN today to access the most up-to-date titanium plate pricing and comprehensive technical information, positioning your business ahead of the curve with our top-tier offerings.
Q1: What products can you offer?
A: We proudly offer an extensive range of steel products, including general steel types like 310S, 316L, 304, 304L, 201, 904L, 316H, and 316.
Additionally, we provide the robust 300 and 400 series, alongside duplex stainless steels such as 2205, 2304, 2101, and 2507. Our high-nickel alloy offerings include 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
A: Absolutely, we can manufacture products tailored precisely to your drawings, ensuring your utmost satisfaction.
Q3. How does your factory do regarding quality control?
A: Quality is our top priority. We meticulously control quality throughout every stage, from inception to completion.
Q4. Can I request to change the form of packaging and transportation?
A: Yes, we can accommodate your requests for packaging and transportation changes.
However, please be aware that any costs and differences incurred during this period will be your responsibility.
Q5. How does your factory do regarding quality control?
A: Quality is our top priority. We meticulously control quality throughout every stage, from inception to completion.
Q6. How long is the delivery time?
A: Typically, delivery takes 7 to 20 working days after payment confirmation.
If your order is urgent, we will expedite the process to meet your needs.
Q7. What is your Payment?
A: We accept 100% T/T in advance, and Western Union for small orders.
For larger orders, we offer 30% T/T with the 70% balance payable before shipment.
We also accept 100% Irrevocable LC at sight for significant orders.
Q8: Can you make DDQ (Deep Drawing Quality)?
A: Yes, we can. Our materials are suitable for stainless steel pots, sinks, bowls, etc. Share your application needs, and we'll adjust mechanical properties accordingly.
Q9: How to get a sample?
A: We provide FREE samples for your evaluation and testing. For small pieces, we may cover courier costs, depending on the situation.
Q10: Which country have you exported to?
A: We have exported stainless steel materials to various countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
Q11: How to visit your company?
A: Fly to Guangzhou Baiyun International Airport, and we will arrange to pick you up.
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}