| Ti-6Al-4V Grade 5 Titanium pipe & Tubes Specification | ASTM B338 / ASTM B861 / ASTM B862 / ASME SB338 / ASME SB861 / ASME SB862 |
| Grade 5 Titanium pipe & Tubes Grades | Commercially pure titanium Grade 5-Ti-6Al4V- TC4- USN 56400 |
| Grade 5 Titanium pipe & Tubes Type | ot Rolled / Cold Drawn / Welded / ERW |
| Grade 5 Titanium pipe & Tubes Outer Diameter Size | Titanium seamless pipe - φ1.0mm to φ508.3mm |
| Titanium welded pipe - φ6.0mm to φ1219mm | |
| Grade 5 Titanium pipe & Tubes Wall Thickness | 1.0mm-50mm (customizable wall thickness) |
| Grade 5 Titanium pipe & Tubes Length | 5 to 7 Meters, 09 to 13 Meters, Single Random Length, Double Random Length And Customize Size. |
| Titanium pipe Form Ti-6Al-4V | ' Hollow, U' bent, LSAW, Hydraulic, Straight Tube, Boiler, Round, Tube Coil, Square, Rectangular Etc |
| Marking TC4 1.37165 | All Titanium Tubes Tubing are marked as follows: Grade, Standard, Thickness, OD, Heat No., Length (Or according to the customer's request.) |
| Uses of Titanium Alloy Tubes | Gas pipes, oil pipes, heat exchanger tubes, boiler tubes, fluid pipes, titanium exhaust pipes. |
| Grade 5 Titanium pipe & Tubes Pipe Ends | Plain Ends / Beveled Ends |
| Grade 5 Titanium pipe & Tubes Delivery Conditions | As Rolled, Cold Drawn, Hot Finish, Stress Relieved, Annealed, Hardened, Tempered |
| Grade 5 Titanium pipe & Tubes Coating | Electropolish, Mechanical Polish, Satin Finish, Passivated |
| Grade 5 Titanium pipe & Tubes Other Testing | ardness Test, Hydrostatic Test, Eddy Current test, Eddy Current, Tensile Test, Flattening, Flare Test, Annealed, Hydrostatic Test, Tempered, Stress Relieved etc. |
| Grade 5 Titanium pipe & Tubes Dimension | All Pipes Is Manufactured and Inspected / Tested to the Relevant standards including ASTM And ASME |
| Grade 5 Titanium pipe & Tubes Value Added Services | Draw / Expansion / Machining / Sand Blasting / Shot Blasting / Heat Treatment |
| Grade 5 Titanium pipe & Tubes Packaging | Loose / Bundle / Wooden Pallet / Wooden box-a / Plastic Cloth Wraps / Plastic End Caps / Beveled Protector |
| Grade 5 Titanium pipe & Tubes Shipment & Transportation | By Road - Truck / Train, By Sea - Break-bulk Conventional Vessel / FCL (Full Container Load) / LCL (Less Container Load) / 20 Feet Container / 40 Feet Container / 45 Feet Container / High Cube Container / Open Top Container, By Air - Freighter Civil Passenger and Cargo Planes |
| Grade 5 Titanium pipe & Tubes Material Test Certificate | Manufacturer Test Certificate As Per EN10204 3.1, 3.2 / Laboratory Test Certificate From NABL Approved Lab. / Under Third Party Inspection Agency Like SGS, TUV, DNV, LLOYDS, ABS ETC |
Grade 5 Titanium Tubes: Engineered for Extreme Corrosive Conditions Across Multiple Industries:
At Daxun, we conduct a series of stringent quality assurance tests, including flattening, flaring, ultrasonic flaw detection, pitting and resistance, mechanical, hardness, material positive identification, and expansion tests. These ensure that our Grade 1 Titanium Welded and Seamless Pipes meet your application needs perfectly. Throughout production, we meticulously measure diameter, thickness, and surface quality. Standard delivery is within 5-7 days, while special size products are delivered in 15-20 days.
Ti-6Al4V Grade 5 Titanium Alloy Tubes are the epitome of commercial titanium alloys, blending high strength and toughness. These tubes offer excellent welding and processing characteristics:
We stock and sell Grade 5 Titanium Alloy Seamless Tubes, Forged Seamless Tubes, Welded Tubes, and more.
As a premier titanium alloy tube manufacturer and supplier in China, Daxun Alloy provides world-class Grade 5 titanium pipes, earning acclaim from numerous projects worldwide.
Ti 6Al-4V (Grade 5 Titanium) is the most extensively used titanium alloy tube, representing over 50% of total titanium usage. Typically employed in the annealed state, it can operate at temperatures up to 400°C (750°F). Ti 6Al/4V is welded with matching or ELI filler wire, offering significantly higher strength than commercially pure titanium tubes, with enhanced stiffness and thermal properties (excluding thermal conductivity). The thermal conductivity of Grade 5 titanium tube is about 60% lower than CP titanium. Among its many advantages, it can be heat-treated to achieve superior strength and performance. Using Grade 5 titanium seamless tubes provides strong formability, low density, and excellent corrosion resistance.
This exceptional grade strikes a harmonious balance of strength, corrosion resistance, weldability, and machinability, making it indispensable across numerous industries. Widely adopted in military aircraft, the aviation sector, rocket components, precision-guided elements, armor equipment, naval machinery, and military vacuum apparatus, it stands as a testament to superior engineering. The closely related variant, 6-4ELI, extends its utility to surgical implants, showcasing its versatility. Ideally suited for applications up to 400°C, it enhances ductility and toughness, particularly under cold working conditions, thanks to its remarkable specific strength. Typically supplied in the annealed state, it can be conveniently heat-treated to bolster its strength for diverse applications. As a general-purpose titan, the Ti 6Al-4V seamless tube boasts a spectrum of desirable properties across a temperature range of -210°C to 400°C. Grade 5 titanium alloy tubes are the epitome of commercialization among titanium alloys, combining unparalleled strength with toughness. These tubes also exhibit commendable welding and processing characteristics, solidifying their top-tier status.
Titanium Alloy Grade 5 Seamless Pipe, Titanium Gr 5 High Pressure Pipe, ASTM B338 Titanium Alloy Gr 5 Seamless Pipe, Titanium Gr 5 Thick Wall Pipe. As a leading supplier in China, we offer China Titanium Grade 5 ERW Pipe. Discover our extensive range of products including Titanium Alloy Gr 5 Pipe, Titanium Gr 5 Electropolished Pipe, and Anti-corrosion Titanium Pipe. Our expertise extends to the provision of Titanium Tube, ASTM B338 Titanium Grade 5 Welded Pipe, and ASTM B861 / ASME SB861 Titanium Grade 5 Seamless Pipe. As a renowned manufacturer of China Titanium Gr-5 Seamless Pipe, we pride ourselves on delivering top-quality products. Explore our offerings such as the Ti-6al-4v Pipe Dealer, ASTM B338 Titanium Grade 5 Pipe, Titanium Gr 5 Bright Annealed Pipe, Ti-6al-4v Pipe, Gr 5 Pipe, Titanium Gr 5 Pipe, and the premium Titanium WERKSTOFF NR 3.7165 Pipe. Elevate your project with our unrivaled titanium solutions.
Titanium Seamless Tubes
Daxun produces:
Hot-finished Titanium Tubes
Our titanium tubes are meticulously crafted, available in forms of hot-rolled or hot-extruded. They are straightened, with both inside and outside diameters precisely machined and surface polished. Choose from heat-treated or non-heat-treated varieties. We boast 100% ultrasonic flaw detection capabilities, ensuring unmatched quality.
Titanium Tube Materials Available:
Hot-rolled Titanium Tubes: Outer Diameter (OD) ranges from 19mm to 325mm, wall thickness spans 9mm to 30mm, and lengths extend up to 5000mm (customized per agreement between manufacturer and customer). - Hot-extruded Titanium Tubes: OD from 50mm to 160mm, wall thickness from 7mm to 35mm, and lengths up to 3000mm (customized per agreement between manufacturer and customer).
Cold-finished Titanium Tubes
Cold-finished Titanium Tubes are supplied heat-treated, surface-etched, hydrostatically, or ultrasonically tested, based on manufacturing specs. Available in OD 6mm to 89mm, wall thickness 0.5mm to 11mm, lengths up to 6000mm (customized per agreement between manufacturer and customer).
Titanium Welded Pipes
DaXun offers a range of titanium pipes with diameters from 12.7mm to 38.1mm (0.47in to 1.5in), wall thickness from 0.4mm to 1.65mm (0.016in to 0.065in), and lengths up to 25000mm. We provide Gr1, Gr2, and Gr12 titanium alloy pipes for engineering and chemical industries. Manufactured from flat rolled raw material using automatic tungsten inert gas (argon) welding, our pipes undergo rigorous heat treatments, mechanical testing, geometric measurements, and comprehensive 100% ultrasonic and eddy current testing, as well as pneumatic or hydrostatic testing. Our products comply with ASTM B 338 and ASME SB 338 standards, and packaging is tailored to customer specifications.
| CP GR1 Titanium tube PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium tube PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium tube PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
• ASTM B338 - Standard heat treatable titanium tubes
• AMS 4928 - Forgings and forging stock (annealed)
• AMS 4965 - Forgings (solution treated and aged)
• AMS 4967 - Forgings (annealed, heat treatable)
Typical hardness in the annealed condition ranges from Rockwell C 30-34, while in the solution treated and aged condition, it ranges from Rockwell C 35-39.
Q1: What products can you offer?
A: We offer a diverse range of steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L as well as the 300 series.
We also provide 400 series, duplex stainless steel such as 2205, 2304, 2101, 2507, and more. Additionally, we specialize in high-nickel alloys like 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
A: Absolutely! We can manufacture products precisely according to your drawings to ensure utmost satisfaction.
Q3. How does your factory do regarding quality control?
A: Quality is our top priority. We meticulously control quality throughout the production process, from start to finish.
Q4. Can I request to change the form of packaging and transportation?
A: Yes, we can adjust the packaging and transportation method as per your request.
Please note that you will need to cover any additional costs incurred during this period.
Q5. How does your factory do regarding quality control?
A: Quality is our top priority. We meticulously control quality throughout the production process, from start to finish.
Q6. How long is the delivery time?
A: Our standard delivery time is 7~20 working days after confirming payment.
If the order is urgent, we will expedite production to meet your needs.
Q7. What is your Payment?
A: We accept 100% T/T advance, Western Union for small orders.
B: For larger orders, we accept 30% T/T advance with the balance of 70% before shipment.
C: For substantial orders, a 100% Irrevocable LC at sight is also an option.
Q8: Can you make DDQ (Deep Drawing Quality)?
A: Yes, our materials are suitable for applications such as stainless steel pots, sinks, bowls, etc. Share your usage requirements, and we will tailor the mechanical properties accordingly.
Q9: How to get a sample?
A: FREE samples are available for your inspection and testing. For small pieces, we may cover courier costs, depending on the situation.
Q10: Which countries have you exported to?
A: We have successfully exported stainless steel materials to countries including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many more.
Q11: How to visit your company?
A: Fly to Guangzhou Baiyun International Airport, and we will arrange to pick you up from there.
){kind=link}