| Type: | Titanium Sheets |
|---|---|
| Application: | Industrial |
| Technique: | Hot Rolled |
| Grade: | Gr5 Ti-6al-4V Gr7 Gr9 Gr23 |
| Shape: | Square |
| Thickness: | 0.3mm-120mm |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier
| Titanium Plate and sheet Type | Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate |
| Grade | ASME SB265,AMS 4911,AMS 4919,AMS 4914,ASTM F67,ASTM F136, MSRR, AMS, BS |
| Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate Length | 1000mm-13000mm or as required |
| Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Titanium Plate Width | 1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required |
| UNS Plate Thickness | 0.3 to 120mm or as required |
| ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate Process | Hot/ Cold Rolled/forging |
| UNS Plate surface | No.1, No. 2D, No. 2B, BA, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc. |
| ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate, Sheet and Strip | JIS: N0, N2, N1, NW2200, NW2201, NW4400, NW5500, NW6002, etc |
| DIN:H-Ni99.96, H-Ni99.95, H-Ni99.92, H-Ni99.90, H-Ni99.5, H-Ni99, etc | |
| Titanium Gr1 Gr2 Gr3 Gr4 Gr5 Sheet ASTM | ASTM B265 |
| Titanium Gr1 Gr2 Gr3 Gr4 Gr5 Sheet AMS | AMS 4902 |
| Tolerances of width and thickness | EN 10258 (formerly DIN 59381),EN 10151 ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 strip for springs,EN 10088 ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 strip (general) |
| Cp Gr1 Gr2 Gr3 Gr4 Gr5 Titanium Plate standards and approvals | EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID |
DAXUN is a leading supplier of commercially pure titanium plates, including Gr1, Gr2, Gr3, and Gr4 (UNS), available in thicknesses from 0.5 mm to 120 mm. These plates are the backbone of the commercially pure titanium family, offering a harmonious blend of high strength, exceptional ductility, and outstanding corrosion resistance, suitable for a multitude of industrial applications.
Gr1, Gr2, Gr3, and Gr4 titanium plates epitomize commercially pure titanium excellence, achieving the perfect balance between strength and ductility. These plates excel in impact strength and weldability, providing superior corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, mildly reducing environments, and wet ***. They also offer unparalleled resistance to seawater and salt solutions.
The Gr5 grade 5 Ti6Al4V titanium plate is a premier titanium alloy comprising 90% titanium, 6% aluminum, and 4% vanadium, classified as an α-β titanium alloy. Aluminum stabilizes the α phase, while vanadium stabilizes the β phase. This alloy boasts exceptional comprehensive performance and processing capabilities. The TC4 titanium alloy demonstrates excellent strength at both room and elevated temperatures, superb creep resistance, thermal stability, high fatigue performance, and resistance to *** growth in seawater, coupled with impressive fracture toughness and resistance to hot salt stress corrosion. Its process plasticity and superplasticity make it versatile for various manufacturing methods, welding, and machining techniques.
About the chemical composition of (Ti 6AL-4V) grade 5 titanium sheet
| Chemical Composition: | |||
| Symbol | Element | Min % | Max % |
| Al | Aluminum | 5.50% | 6.75% |
| V | Vanadium | 3.50% | 4.50% |
| Fe | Iron | 0.30% | |
| O | Oxygen | 0.20% | |
| C | Carbon | 0.08% | |
| N | Nitrogen | 0.05% | |
| H | Hydrogen | 0.01% | |
| Y | Yttrium | 0.01% | |
| Other, each | 0.10% | ||
| Other, total | 0.40% | ||
| Ti | Titanium | Remainder | |
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
About the chemical composition of grade 2 titanium sheet
| Element | Weight % |
| C | ≤0.08 |
| O | ≤0.25 |
| N | ≤0.03 |
| H | ≤0.015 |
| Fe | ≤0.30 |
| *OEE | ≤0.10 |
| *OET | ≤0.40 |
| Ti | Remaining |
About the mechanical properties of grade 2 titanium sheet
| Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
| psi | MPa | ksi | psi | MPa | ksi | % | |||||||
| Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
| 50,000 | |||||||||||||
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
| Fe | 0.2 | ||
| O | 0.18 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
| Density | |
| lb/in3 | g/cm3 |
| 0.163 | 4.51 |
| Tensile Strength | |
| ksi | MPa |
| 35 min | 240 min |
| Yield Strength | |
| ksi | MPa |
| 20 min | 138 min |
| Hardness | |
| 70 HRC max | |
| Elongation | |
| 24% min |
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
|---|---|---|---|
| Al | 2.5 | 3.5 | |
| V | 2.0 | 3.0 | |
| Fe | 0.25 | ||
| O | 0.15 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
1. Cold-Rolled Titanium Plate: This premium plate is meticulously produced through advanced plate rolling techniques, with the final stage being cold rolling. These sheets are available in work-hardened or heat-treated conditions, ensuring durability and resilience. Further enhancements can be tailored to your specific requirements, whether through mechanical or chemical processing. 2. Hot-Rolled Titanium Plate: Crafted through both longitudinal and transverse rolling, these plates range in thickness from 3.0mm to 155mm and are supplied heat-treated for optimal performance. For those requiring special flatness, creep flattening can be utilized to eliminate internal stress. These plates can be delivered as cut blanks, allowing for the creation of complex shaped parts tailored to your needs. Further customization is available to meet precise customer specifications.3. Forged Titanium Plate: Forged to perfection, these plates are produced by forging steel ingots on a vertical hydraulic press, followed by rolling or open die forging techniques. The slabs are available in standard dimensions: up to 580mm in thickness, 2000mm in width, and 6000mm in length. Custom dimensions and weights can be arranged between the manufacturer and the customer, ensuring a perfect fit for your needs.
| CP GR1 Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium plate PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
DAXUN, a leading Ti 6AL 4V-Grade 5-TC4 UNS R56400 Alloy Titanium Plate Manufacturer and Supplier from China, is dedicated to producing the highest-quality titanium alloy plates in the industry. Our swift worldwide delivery includes ASTM B265 Grade 2 and Grade 5 Titanium Plates. We stock Grade 5 (UNS R56400) alloy titanium plates in various thicknesses from 0.5mm to 300mm. The 0.5mm-6.0mm range is cold rolled, 6.0-50mm is hot rolled, and 50mm and above are forged. Grade 5 titanium plate (Ti-6Al-4V), the 'workhorse' of titanium materials, is prized for its superior strength, ductility, corrosion resistance, and high-temperature resilience, making it indispensable in numerous general and military applications. Our products comply with ASTM, ASME, AMS, GB, GJB, MIL, JIS, EN, and more.
Renowned for its versatility, the Ti-6Al-4V Grade 5 titanium plate is extensively used in aerospace, military sectors, power industries, vehicle armor, precision rocket guidance components, and marine industries.
Grade 1
Today, DAXUN Alloys stands as a preeminent global producer and supplier of top-tier Grade 1 titanium plates.
Pure Grade 1 titanium plates boast excellent ductility and cold formability, making them ideal for deep drawing applications. Recognized for their superior general and seawater corrosion resistance, they excel in oxidizing, neutral, and mildly reducing environments, including chloride solutions. With a low density (approximately half that of nickel-based alloys), high strength-to-weight ratio, and outstanding corrosion resistance, titanium Grade 1 is an exemplary choice for a multitude of harsh chemical environments. Commercially pure Grade 1 titanium is the most malleable and ductile, featuring excellent cold formability, exceptional corrosion resistance, remarkable weldability, and solid impact hardness.
Producers of ASTM B265 Titanium Gr 1 Plates, Sheets, and Coils. We offer finished and patterned plates, perforated plates, hot and cold rolled plates, and more. As leading manufacturers in China, we cater to a wide range of applications with our high-quality Grade 1 titanium products.
Grade 2
DAXUN specializes in the production and stock of commercially pure titanium plates, Grade 2 (UNS R50400), available in thicknesses from 0.5mm to 120mm. The Grade 2 Titanium Plate, also known as the 'workhorse' of commercially pure titanium, offers a remarkable blend of strength, ductility, and corrosion resistance, tailored for numerous industrial sectors.
Grade 2 Titanium Plate, a commercially pure form of titanium, offers an exceptional balance of strength and ductility. It provides robust impact strength, excellent weldability, and impressive corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, and wet ***. It also demonstrates remarkable resilience against seawater and salt solutions.
Titanium's low density and high strength-to-weight ratio, combined with its excellent corrosion resistance, make it an ideal material for diverse applications. Grade 2 Titanium Plate effectively withstands stress corrosion cracking, pitting, and crevice corrosion in chloride solutions below 70°C. With a melting point of 1660°C, it is the alloy of choice for industrial applications demanding good ductility and corrosion resistance.
DAXUN is a specialist in both small and large titanium plate projects. As your trusted partner and reference point, we provide not only premium titanium plates but also comprehensive technical assistance for your business. Consider DAXUN your strategic ally, helping you navigate challenges and meet your project goals with our industrial pure titanium and titanium alloy plates.
At DAXUN, our premier service center in China maintains an extensive inventory of high-quality titanium plate products, ensuring rapid order fulfillment. By offering essential processing services, including water jet cutting and precise plate nesting, we deliver significant added value to our customers, helping them save both time and costs.
With sustained investments in DAXUN's state-of-the-art production facilities and strategic capacity agreements with key partners, we guarantee that DAXUN remains at the pinnacle of titanium plate excellence, both now and in the future.
Reach out to DAXUN today for the most current titanium plate pricing and comprehensive technical information.
Q1: What products can you offer?
A: We offer a wide array of premium steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, 316, 316L 300 series.
Additionally, we provide the 400 series and duplex stainless steel varieties like 2205, 2304, 2101, 2507, as well as high-nickel alloys such as 904L, 800H, and 600H.
Q2. Can you produce the products according to my own drawings?
Absolutely, we can meticulously produce products according to your specific drawings to ensure they meet your utmost satisfaction.
Q3. How does your factory handle quality control?
Quality is our top priority. We implement rigorous quality control measures from inception to completion to ensure excellence.
Q4. Can I request to change the form of packaging and transportation?
Yes, we can customize the packaging and transportation methods based on your request,
though you will need to cover any additional costs incurred during this process.
Q5. How does your factory handle quality control?
Quality is our top priority. We implement rigorous quality control measures from inception to completion to ensure excellence.
Q6. What is the delivery time?
A: Typically, the delivery time is 7 to 20 working days after confirming the payment.
For urgent orders, we will prioritize and expedite the process to meet your timelines.
Q7. What are your payment terms?
A: 100% T/T in advance, or Western Union for small orders.
B: 30% T/T upfront and the balance of 70% before shipment.
C: 100% Irrevocable LC at sight for large orders.
Q8: Can you produce Deep Drawing Quality (DDQ) material?
A: Yes, we certainly can. Our materials are ideal for applications like stainless steel pots, sinks, and bowls. Share your specific usage with us, and we will tailor the mechanical properties to meet your exact requirements.
Q9: How can I get a sample?
A: FREE samples are available for your evaluation and testing. For small pieces, we may cover the courier costs based on the situation.
Q10: Which countries have you exported to?
A: We have successfully exported stainless steel materials to numerous countries, including Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and many more.
Q11: How can I visit your company?
A: You can fly into Guangzhou Baiyun International Airport, and we will be delighted to pick you up from there.
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}