| Titanium Plate and sheet Type | Plate, Sheet, Strip, Coils, Foils, Flats, Clad Plate, Plain Sheet, Rolling Sheet, Rolling Plate, Flat Shim, Flat Sheet, Shim Sheet, Rolls, Blank (Circle), sheared, annealed, soft annealed, descaled, tread plate, Checker Plate |
| Grade | ASME SB265,AMS 4911,AMS 4919,AMS 4914,ASTM F67,ASTM F136, MSRR, AMS, BS |
| Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate Length | 1000mm-13000mm or as required |
| Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Titanium Plate Width | 1000mm-1219mm-1500mm-1800mm-2000mm-2500mm or as required |
| UNS Plate Thickness | 0.3 to 120mm or as required |
| ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate Process | Hot/ Cold Rolled/forging |
| UNS Plate surface | No.1, No. 2D, No. 2B, BA, No.3, No.4, No.6, No.7, 2B, 2D, BA NO(8), Cold rolled sheet (CR), Hot rolled plate (HR), SATIN (Met with Plastic Coated), No.1 finish hot rolled ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate, 1D, 2B, No.4, BA, 8K, satin, hairline, brush, mirror etc. |
| ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 Plate, Sheet and Strip | JIS: N0, N2, N1, NW2200, NW2201, NW4400, NW5500, NW6002, etc |
| DIN:H-Ni99.96, H-Ni99.95, H-Ni99.92, H-Ni99.90, H-Ni99.5, H-Ni99, etc | |
| Titanium Gr1 Gr2 Gr3 Gr4 Gr5 Sheet ASTM | ASTM B265 |
| Titanium Gr1 Gr2 Gr3 Gr4 Gr5 Sheet AMS | AMS 4902 |
| Tolerances of width and thickness | EN 10258 (formerly DIN 59381),EN 10151 ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 strip for springs,EN 10088 ASTM B265 Titanium Alloy Gr1 Gr2 Gr3 Gr4 Gr5 6Al4V Gr7 Gr9 Gr12 Gr23 strip (general) |
| Cp Gr1 Gr2 Gr3 Gr4 Gr5 Titanium Plate standards and approvals | EN ISO 18286 EN 10051 EN 10088-1 ISO 15510 EN ISO 9445 ASTM A 480 ASTM A 959 ASME IID |
At DAXUN, we specialize in the production and stocking of commercially pure titanium plates in Gr1, Gr2, Gr3, and Gr4 (UNS). These plates range from 0.5 mm to 120 mm in thickness. Known as the 'workhorse' of the commercially pure titanium family, Gr1 Gr2 Gr3 Gr4 titanium plate (UNS) combines remarkable strength, ductility, and outstanding corrosion resistance, making it ideal for a multitude of industrial applications.
Gr1, Gr2, Gr3, and Gr4 titanium plates represent the essence of commercially pure titanium. These plates offer an extraordinary balance of strength and ductility, coupled with excellent impact strength and weldability. They exhibit superior corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, weakly reducing atmospheres, and wet ***. Additionally, they provide exceptional resistance to seawater and salt solutions, ensuring longevity and reliability.
Gr5 Ti-6Al-4V titanium plate is a high-performance titanium alloy plate comprising 90% titanium, 6% aluminum, and 4% vanadium. As an α-β type titanium alloy, aluminum stabilizes the α phase, while vanadium stabilizes the β phase. Gr5 Ti-6Al-4V titanium alloy plate is renowned for its comprehensive performance and superior processability. The TC4 titanium alloy showcases outstanding strength at both room and high temperatures, exceptional creep resistance, thermal stability, high fatigue performance, resistance to *** growth in seawater, impressive fracture toughness, and resistance to hot salt stress corrosion. This alloy also boasts excellent process plasticity and superplasticity, making it suitable for various processing, welding, and machining methods.
Chemical Composition Insights: (Ti 6AL-4V) Grade 5 Titanium Sheet
| Chemical Composition: | |||
| Symbol | Element | Min % | Max % |
| Al | Aluminum | 5.50% | 6.75% |
| V | Vanadium | 3.50% | 4.50% |
| Fe | Iron | 0.30% | |
| O | Oxygen | 0.20% | |
| C | Carbon | 0.08% | |
| N | Nitrogen | 0.05% | |
| H | Hydrogen | 0.01% | |
| Y | Yttrium | 0.01% | |
| Other, each | 0.10% | ||
| Other, total | 0.40% | ||
| Ti | Titanium | Remainder | |
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
Chemical Composition Details: Grade 2 TitaniumSheet
| Element | Weight % |
| C | ≤0.08 |
| O | ≤0.25 |
| N | ≤0.03 |
| H | ≤0.015 |
| Fe | ≤0.30 |
| *OEE | ≤0.10 |
| *OET | ≤0.40 |
| Ti | Remaining |
Mechanical Properties of Grade 2 Titanium Sheet
| Alloy | UNS Designation | Spec. | Tensile Strength (min.) | Yield Strength 0.2% Offset (min.) | Elongation in 2 inches (min.) | Max Hardness | Modulus of Elasticity (x106 psi) | Mean Coefficient of Thermal Expansion IN./IN./°F x 10-6) | Thermal Conductivity (BTU-in/ft2-h-°F) | ||||
| psi | MPa | ksi | psi | MPa | ksi | % | |||||||
| Grade 2 Titanium | R50400 | B338 | 50,000 | -345 | 50 | 40,000- | (276-448) | 40-65 | 20 | - | 16 | 5.1 | 144 |
| 50,000 | |||||||||||||
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
| Fe | 0.2 | ||
| O | 0.18 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
| Density | |
| lb/in3 | g/cm3 |
| 0.163 | 4.51 |
| Tensile Strength | |
| ksi | MPa |
| 35 min | 240 min |
| Yield Strength | |
| ksi | MPa |
| 20 min | 138 min |
| Hardness | |
| 70 HRC max | |
| Elongation | |
| 24% min |
| Element | Minimum (weight %) | Maximum (weight %) | Typical (weight %) |
|---|---|---|---|
| Al | 2.5 | 3.5 | |
| V | 2.0 | 3.0 | |
| Fe | 0.25 | ||
| O | 0.15 | ||
| C | 0.08 | ||
| N | 0.03 | ||
| H | 0.015 | ||
| Ti | Balance |
1. Cold-rolled Titanium Plate: Crafted through an intricate plate rolling process, culminating in a meticulous cold rolling step, our cold-rolled titanium plates are available in both work-hardened and heat-treated conditions. Further processing can be tailored to your specific requirements, whether that involves mechanical or chemical treatments. 2. Hot-rolled Titanium Plate: Produced through advanced longitudinal rolling and both longitudinal and transverse rolling, these plates have thicknesses ranging from 3.0mm to 155mm and are supplied in a heat-treated state. Additionally, creep flattening can be employed as a heat treatment to alleviate internal stress and meet unique flatness specifications. Available as cut blanks or complex shaped parts, further processing is adaptable to your needs.3. Forged Titanium Plate: Manufactured by forging steel ingots on a vertical hydraulic press followed by rolling, or through open die forging and then rolling. Our standard slab dimensions include thickness up to 580 mm, width up to 2000 mm, and length up to 6000 mm. Custom dimensions and weights are negotiable to match your precise requirements.
| CP GR1 Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium plate PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium plate PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
DAXUN is a Ti 6AL 4V-Grade 5-TC4 UNS R56400 Alloy Titanium Plate Manufacturer and Supplier from China! With the goal of creating the world's high-performance titanium alloy plates. We deliver quickly worldwide - ASTM B265 Grade 2, Grade 5 Titanium Plates. DAXUN produces and stocks alloy titanium plates Grade 5 (UNS R56400) with thicknesses ranging from 0.5mm to 300mm (0.5mm-6.0mm is cold rolled. 6.0-50mm is hot rolled, and 50mm and above are forged). Grade 5 titanium plate (Ti-6Al-4V) is the "workhorse" of titanium alloy materials. It combines high strength, ductility and excellent corrosion resistance, high temperature resistance, thus being favored by many general and military industries. Compliant with: ASTE, ASME, AMS, GB, GJB, MIL, JIS, EN, etc.
Ti-6Al-4V grade 5 titanium plate is mainly used in aerospace, military industry, power industry, vehicle armor, rocket precision guidance parts, marine industry, etc.
Grade 1
Today, DAXUN Alloys is a leading global producer and supplier of high-quality Grade 1 titanium plate.
Pure Grade 1 titanium plate has excellent ductility and cold formability, making it ideal for deep drawing. Grade 1 titanium is known for its excellent general and seawater corrosion resistance, as well as its resistance to oxidizing, neutral and mildly reducing media (solutions), including chlorides. Titanium's low density (about half that of nickel-based alloys), high strength-to-weight ratio and corrosion resistance make it an excellent choice for a wide range of harsh chemical conditions. Commercially pure Grade 1 titanium is the softest and most ductile. It has good cold formability and excellent corrosion resistance. It also has excellent weldability and good impact hardness.
ASTM B265 Titanium Gr 1 Plate Producers, Titanium Gr 1 Sheets, Titanium Gr 1 Finished Plates, ASTM B265 Titanium Grade 1 Coil Suppliers, Pure Titanium Titanium Gr 1 Hot Rolled Plates, Titanium Gr 1 Cold Rolled Plates, Titanium ASTM B265 Gr 1 Sheets, Gr 1 Titanium Patterned Plates Dealers, Titanium Gr 1 Perforated Plates, Titanium Grade 1 Sheets and Plates Manufacturers in China.
Grade2
DAXUN produces and stocks commercially pure titanium plates Grade 2 (UNS R50400) in thicknesses ranging from 0.5mm to 120mm. Grade 2 Titanium Plate (UNS R50400) is the "workhorse" of the commercially pure titanium family. It combines high strength, ductility, and excellent corrosion resistance for many industrial applications.
Grade 2 Titanium Plate is a commercially pure titanium plate. It offers an excellent balance between strength and ductility. It has good impact strength and is easily weldable. It has good corrosion resistance in highly oxidizing environments, alkaline media, brine solutions, weakly reducing environments, and wet ***. It also has excellent resistance to seawater and salt solutions.
Titanium's low density, high strength-to-weight ratio, and corrosion resistance make it an ideal material for a wide range of applications, and it effectively resists stress corrosion cracking, pitting, and crevice corrosion in chloride solutions below 70°C. With a melting point of 1660°C, Grade 2 Titanium Plate is the alloy of choice for most industrial applications requiring good ductility and corrosion resistance.
DAXUN is a metal expert focused on small and large titanium plate projects. DAXUN is your reference point and long-term partner, ready to provide you and your business with titanium plates and any technical assistance you may need. You can consider DAXUN not only as your supplier of industrial pure titanium plates and titanium alloy plates, but also as your strategic partner to help you meet any challenges and needs you may encounter, ultimately allowing you to achieve your project goals.
At Jiangsu Daxun Alloy Co., Ltd., our dedicated service center in China boasts an extensive stock of premium titanium plate products, ensuring rapid order processing. Leveraging advanced techniques such as water jet cutting and precise plate nesting, we deliver exceptional value to our customers by significantly reducing both time and costs.
Through unwavering investment in state-of-the-art production facilities and strategic capacity agreements with key partners, Jiangsu Daxun Alloy Co., Ltd. consistently leads the industry in titanium plate quality, setting the benchmark for excellence both today and in the future.
Connect with Jiangsu Daxun Alloy Co., Ltd. today to access the most competitive titanium plate prices and comprehensive technical information. Let us be your trusted partner in achieving superior performance and reliability.
Q1: What products can you offer?
A: We provide a diverse range of general steel types including 310S, 316L, 304, 304L, 201, 904L, 316H, and more.
We also specialize in 400 series and duplex stainless steel such as 2205, 2304, 2101, 2507, in addition to 904L, 800H, and 600H high-nickel alloys.
Q2: Can you produce the products according to my own drawings?
A: Absolutely, we can manufacture products tailored to your specific drawings, ensuring your utmost satisfaction.
Q3: How does your factory manage quality control?
A: Quality is our top priority. We meticulously manage quality control from the initial stages to the final product.
Q4: Can I request to change the form of packaging and transportation?
A: Yes, we can adapt the packaging and transportation methods according to your requests.
However, please note that any additional costs incurred during this adjustment will be your responsibility.
Q5: How does your factory manage quality control?
A: Quality is our top priority. We meticulously manage quality control from the initial stages to the final product.
Q6: What is your delivery time?
A: Our standard delivery time is 7 to 20 working days after payment confirmation.
For urgent orders, we expedite the process to ensure timely delivery.
Q7: What are your payment options?
A: We offer several payment options:
B: 30% T/T in advance, with the remaining 70% before shipment
C: 100% irrevocable LC at sight for large orders
Q8: Can you provide DDQ (Deep Drawing Quality)?
A: Yes, we can. Our materials are suitable for stainless steel pots, sinks, bowls, etc. Let us know your requirements, and we will adjust the mechanical properties accordingly.
Q9: How can I get a sample?
A: We offer FREE samples for your review and testing. For small pieces, we may cover the courier cost depending on the situation.
Q10: Which countries have you exported to?
A: We have exported stainless steel materials to countries such as Vietnam, Thailand, Turkey, Russia, Morocco, Korea, India, Pakistan, UAE, Ukraine, and more.
Q11: How can I visit your company?
A: You can fly to Guangzhou Baiyun International Airport, and we will arrange to pick you up from there.
){kind=link}