| Ti-6Al-4V Grade 5 Titanium pipe & Tubes Specification | ASTM B338 / ASTM B861 / ASTM B862 / ASME SB338 / ASME SB861 / ASME SB862 |
| Grade 5 Titanium pipe & Tubes Grades | Commercially pure titanium Grade 5-Ti-6Al4V- TC4- USN 56400 |
| Grade 5 Titanium pipe & Tubes Type | ot Rolled / Cold Drawn / Welded / ERW |
| Grade 5 Titanium pipe & Tubes Outer Diameter Size | Titanium seamless pipe - φ1.0mm to φ508.3mm |
| Titanium welded pipe - φ6.0mm to φ1219mm | |
| Grade 5 Titanium pipe & Tubes Wall Thickness | 1.0mm-50mm (customizable wall thickness) |
| Grade 5 Titanium pipe & Tubes Length | 5 to 7 Meters, 09 to 13 Meters, Single Random Length, Double Random Length And Customize Size. |
| Titanium pipe Form Ti-6Al-4V | ' Hollow, U' bent, LSAW, Hydraulic, Straight Tube, Boiler, Round, Tube Coil, Square, Rectangular Etc |
| Marking TC4 1.37165 | All Titanium Tubes Tubing are marked as follows: Grade, Standard, Thickness, OD, Heat No., Length (Or according to the customer's request.) |
| Uses of Titanium Alloy Tubes | Gas pipes, oil pipes, heat exchanger tubes, boiler tubes, fluid pipes, titanium exhaust pipes. |
| Grade 5 Titanium pipe & Tubes Pipe Ends | Plain Ends / Beveled Ends |
| Grade 5 Titanium pipe & Tubes Delivery Conditions | As Rolled, Cold Drawn, Hot Finish, Stress Relieved, Annealed, Hardened, Tempered |
| Grade 5 Titanium pipe & Tubes Coating | Electropolish, Mechanical Polish, Satin Finish, Passivated |
| Grade 5 Titanium pipe & Tubes Other Testing | ardness Test, Hydrostatic Test, Eddy Current test, Eddy Current, Tensile Test, Flattening, Flare Test, Annealed, Hydrostatic Test, Tempered, Stress Relieved etc. |
| Grade 5 Titanium pipe & Tubes Dimension | All Pipes Is Manufactured and Inspected / Tested to the Relevant standards including ASTM And ASME |
| Grade 5 Titanium pipe & Tubes Value Added Services | Draw / Expansion / Machining / Sand Blasting / Shot Blasting / Heat Treatment |
| Grade 5 Titanium pipe & Tubes Packaging | Loose / Bundle / Wooden Pallet / Wooden box-a / Plastic Cloth Wraps / Plastic End Caps / Beveled Protector |
| Grade 5 Titanium pipe & Tubes Shipment & Transportation | By Road - Truck / Train, By Sea - Break-bulk Conventional Vessel / FCL (Full Container Load) / LCL (Less Container Load) / 20 Feet Container / 40 Feet Container / 45 Feet Container / High Cube Container / Open Top Container, By Air - Freighter Civil Passenger and Cargo Planes |
| Grade 5 Titanium pipe & Tubes Material Test Certificate | Manufacturer Test Certificate As Per EN10204 3.1, 3.2 / Laboratory Test Certificate From NABL Approved Lab. / Under Third Party Inspection Agency Like SGS, TUV, DNV, LLOYDS, ABS ETC |
Grade 5 Titanium Tubes: Trusted Across High-Stakes Industries in Extreme Corrosive Environments:
At Daxun, Quality Assurance is Paramount. Our Tests Include: Flattening, Flaring, Ultrasonic Flaw Detection, Pitting and Resistance, Mechanical, Hardness, Material Positive Identification, Expansion Tests, and more. These validations ensure the Grade 1 Titanium Welded and Seamless Pipes are impeccably suited for varied applications. We meticulously measure diameter, thickness, and surface during production. Standard delivery is 5-7 days, with special sizes taking 15-20 days.
The Ti-6Al4V Grade 5 Titanium Alloy Tube: A Commercial Titan Known for Its High Strength and Toughness. It Exhibits Excellent Welding and Processing Properties:
We Stock and Distribute: Grade 5 Titanium Alloy Seamless Tubes, Forged Seamless Tubes, Welded Tubes, and More.
As a Premier Manufacturer and Supplier, Daxun Alloy Delivers Top-Tier Grade 5 Titanium Pipes Globally, Earning High Praise Across Numerous Projects.
Ti 6Al-4V (Grade 5 Titanium): The Industry Favorite, Constituting Over 50% of Total Titanium Usage. Typically Annealed, It Functions Up to 400°C (750°F). Ti 6Al/4V is Compatible with Matching or ELI Filler Wire. It Offers Superior Strength, Stiffness, and Thermal Properties Compared to Pure Titanium (excluding thermal conductivity, which is about 60% lower). Additionally, It Can Be Heat Treated for Ideal Strength and Performance. Its Seamless Tubes Boast Strong Formability, Low Density, and Exceptional Corrosion Resistance.
Grade 5 Titanium: The Optimal Blend of Strength, Corrosion Resistance, Weldability, and Machinability. Widely Utilized in Military Aircraft, Rocket Parts, Precision-Guided Components, Armor Parts, Ship Equipment, and Military Vacuum Equipment. The Close Variant, 6-4ELI, Finds Use in Surgical Implants. Optimal for Temperatures Up to 400°C, It Enhances Ductility and Toughness in Cold Conditions. Available in an Annealed State, It's Easy to Heat Treat for Increased Strength, Catering to a Variety of Applications. This All-Purpose Titanium Alloy Offers Ideal Properties from -210°C to 400°C, Making It the Most Commercialized Titanium Alloy with High Strength and Toughness, Plus Excellent Welding and Processing Features.
cf48ccae
Titanium Seamless Tubes
Daxun produces:
Hot-finished Titanium Tubes
These tubes are supplied in a pristine form, either hot-rolled or hot-extruded. Each tube is meticulously straightened, with both inside and outside diameters precisely machined and surfaces polished to perfection. Available in both heat-treated and non-heat-treated variants, our tubes undergo 100% ultrasonic flaw detection to ensure unmatched quality and reliability.
Titanium Tube Materials Available:
Hot-rolled Titanium Tubes: Outer diameters ranging from 19mm to 325mm, wall thickness from 9mm to 30mm, and lengths up to 5000mm (subject to agreement between manufacturer and customer). - Hot-extruded Titanium Tubes: Outer diameters from 50mm to 160mm, wall thickness from 7mm to 35mm, and lengths up to 3000mm (subject to agreement between manufacturer and customer).
Cold-finished Titanium Tubes
Cold-finished Titanium Tubes are available in heat-treated form, with surface etching, hydrostatic testing, or ultrasonic testing as per manufacturing specifications. Specifications: Outer diameters from 6mm to 89mm, wall thickness from 0.5mm to 11mm, and lengths up to 6000mm (subject to agreement between manufacturer and customer).
Titanium Welded Pipes
DaXun manufactures and supplies titanium pipes with precision, featuring diameters ranging from 12.7 mm to 38.1 mm (0.47 in to 1.5 in), and wall thickness from 0.4 mm to 1.65 mm (0.016 in to 0.065 in), with lengths extending up to 25000 mm. These titanium alloy pipes, available in Gr1, Gr2, and Gr12, are ideal for engineering and chemical industries. Constructed from flat rolled raw material through automatic tungsten inert gas (argon) welding on electric pipe welders, and heat-treated on the mill line, each welded pipe undergoes rigorous mechanical testing, geometrical measurements, 100% ultrasonic and eddy current testing, as well as pneumatic or hydrostatic testing. Pipes are meticulously packed according to customer specifications. Our advanced manufacturing processes and inspection test equipment ensure that thin wall welded pipes meet the stringent ASTM B 338 and ASME SB 338 standards.
| CP GR1 Titanium tube PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.50 g/cc | 0.163 lb/in³ | |
| a Lattice Constant | 2.95 Å @Temperature 25.0 °C | 2.95 Å @Temperature 77.0 °F | alpha phase |
| 3.29 Å @Temperature 900 °C | 3.29 Å @Temperature 1650 °F | beta phase | |
| c Lattice Constant | 4.683 Å | 4.683 Å @Temperature 77.0 °F | c/a = 1.587 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 120 | 120 | annealed |
| Hardness, Knoop | 132 | 132 | Estimated from Brinell. |
| Hardness, Rockwell B | 70 | 70 | annealed |
| Hardness, Vickers | 122 | 122 | Estimated from Brinell. |
| Tensile Strength | 124 - 138 MPa @Temperature 427 °C | 18000 - 20000 psi @Temperature 801 °F | |
| 152 - 179 MPa @Temperature 316 °C | 22000 - 26000 psi @Temperature 601 °F | ||
| 193 - 207 MPa @Temperature 204 °C | 28000 - 30000 psi @Temperature 399 °F | ||
| Tensile Strength, Ultimate | 240 MPa | 34800 psi | |
| Tensile Strength, Yield | 170 - 310 MPa | 24700 - 45000 psi | |
| 76.0 - 90.0 MPa @Temperature 427 °C | 11000 - 13100 psi @Temperature 801 °F | 0.2% offset | |
| 83.0 - 103 MPa @Temperature 316 °C | 12000 - 14900 psi @Temperature 601 °F | 0.2% offset | |
| 110 - 124 MPa @Temperature 204 °C | 16000 - 18000 psi @Temperature 399 °F | 0.2% offset | |
| Elongation at Break | 24% | 24% | |
| 25 - 30 % @Temperature 427 °C | 25 - 30 % @Temperature 801 °F | ||
| 30 - 35 % @Temperature 316 °C | 30 - 35 % @Temperature 601 °F | ||
| 40 - 50 % @Temperature 204 °C | 40 - 50 % @Temperature 399 °F | ||
| Reduction of Area | 35% | 35% | |
| Tensile Modulus | 103 GPa | 14900 ksi | |
| Compressive Modulus | 110 GPa | 16000 ksi | |
| Poissons Ratio | 0.37 | 0.37 | |
| Shear Modulus | 45.0 GPa | 6530 ksi | |
| Charpy Impact | 310 J | 229 ft-lb | V-notch |
| Impact Test | 136 J | 100 ft-lb | Impact Strength |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | Ti sliding on Ti; 300 m/min |
| 0.8 | 0.8 | Ti sliding on Ti; 40 m/min | |
| CP GR2 Titanium tube PHYSICAL PROPERTIES | |
| Density | Magnetic Permeability |
| 0.163 lbs/in-3 | Nonmagnetic |
| 4.51 g/cm-3 | Electrical Resistivity |
| Beta Transus (+/-25°F, +/--3.9°C) | 21 µΩ/in |
| 1680°F | 0.53 µΩ/m |
| 915°C | Elastic Modulus |
| Thermal Conductivity | 15.2-17.4 Msi |
| 12.60 BTU hr-1ft-1 °F-1 | 105-120 GPa |
| 21.79 W m-1 °C-1 | Typical values at room temperature of about 68-78°F (20-25°C) |
| GR5 TI6AL4V Titanium tube PHYSICAL PROPERTIES | |||
| Physical Properties | Metric | English | Comments |
| Density | 4.43 g/cc | 0.16 lb/in³ | |
| Mechanical Properties | |||
| Hardness, Brinell | 334 | 334 | Estimated from Rockwell C. |
| Hardness, Knoop | 363 | 363 | Estimated from Rockwell C. |
| Hardness, Rockwell C | 36 | 36 | |
| Hardness, Vickers | 349 | 349 | Estimated from Rockwell C. |
| Tensile strength | min. 895MPa | 129810 psi | |
| Yield strength | min. 828MPa | 120090 psi | |
| Elongation at Break | min.10 % | 10 % | |
| Reduction of Area | min.25 % | 25 % | |
| Modulus of Elasticity | 113.8 GPa | 16500 ksi | |
| Compressive Yield Strength | 970 MPa | 141000 psi | |
| Notched Tensile Strength | 1450 MPa | 210000 psi | Kt (stress concentration factor) = 6.7 |
| Ultimate Bearing Strength | 1860 MPa | 270000 psi | e/D = 2 |
| Bearing Yield Strength | 1480 MPa | 215000 psi | e/D = 2 |
| Poisson's Ratio | 0.342 | 0.342 | |
| Charpy Impact | 17 J | 12.5 ft-lb | V-notch |
| Fatigue Strength | 240 MPa | 34800 psi | at 1E+7 cycles. Kt (stress concentration factor) = 3.3 |
| Fatigue Strength | 510 MPa | 74000 psi | Unnotched 10,000,000 Cycles |
| Fracture Toughness | 75 MPa-m½ | 68.3 ksi-in½ | |
| Shear Modulus | 44 GPa | 6380 ksi | |
| Shear Strength | 550 MPa | 79800 psi | Ultimate shear strength |
| Electrical Properties | |||
| Electrical Resistivity | 0.000178 ohm-cm | 0.000178 ohm-cm | |
| Magnetic Permeability | 1.00005 | 1.00005 | at 1.6kA/m |
| Magnetic Susceptibility | 3.30E-06 | 3.30E-06 | cgs/g |
| Thermal Properties | |||
| CTE, linear 20°C | 8.6 µm/m-°C | 4.78 µin/in-°F | 20-100ºC |
| CTE, linear 250°C | 9.2 µm/m-°C | 5.11 µin/in-°F | Average over the range 20-315ºC |
| CTE, linear 500°C | 9.7 µm/m-°C | 5.39 µin/in-°F | Average over the range 20-650ºC |
| Specific Heat Capacity | 0.5263 J/g-°C | 0.126 BTU/lb-°F | |
| Thermal Conductivity | 6.7 W/m-K | 46.5 BTU-in/hr-ft²-°F | |
| Melting Point | 1604 - 1660 °C | 2920 - 3020 °F | |
| Solidus | 1604 °C | 2920 °F | |
| Liquidus | 1660 °C | 3020 °F | |
| Beta Transus | 980 °C | 1800 °F | |
• ASTM B338 - Tubes Titanium tubes standard, heat treatable
• AMS 4928 - Forgings and forging stock (annealed)
• AMS 4965 - Forgings (solution treated and aged)
• AMS 4967 - Forgings (annealed, heat treatable)
Typical hardness ranges from Rockwell C 30-34 in the annealed condition to Rockwell C 35-39 in the solution and aged condition.
Q1: What products can you offer?
A: We offer a wide range of steel types, including common varieties such as 310S, 316L, 304, 304L, 201, 904L, 316H, and 316. Additionally, we provide an extensive selection of high-nickel alloys and duplex stainless steels like 2205, 2304, 2101, 2507, and 800H.
400 series, and duplex stainless steel like 2205, 2304,2101,2507,etc. 904L, 800H, 600H high-nickel alloy.
Q2. Can you produce the products according to my own drawings?
A: Yes, we can manufacture products based on your drawings to ensure they meet your specific requirements.
Q3. How does your factory manage quality control?
A: Quality is our top priority. We implement stringent quality control measures at every stage of the manufacturing process, from inception to completion.
Q4. Can I request to change the form of packaging and transportation?
A: Yes, we can accommodate requests to modify packaging and transportation methods according to your needs.
However, please note that you will need to cover any additional costs and price differences incurred during this process.
Q5. How does your factory manage quality control?
A: Quality is our top priority. We implement stringent quality control measures at every stage of the manufacturing process, from inception to completion.
Q6. How long is the delivery time?
A: Our standard delivery time is 7 to 20 working days after payment confirmation.
For urgent orders, we can expedite production to meet your deadlines.
Q7. What payment methods do you accept?
A: We accept various payment methods to suit your convenience:
B: 30% T/T in advance and the remaining 70% before shipment.
C: 100% Irrevocable Letter of Credit (LC) at sight for large orders.
Q8: Can you produce Deep Drawing Quality (DDQ) materials?
A: Yes, we specialize in DDQ materials that are ideal for making stainless steel pots, sinks, bowls, and more. Inform us of your specific application, and we will adjust the mechanical properties to meet your needs.
Q9: How can I obtain a sample?
A: We offer FREE samples for your evaluation and testing. For small sample pieces, we can cover the courier costs, depending on the situation.
Q10: Which countries have you exported to?
A: We have successfully exported stainless steel materials to numerous countries, including Vietnam, Thailand, Turkey, Russia, Morocco, South Korea, India, Pakistan, UAE, Ukraine, and many more.
Q11: How can I visit your company?
A: The nearest airport to our company is Guangzhou Baiyun International Airport. Upon your arrival, we will arrange a pickup for you.
){kind=link}